PURPOSE: The purpose of this in vitro study was to evaluate the SR, tensile strength (TS), and percentage elongation (% E) of different SEs subjected to outdoor weathering in the Malaysian climate.
MATERIAL AND METHODS: Type-II dumbbell-shaped specimens (N-120) (nonweathered=15, weathered=15) were made from 3 room-temperature vulcanized (A-2000, A-2006, and A-103) and 1 heat-temperature vulcanized (M-511) silicone (Factor II). For 6 months, weathered specimens were subjected to outdoor weathering inside a custom exposure rack. Simultaneously, the nonweathered specimens were kept in a dehumidifier. Subsequently, the SR was measured with a profilometer; TS and % E were measured by using a universal testing machine. Two-way ANOVA was used to compare the means of the tested properties of the nonweathered and weathered specimens, and pairwise comparison was carried out between the silicones (α=.05).
RESULTS: After outdoor weathering, the SR, TS, and % E were adversely affected by weathering in the Malaysian environment. Among the silicone materials, A-2000 showed the least TS changes (2.51 MPa), while A-2006 demonstrated significant changes in percentage elongation after outdoor weathering (266.5%). M-511 exhibited the highest mean value (2.50 μm) for SR changes. In addition, A-103 SE showed statistically significant differences in most pairwise comparisons for all 3 dependent variables.
CONCLUSIONS: Based on the evaluation of mechanical properties, A-103 can be suggested as a suitable silicone for maxillofacial prostheses fabricated for tropical climates. However, A-2000 can be a suitable alternative, although significant changes to surface roughness were detected after outdoor weathering.
METHODS: Eighty (80) male, 6-week-old Sprague Dawley rats were grouped in to four groups, the first group was irradiated with (940 nm) diode laser, second group with LIPUS, and third group with combination of both LLLT and LIPUS. A forth group used was a control group in an incomplete block split-mouth design. The LLLT and LIPUS were used to treat the area around the moving tooth once a day on days 0-7, then the experiment was ended in each experimental endpoint (1, 3, 7, 14, and 21 days). For amount of tooth movement, models were imaged and analyzed. Histological examination was performed after staining with (hematoxylin and eosin) and (alizarin red and Alcian Blue) stain. One step reverse transcription-polymerase chain reaction RT-PCR was also performed to elucidate the gene expression of RANK, RANKL, OPG, and RUNX-2.
RESULTS: The amount of tooth movement, the histological bone remodeling, and the RT-PCR were significantly greater in the treatment groups than that in the control group. Among the treatment groups, the combination group was the highest and the LIPUS group was the lowest.
CONCLUSION: These findings suggest that LLLT and LIPUS can enhance the velocity of tooth movement and improve the quality of bone remodeling during orthodontic tooth movement.
Methods: PubMed, SCOPUS, Science Direct, Web of Science, and Google Scholar electronic databases were searched systematically with restricting the languages to only English and year (January 2001 to March 2020), and studies were selected based on the inclusion criteria. Study quality and publication bias were assessed by using the Robvis, a software package of R statistical software.
Results: This systematic review included 32 studies (1172 patients) based on the inclusion and exclusion criteria. Most of the studies reported significant reduction of pain by the use of the laser during TMD treatment. Two-thirds of the study (78.13%) found a better outcome comparing with conventional one. According to Robvis, 84.4% of the studies were high methodological studies with low risk of bias.
Conclusion: TMD patients suffer with continuous pain for long time even after conventional treatment. Laser therapy shows a promising outcome of pain reduction for TMD patients. Therefore, laser therapy can be recommended for the TMD patients' better outcome. This trial is registered with PROSPERO (CRD42020177562).
Methods: Twenty-two patients (11 males and 11 females; mean age 19.18 ± 2.00 years) having Angle's Class II division 1 malocclusion needing bilateral extractions of maxillary first bicuspids were recruited for this split-mouth randomized clinical trial. After the initial stage of alignment and leveling with contemporary edgewise MBT (McLaughlin-Bennett-Trevisi) prescription brackets (Ortho Organizers, Carlsbad, Calif) of 22 mil, followed by extractions of premolars bilaterally, 6 mm nickel-titanium spring was used to retract the canines separately by applying 150 g force on 0.019 × 0.025-in stainless steel working archwires. LIPUS (1.1 MHz frequency and 30 mW/cm2 intensity output) was applied for 20 minutes extraorally and reapplied after 3 weeks for 2 more successive visits over the root of maxillary canine on the experimental side whereas the other side was placebo. A numerical rating scale- (NRS-) based questionnaire was given to the patients on each visit to record their weekly pain experience. Impressions were also made at each visit before the application of LIPUS (T1, T2, and T3). Models were scanned with a CAD/CAM scanner (Planmeca, Helsinki, Finland). Mann-Whitney U test was applied for comparison of canine movement and pain intensity between both the groups.
Results: No significant difference in the rate of canine movement was found among the experimental (0.90 mm ± 0.33 mm) and placebo groups (0.81 mm ± 0.32 mm). There was no difference in pain reduction between experimental and placebo groups (p > 0.05).
Conclusion: Single-dose application of LIPUS at 3-week intervals is ineffective in stimulating the OTM and reducing associated treatment pain.
Materials and Methods: Twenty patients with Angle's class II div 1 (10 males and 10 females; aged 20.25 ± 3.88 years) needing bilateral extractions of maxillary first bicuspids were recruited. Conventional brackets MBT of 0.022 in slot (McLaughlin Bennett Trevisi) prescription braces (Ortho Organizers, Carlsbad, Calif) were bonded. After alignment and levelling phase, cuspid retraction began with nitinol closed coil spring on 19 × 25 stainless steel archwire, wielding 150 gram force. 7.5 J/cm2 energy was applied on 10 points (5 buccal and 5 palatal) on the canine roots on the investigational side using gallium-aluminum-arsenic diode laser (940 nm wavelength, iLase™ Biolase, Irvine, USA) in a continuous mode. Target tissues were irradiated once in three weeks for 9 weeks at a stretch (T0, T1, and T2). Patients were given a feedback form based on the numeric rating scale (NRS) to record the pain intensity for a week. Silicon impressions preceded the coil activation at each visit (T0, T1, T2, and T3), and the casts obtained were scanned with the Planmeca CAD/CAM™ (Helsinki, Finland) scanner.
Results: The regimen effectively accelerated (1.55 ± 0.25 mm) tooth movement with a significant reduction in distress on the investigational side as compared to the placebo side (94 ± 0.25 mm) (p < 0.05).
Conclusions: This study reveals that the thrice-weekly LLLT application can accelerate OTM and reduce the associated pain.
MATERIALS AND METHODS: A gypsum mold was coated with clear acrylic spray. The coated mold was then used to produce modified silicone experimental specimens (n = 35). The surface roughness of the modified silicone elastomers was compared with that of the control specimens, which were prepared by conventional flasking methods (n = 35). An atomic force microscope (AFM) was used for surface roughness measurement of silicone elastomer (unmodified and modified), and a scanning electron microscope (SEM) was used to evaluate the topographic conditions of coated and noncoated gypsum and silicone elastomer specimens (unmodified and modified) groups. After the gypsum molds were characterized, the fabricated silicone elastomers molded on noncoated and coated gypsum materials were evaluated further. Energy-dispersive X-ray spectroscopy (EDX) analysis of gypsum materials (noncoated and coated) and silicone elastomer specimens (unmodified and modified) was performed to evaluate the elemental changes after coating was conducted. Independent t test was used to analyze the differences in the surface roughness of unmodified and modified silicone at a significance level of p < 0.05.
RESULTS: Roughness was significantly reduced in the silicone elastomers processed against coated gypsum materials (p < 0.001). The AFM and SEM analysis results showed evident differences in surface smoothness. EDX data further revealed the presence of the desired chemical components on the surface layer of unmodified and modified silicone elastomers.
CONCLUSIONS: Silicone elastomers with lower surface roughness of maxillofacial prostheses can be obtained simply by coating a gypsum mold.
METHODS: Relevant articles written in English only, before January 15, 2017, were identified using an electronic search in the PubMed, Scopus, and Google Scholar databases. Furthermore, a manual search of the related major journals was also conducted to identify more pertinent articles. The relevancy of the articles was verified by screening the title, abstract, and full text if they met the inclusion criteria. A total of 37 articles satisfied the criteria, from which data were extracted for qualitative synthesis.
RESULTS: Among the 37 included articles, 14 were without aging, 15 were natural or artificial accelerated aging, 7 were outdoor weathering, and 1 contained both artificial aging and outdoor weathering. Only 4 studies out of the 14 without aging had significant observations; whereas 9 articles with natural or artificial aging published significant results, and 3 out of 7 outdoor weathering articles showed significant changes in the evaluated silicone elastomers.
CONCLUSIONS: Despite the varying research, it seems that the single "ideal" maxillofacial prosthetic material that can provide sufficient resistance against different aging conditions is yet to be identified. Therefore, it is imperative for standardization organizations, the scientific community, and academia to develop modified prosthetic silicones possessing improved physical properties and color stability, limiting the clinical problems regarding degradation of maxillofacial prostheses.
MATERIALS AND METHODS: Candida albicans, Streptococcus mutans, and Staphylococcus aureus were incubated with modified and unmodified silicone groups (N = 35) for 30 days at 37°C. The counts of viable microorganisms in the accumulating biofilm layer were determined and converted to cfu/cm2 unit surface area. A scanning electron microscope (SEM) was used to evaluate the microbial adhesion. Statistical analysis was performed using t-test, one-way ANOVA, and post hoc tests as indicated.
RESULTS: Significant differences in microbial adhesion were observed between modified and unmodified silicone elastomers after the cells were incubated for 30 days (p < 0.001). SEM showed evident differences in microbial adhesion on modified silicone elastomer compared with unmodified silicone elastomer.
CONCLUSIONS: Surface modification of silicone elastomer yielding a smoother and less porous surface showed lower adhesion of different microorganisms than observed on unmodified surfaces.
MATERIALS AND METHODS: The overjet (measured clinically) and electromyographical activity (rest, chew, post chew rest, clench and post clench rest) of the masseter and temporalis muscle of class II malocclusion patient were assessed in 18 patients (3 males and 15 females) from the School of Dental Science, Hospital University Sains Malaysia.
RESULTS: The results were compared by simple linear regression test to evaluate the association between overjet and muscle activity in different genders. Class II malocclusion patients with increased overjet group showed significant association with masseter muscle activity on chewing stage (P = 0.005, F = 6.081 and adj-R2 = 0.473). Left temporalis muscle in class II malocclusion showed a significant linear association (P = 0.014, F = 0.812 and adj-R2= -0.034) with gender during clench.
CONCLUSION: In conclusion, class II malocclusion patient with increased overjet can affect masticatory muscle function and as well as clench force may differ in gender.
Materials and Methods: The study was performed using cell viability assay for mitochondrial dehydrogenase activity in stem cells from human exfoliated deciduous teeth (SHED), after 1, 2, and 3 days of exposure to the biomaterial extracts of varying concentrations. Differences in mean cell viability values were assessed by one-way analysis of variance, followed by Dunnett T3 post hoc test for multiple comparisons (P < 0.05).
Results: The cell viability to Gyp-CHT in low extract concentrations was statistically similar to that of the control and different from that of high extract concentrations. Gyp-5% CHT showed the highest percentage of cell viability with 110.92%, 108.56%, and 109.11%. The cell viability showed a tendency toward increment with low extract concentration and no constant effect of CHT on cell viability toward higher or lower.
Conclusions: Gyp-CHT biomaterial has no cytotoxic effects on the cultured SHED.