METHODS: PubMed and Science Direct were searched for papers published between the years 1974 and 2018. The search was restricted to articles written in English related to modification of glass ionomer cements. Only articles published in peer-reviewed journals were included. The search included literature reviews, in vitro, and in vivo studies. Articles written in other languages, without available abstracts and those related to other field were excluded. About 198 peer-review articles in the English language were reviewed.
CONCLUSION: Based on the finding, most of the modification has improved physical-mechanical properties of glass ionomer cements. Recently, researchers have attempted to improve their antimicrobial properties. However, the attempts were reported to compromise the physical-mechanical properties of modified glass ionomer cements.
CLINICAL SIGNIFICANCE: As the modification of glass ionomer cement with different material improved the physical-mechanical and antimicrobial properties, it could be used as restorative material for wider application in dentistry.
METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.
RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.
CONCLUSION: Different luting agents have an influence on the fracture resistance of Procera AllCeram copings.
AIM: To evaluate the shear bond strength of Zinc phosphate cement Elite, glass ionomer cement Fuji I, resin-modified glass ionomer cement Fuji Plus and resin luting cement Panavia-F to Turkom-Cera all-ceramic material.
MATERIALS AND METHODS: Turkom-Cera was used to form discs 10mm in diameter and 3 mm in thickness (n = 40). The ceramic discs were wet ground, air - particle abraded with 50 - μm aluminium oxide particles and randomly divided into four groups (n = 10). The luting cement was bonded to Turkom-Cera discs as per manufacturer instructions. The shear bond strengths were determined using the universal testing machine at a crosshead speed of 0.5 mm/min. The data were analysed using the tests One Way ANOVA, the nonparametric Kruskal - Wallis test and Mann - Whitney Post hoc test.
RESULTS: The shear bond strength of the Elite, Fuji I, Fuji Plus and Panavia F groups were: 0.92 ± 0.42, 2.04 ± 0.78, 4.37 ± 1.18, and 16.42 ± 3.38 MPa, respectively. There was the statistically significant difference between the four luting cement tested (p < 0.05).
CONCLUSION: the phosphate-containing resin cement Panavia-F exhibited shear bond strength value significantly higher than all materials tested.
Materials and Methods: In this in-vitro study, a total of 48 single-rooted permanent human teeth were decoronated, and the roots were treated endodontically. Following post space preparation, the sample was divided into four groups (n= 12 each) based on the types of post and cement. Two different types of post [GC everStick®POST (ES) and Parapost® Fiber LuxTM (PF)], and two different types of cement [G-CEMTM (G), and RelyXTM Unicem (R)] were used according to the manufacturer's instructions. All roots were sectioned at the coronal and middle thirds with a thickness of 3±0.1mm. The Push-out bond strength (PBS) test was performed using a universal testing machine at a cross-head speed of 0.5mm/ min. The bond strength values were recorded, and the data were analyzed using the SPSS program. Apart from descriptive statistics, three-way ANOVA was used for the interaction of the independent variables (post, cement, and root level). For differences between the groups, the Mann-Whitney U test was used. A P-value of less than 0.05 was considered significant for all analyses.
Results: Push-out bond strength of samples at the middle level (11.38±10.31 MPa), with PF posts (11.18±9.98 MPa), and of those luted with RelyXTM Unicem cement (13.26±8.73 MPa) was higher than that of their counterparts. The PBS means of RelyXTM Unicem cement at both root levels were much higher than PBS means of G-CEMTM cement. Three-way ANOVA test revealed a significant effect for each variable with a higher effect of cement (Sum of Squares= 1310.690; P< 0.001). No significant difference (P= 0.153) was found between the coronal and middle parts and between ES and PF posts (P= 0.058). However, a highly significant difference (P< 0.001) was found between RelyXTM Unicem and G-CEMTM cements.
Conclusion: The type of cement had a significant effect on push-out bond strength with RelyXTM Unicem which had higher values than G-CEMTM. However, the type of post and root level had no significant effect on PBS, although Parapost® Fiber LuxTM and middle root level had higher values than their counterparts.
Objectives: The aim of this study is to evaluate the efficacy of dentin bonding agent (DBA) in preventing coronal discoloration caused by four different root canal sealers- MTA Fillapex, Sealapex, Zical and Z. O. B seal at different time intervals by measuring chromatic alterations using digital images analysis method.
Methodology: Ninety mandibular premolars were collected and sectioned at 1 mm below the cementoenamel junction. Standard access cavity preparations of dimensions (depth-3 mm, width-0.8 mm, and length-3 mm) were prepared with a No. 245 bur through the cervical access. Following the standard irrigation protocol, specimens were then randomly divided into nine groups (four groups without DBA [1-4] +4 groups with DBA [5-8] +1 negative control [9]). In Groups 1-4, four different root canal sealers (MTA Fillapex, Sealapex, Zical, and Z.O.B seal) were applied to the walls of the pulp chamber. For Groups 5-8, the samples were etched with 37% phosphoric acid and DBA application was done before the respective root canal sealer application. The cervical access in all specimens was sealed using glass ionomer cement. Digital photographs were taken under standard lighting and environmental conditions at different time intervals: preprocedural, postprocedural, and after 1, 2, 3, and 4 months. These images were analyzed using Adobe Photoshop CS6 from which laboratory values and subsequently Delta E values were obtained.
Results: Statistical analysis performed using repeated measures ANOVA and post hoc Tukey's tests show that the groups with DBA application had significantly lower mean Delta E values (P < 0.05) compared to the groups without DBA application.
Conclusion: DBAs applied to the dentinal walls of the pulp chamber before obturation can effectively reduce the sealer-induced coronal discoloration.