METHODS: Sixty-five cylindrical block of Fuji IX Fast were prepared using split moulds. The demineralizing solution was an acetate buffered demineralizing solution at pH 403. The remineralizing solution was a buffered solution containing 1.5 mM Ca, 0.9 mM P and 10 ppm F at pH 7. The blocks of Fuji IX Fast were subjected either to two-day alternating cycles of remineralization and demineralization for up to 24 days (test); 6 two-day cycles of demineralizing or remineralizing solution separately, or deionized distilled water alone (controls) or were left untreated (base line control). Mineral profiles of Ca, P, Sr and F within 100 microm of the material surface were assessed following 8, 16 and 24 days of treatment (test); 4, 8 or 12 days (controls) or for baseline control samples, using electron probe microanalysis (EPMA).
RESULTS: There were significant changes in mineral profile in the test specimens in terms of Sr and Ca concentrations. A molecule for molecule exchange of these elements resulted between GIC and eluant solutions. Fluoride loss from the GIC occurredto the level comparable with uptake levels recorded in eluant solutions from previous studies. The ionic exchanges appeared to be the result of dissolution followed by an equilibrium-driven diffusion. These exchanges were superficial though substantial.
CONCLUSIONS: Simulated exposure of Fuji IX to the oral environment resulted in an exchange of Ca from the bathing solutions into Fuji IX to replace any Sr which was lost to the GIC. Fluorine loss from the GIC followed previously described patterns. The possible clinical significance of this exchange was discussed.
Results: A significant difference (p < 0.001) of mean debonding force was found between different types of teeth in vivo. Clinically, ARI scores were not significantly different (p = 0.921) between different groups, but overall higher scores were predominant.
Conclusion: Bracket debonding force should be measured on the same tooth from the same arch as the significant difference of mean debonding force exists between similar teeth of the upper and lower arches. The insignificant bracket failure pattern with higher ARI scores confirms less enamel damage irrespective of tooth types.
MATERIALS AND METHODS: PubMed and Semantic Scholar databases were scoured for articles using 10 search terms. In vitro studies satisfying the inclusion criteria were probed which were meticulously screened and scrutinized for eligibility adhering to the 11 exclusion criteria. The quality assessment tool for in vitro studies (QUIN Tool) containing 12 criteria was employed to assess the risk of bias (RoB).
RESULTS: A total of 48 studies assessing shear bond strength (SBS) and 15 studies evaluating tensile bond strength (TBS) were included in the qualitative synthesis. Concerning SBS, 33.4% moderate and 66.6% high RoB was observed. Concerning TBS, 26.8% moderate and 73.2% high RoB was discerned. Seventeen and two studies assessing SBS and TBS, respectively, were included in meta-analyses.
CONCLUSIONS: Shear bond strength and TBS increased for the primed alloys. Cyclic disulfide primer is best-suited for noble alloys when compared with thiol/thione primers. Phosphoric acid- and phosphonic acid ester-based primers are opportune for base alloys.
CLINICAL SIGNIFICANCE: The alloy-resin interface (ARI) would fail if an inappropriate primer was selected. Therefore, the selection of an appropriate alloy adhesive primer for an alloy plays a crucial role in prosthetic success. This systematic review would help in the identification and selection of a congruous primer for a selected alloy.
METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.
RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.
CONCLUSION: Different luting agents have an influence on the fracture resistance of Procera AllCeram copings.
AIM: To evaluate the shear bond strength of Zinc phosphate cement Elite, glass ionomer cement Fuji I, resin-modified glass ionomer cement Fuji Plus and resin luting cement Panavia-F to Turkom-Cera all-ceramic material.
MATERIALS AND METHODS: Turkom-Cera was used to form discs 10mm in diameter and 3 mm in thickness (n = 40). The ceramic discs were wet ground, air - particle abraded with 50 - μm aluminium oxide particles and randomly divided into four groups (n = 10). The luting cement was bonded to Turkom-Cera discs as per manufacturer instructions. The shear bond strengths were determined using the universal testing machine at a crosshead speed of 0.5 mm/min. The data were analysed using the tests One Way ANOVA, the nonparametric Kruskal - Wallis test and Mann - Whitney Post hoc test.
RESULTS: The shear bond strength of the Elite, Fuji I, Fuji Plus and Panavia F groups were: 0.92 ± 0.42, 2.04 ± 0.78, 4.37 ± 1.18, and 16.42 ± 3.38 MPa, respectively. There was the statistically significant difference between the four luting cement tested (p < 0.05).
CONCLUSION: the phosphate-containing resin cement Panavia-F exhibited shear bond strength value significantly higher than all materials tested.
METHODS: Six makes, three each monocrystalline (M) and polycrystalline (P) were used; PureSapphire (M), SPA Aesthetic (M), Ghost (M), Mist (P), Reflections (P), and Dual Ceramic (P). The Ortholux™ Light Curing Unit (LCU) was used to cure the orthodontic adhesive Transbond™XT. The LCU's tip irradiance was measured and TLE transmitted through the ceramic bracket was obtained, then adhesive added to the bracket, and transmitted TLE measured through bracket-plus-adhesive samples. The LCU was set at five seconds as recommended for curing adhesive through ceramic brackets.
RESULTS: Mean tip irradiance was 1859.2±16.2mW/cm2. The TLE transmitted through brackets alone ranged 1.7 to 3.9J/cm2, in the descending order: Ghost>Pure Sapphire>Reflections>Mist>SPA Aesthetics>Dual Ceramic. The TLE transmitted through bracket-plus-adhesive samples ranged 1.6 to 3.7J/cm2, in the descending order: Ghost>Mist>Reflections>Pure Sapphire>SPA Aesthetics>Dual Ceramic. TLE was reduced with the addition of adhesive (range -0.1 to -0.7J/cm2). There was a significant difference for Pure Sapphire, Reflections, and Mist (P<0.05), but not for SPA Aesthetics, Ghost, and Dual Ceramic. There was no overall significant difference between the monocrystalline and polycrystalline makes. The two best makes were of the monocrystalline type, concerning TLE transmission, but with the exception of polycrystalline Dual Ceramic; the next worst make was a monocrystalline bracket, SPA Aesthetics.
CONCLUSION: Light energy attenuation through ceramic orthodontic brackets is make-dependent, with no overall difference between monocrystalline and polycrystalline brackets. Light energy is further attenuated with the addition of resin-based orthodontic adhesive.
Materials and Methods: One hundred and sixty endodontically treated maxillary central incisors embedded in acrylic resin with decoronated root portion were taken for the study. The postspaces were prepared according to standard protocol. The samples were divided into two groups according to the post material: glass-fiber post and Quartz fiber post. These groups were further subdivided on the basis of coronal extension of 4 and 6 mm for glass fiber and Quartz fiber posts, respectively. The posts were then luted with dual-polymerizing resin cement followed by core buildup. Samples were subjected to increasing compressive oblique load until fracture occurred in a universal testing machine. Data were analyzed with one-way ANOVA and independent Student's t-test. Analysis was done using SPSS version 15 (SPSS Inc., Chicago, IL, USA) Windows software program.
Results: Glass fiber post with coronal extension of 4 mm (182.8 N) showed better results than with 6-mm length (124.1 N). Similarly, in quartz fiber posts group, 4-mm postlength (314 N) was better when compared with 6 mm (160 N). The 4-mm coronal extension of quartz fiber post displayed superior fracture resistance.
Conclusions: Glass fiber posts showed better fracture resistance than Quartz fiber posts. 4-mm coronal length showed more fracture resistance than 6 mm.
MATERIALS AND METHODS: A questionnaire consisting of 35 questions was distributed by mail or an online survey to 425 registered dentists selected according to place of work by stratified random sampling.
RESULTS: One hundred fifty-three dentists responded to the survey. A positive attitude towards FS and PRR was noted among most Malaysian dentists. About half of the respondents used FS/PRR occasionally (48.4%), while few (13.7%) applied them routinely. The majority of the dentists agreed that minimally invasive dentistry is important and FS are effective in caries prevention, using them on high caries-risk individuals. Most of the dentists used pumice or paste to clean teeth before placing FS/PRR. A significant number of dentists used a bonding agent prior to placing FS. Although only 57.5% dentists were aware of guidelines for FS use, most dentists agreed that guidelines are important.
CONCLUSION: Although there was a positive attitude towards FS/PRR, few dentists applied them routinely. Some of the steps undertaken for placement of FS and PRR were outdated. Updating local guidelines for dentists to ensure uniform practice of FS and PRR is justified.
MATERIALS AND METHODS: An experimental adhesive system based on bis-GMA, HEMA and hydrophobic monomer was doped with RF0.125 (RF - Riboflavin) or RF/VE-TPGS (0.25/0.50) and submitted to μTBS evaluation. Resin dentine slabs were prepared and examined using SEM and TEM. Adhesion force was analysed on ends of AFM cantilevers deflection. Quenched peptide assays were performed using fluorescence scanner and wavelengths set to 320nm and 405nm. Cytotoxicity was assessed using human peripheral blood mononuclear cell line. Molecular docking studies were carried out using Schrödinger small-molecule drug discovery suite 2018-2. Data from viable cell results was analyzed using one-way ANOVA. Bond strength values were analysed by two-way ANOVA. Nonparametric results were analyzed using a Kruskal-Wallis test at a 0.05 significance level.
RESULTS: RF/VE-TPGS0.25 groups showed highest bond strength results after 24-h storage in artificial saliva (p<0.05). RF/VE-TPGS0.50 groups showed increased bond strength after 12-months of ageing. RF/VE-TPGS modified adhesives showed appreciable presence of a hybrid layer. Packing fraction indicated solid angle profiles describing well sized density and topology relations for the RF/VE-TPGS adhesives, in particular with the RF/VE-TPGS0.50 specimens. Qualitative analysis of the phenotype of macrophages was prominently CD163+ in the RF/VE-TPGS0.50. Both the compounds showed favourable negative binding energies as expressed in terms of 'XP GScore'.
CONCLUSION: New formulations based on the incorporation of RF/VE-TPGS in universal adhesives may be of significant potential in facilitating penetration, distribution and uptake of riboflavin within the dentine surface.