This is a review of the literature concerning wear related to the following materials used in dentistry: dental amalgam, composite resins, and glass-ionomer cements, as well as natural tooth substance. Discussions are included on both in vivo and in vitro studies in which various methods were used to help determine wear resistance.
Adhesive bond strength studies for the tray adhesive of an addition vinyl polysiloxane (President) impression material were conducted with an acrylic resin, chromium-plated brass, and plastic trays. Tensile and shear stress studies were performed on the Instron Universal testing machine. Acrylic resin specimens roughened with 80-grit silicon carbide paper exhibited appreciably higher bond strengths compared with different types of tray material and methods of surface preparation.
The mean strength that has traditionally been taken as a measurement of the strength of a material does not reflect the true strength, and therefore it cannot be used as a design parameter. This explains why many brittle materials fail at unpredictable stress, either below or above the mean strength. By using Weibull statistics, the prediction and assessment of strength can be made more sensibly. The performance of a material can be predicted by considering a stress at a lower level of failure probability.
The incidence of breakage of Piezon-Master ultrasonic K files were evaluated. Three groups of unused files were subjected to three treatments, namely; free vibration in air without irrigation, free vibration in root canal while minimizing contact with the wall of canal in the presence of irrigation and light filing in root canal with free flow of irrigation. Cavitation produced by files in contact and free of contact with a glass surface was examined in order to observe the relationship between cavitation defects and breakage. In addition, the fractured and unfractured files were examined under a scanning electron microscope for the presence of cavitation pits. The results indicated that more files broke in air. In water, a higher incidence of breakage occurred when files were allowed to freely vibrate while no breakage occurred when the files were used in filing. All files generated cavitation which resulted in pitting of their surfaces. However, it was considered unlikely that the pits contributed to fracture. Fatigue cracks which could be the result of the manufacturing process were observed at some of the corners of the cross sections of the fractured files and could be the main contributory factor to fracture.
In the fabrication of a bioprosthetic heart valve from bovine pericardial tissues, the tissues are subjected to suturing. The stress-strain response of sutured as well as unsutured strips of this tissue were examined. The stress-strain response was determined using a tensile-testing machine. It was found that suturing weakens the tissue in that sutured strips are more extensible, exhibit a lower stress at rupture and a lower final elastic modulus. In addition, it was also found that the bigger the suture/needle size used the greater the decrease in tissue strength. In all, tissue strength was observed to decrease by 22 to 59% in this study. The weakening of the tissue is attributed to the puncture holes created by the surgeon's needle which create regions of weakness. This response of bovine pericardial tissue to suturing should be given due consideration in the fabrication of a bioprosthetic heart valve using this tissue.
Microleakage testing has been used to determine the possible clinical performance of a restorative material. Many microleakage testing materials have been developed and performed through the years. There has been no agreement as to which testing methodology would give the most accurate results. Attempts have been made to simulate the oral conditions and to give a more quantitative representation of micro leakage. The different micro leakage testing methodologies are presented in this paper.
This study (1) compared the curing-light intensity with various barrier infection-control methods used to prevent cross contamination, (2) compared the Knoop hardness value of cured composite resin when various barrier control methods were used, and (3) correlated the hardness of the composite resin with the light-intensity output when different infection-control methods were used. The light-cure unit tips were covered with barriers, such as cellophane wrap, plastic gloves, Steri-shields, and finger cots. The control group had no barrier. Composite resins were then cured for each of the five groups, and their Knoop hardness values recorded. The results showed that there was significant statistical difference in the light-intensity output among the five groups. However, there was no significant statistical difference in the Knoop hardness values among any of the groups. There was also no correlation between the Knoop hardness value of the composite resin with the light-intensity output and the different infection-control methods. Therefore, any of the five infection-control methods could be used as barriers for preventing cross-contamination of the light-cure unit tip, for the light-intensity output for all five groups exceeded the recommended value of 300 W/m2. However, to allow a greater margin of error in clinical situations, the authors recommend that the plastic glove or the cellophane wrap be used to wrap the light-cure tip, since these barriers allowed the highest light-intensity output.
Stainless steel wrought wires used as clasp arms for removable partial dentures in Thailand were compared with those used in some other countries (in the as-received condition) in terms of flexibility, Vickers microhardness and composition. The results showed that there were significant differences (P< or =0.05) among the wires. A Japanese stainless steel wire (SK) was obviously different from the others. It had the lowest proportional limit and microhardness, but its flexibility was almost the same. The chemical composition of each wire was not greatly different. The wires were about 18-20 wt% chromium and 8-9 wt% nickel, except for the SK wire, which had about 12 wt% nickel.
PURPOSE: The impact strength and the flexural properties of denture base materials are of importance in predicting their clinical performance upon sudden loading. This study compares the impact and transverse strengths and the flexural modulus of three denture base polymers.
MATERIALS AND METHODS: The investigation included a relatively new microwave-polymerized polyurethane-based denture material processed by an injection-molding technique, a conventional microwave-polymerized denture material, and a heat-polymerized compression-molded poly(methyl methacrylate) (PMMA) denture material. Impact strength was determined using a Charpy-type impact tester. The transverse strength and the flexural modulus were assessed with a three-point bending test. The results were subjected to statistical analysis using a one-way analysis of variance and the Scheffé test for comparison.
RESULTS: The impact strength of the microwave-polymerized injection-molded polymer was 6.3 kl/m2, while its flexural strength was 66.2 MPa. These values were lower than those shown by the two compression-molded PMMA-based polymers. The differences were statistically significant. The flexural modulus of the new denture material was 2,832 MPa, which was higher than the conventional heat-polymerized polymer but was comparable to the other microwave-polymerized PMMA-based polymer. The difference in the flexural modulus was statistically significant.
CONCLUSION: In terms of the impact and flexural strengths, the new microwave-polymerized, injection-molded, polyurethane-based polymer offered no advantage over the existing heat- and microwave-polymerized PMMA-based denture base polymers. However, it has a rigidity comparable to that of the microwave-polymerized PMMA polymer.
Nanocomposites of Zn/Al-layered double hydroxide(anthraquinone-2,6-disulfonate) were synthesized by spontaneous direct assembly of inorganic and organic phases from aqueous solution. Powder X-ray diffraction patterns showed that a pure, single nanocomposite phase of good crystallinity was obtained using 1.0 M antraquinone-2,6-disulfonate ion (AQ26) and aging at 80 degrees C using conventional heating for 7 days or 0.5 h under microwave radiation, and these samples are denoted as ZAAN26C or ZAAN26MH, respectively. Zn/Al-nitrate-layered double hydroxide synthesized by a conventional method (ZANLC) showed a basal spacing of 8.3 A while both the nanocomposites showed 18.8 A as a result of AQ26 intercalation. FTIR study showed that the resulting nanocomposites are free from nitrate, the co-anion present in the mother liquor, indicating that only AQ26 is preferred during intercalation for the formation of the nanocomposite. The Brunauer, Emmet and Teller (BET) and micropore surface areas for ZAAN26C decreased relative to the ZANLC from 16.2 to 4.7 and 1.6 to 1.3 m2/g, respectively. These results indicate that AQ26 can be rapidly interdcalated in layered double hydroxide using microwave-aging resulting in a nanocomposite.
Hydrotalcite-like inorganic layers of Zn-Al, a host containing an organic moiety, 2,4-dichlorophenoxy-acetate, as a guest, was prepared by the spontaneous self-assembly method from an aqueous solution for the formation of a new layered organic-inorganic hybrid nanocomposite material. In this synthesis, the host- and guest-forming species were simultaneously included in the mother liquor, aged, and separated. Various Zn/Al ratios (R = 2, 3, and 4), concentrations of 2,4-dichlorophenoxyacetic acid (0.03-0.1 M), and pH (7 and 10) were studied to optimize the formation of the layered nancomposite. It was found that the optimum conditions for the formation of the nanocomposite were R = 4, pH 7, and concentration of 2,4-dichlorophenoxyacetic acid = 0.08 M. X-ray diffraction shows that this sample affords a nanolayered structure with a basal spacing of 24.6 A.
Biocompatibility of two variants of accelerated Portland cement (APC) were investigated in vitro by observing the cytomorphology of SaOS-2 osteosarcoma cells in the presence of test materials and the effect of these materials on the expression of markers of bone remodelling. Glass ionomer cement (GIC), mineral trioxide aggregate (MTA) and unmodified Portland cement (RC) were used for comparison. A direct contact assay was undertaken in four samples of each test material, collected at 12, 24, 48 and 72 h. Cell morphology was observed using scanning electron microscopy (SEM) and scored. Culture media were collected for cytokine quantification using enzyme-linked immunosorbent assay (ELISA). On SEM evaluation, healthy SaOS-2 cells were found adhering onto the surfaces of APC variant, RC and MTA. In contrast, rounded and dying cells were observed on GIC. Using ELISA, levels of interleukin (IL)-1beta, IL-6, IL-18 and OC were significantly higher in APC variants compared with controls and GIC (p<0.01), but these levels of cytokines were not statistically significant compared with MTA. The results of this study provide evidence that both APC variants are non-toxic and may have potential to promote bone healing. Further development of APC is indicated to produce a viable dental restorative material and possibly a material for orthopaedic
Tricalcium phosphate/hydroxyapatite (TCP/HA), hydroxyapatite (HA), chitosan and calcium sulphate (CaSO4) were studied and evaluated for possible bone tissue engineered construct acting as good support for osteogenic cells to proliferate, differentiate, and eventually spread and integrate into the scaffold. Surface morphology visualized by SEM showed that scaffold materials with additional fibrin had more cell densities attached than those without, depicting that the presence of fibrin and collagen fibers were truly a favourite choice of cells to attach. In comparison of various biomaterials used incorporated with fibrin, TCP/HA had the most cluster of cells attached.
The present paper reports on the influence of sintering temperature on the porosity and strength of porous hydroxyapatite (HA). HA powder was first prepared by the sol-gel precipitation method using calcium hydroxide and ortho-phosporic acid. The fine HA powder, measuring <50 microm was then mixed into a slurry with the addition of binder agent, being a mixture of sago and PVA. A small amount of sodium dodecyl sulphate was also used as a foaming agent. Porous HA samples were then prepared via slip casting technique. The surface morphology of the sintered samples was observed under scanning electron microscopy at 20 kV and the compositions were determined via SEM-EDX. A universal testing machine was used to determine the compaction strength of the sintered samples.
Metal implants such as titanium, stainless steel and Co-Cr-Mo are used for load bearing purposes such as hip joint prostheses, fixing plates and dental root implants. For practical application, plasma-sprayed coatings of hydroxyapatite (HA) on metal implants are applied to promote early formation of strong bonds between metal implant and living bone. Plasma spray coating involves heating of HA material to a semi-molten or molten state and then propels its to a metal substrate. The plasma flame temperature is in the range of 6,000 degrees C to 16,000 degrees C but the surface temperature of the substrate rarely exceeds 150 degrees C. The HA materials are feed into the spray gun in the form of powders. Furthermore, this paper will discuss the processes of plasma-sprayed coating of HA on various types of metal implants.
The human fibroblast MRC-5 cells incubated with PHB granules (TM) added at a final concentration of 4 mg/ml showed a time-course pattern of survival. The percentages of dead cells obtained were at the rate of 3.8% after 7 days, respectively. When the MRC-5 cells grown in different material, using the test concentration of 4 mg/ml PCM, they were found to show a similar time-course increasing pattern of death as that obtained with PHB. However, the death was noted in the cells incubated for 7 days, the death rates obtained was 40.54% respectively.
Defects were created in the mandible of a rabbit model whereby the right side was implanted with hydroxyapatite (HA) while the left side was left empty to act as control. Both the implant and control sites were evaluated clinically and histologically at 4,12,20,22 weeks. Decalcified sections were studied under confocal laser scanning microscope. No reactive cells were evident microscopically in all sections. There was bone ingrowth as early as 4 weeks when viewed by the topographic method. Enhancement of osteoconduction was evident by the presence of abundant capillaries, perivascular tissue and osteoprogenitor cells of the host. At 22 weeks, the implanted defect showed mature bone formation filling almost the whole field. This study demonstrated that the dense HA exhibits excellent biocompatibility as noted by the complete absence of reactive cells. It also promotes osteoconduction.
A study was conducted to investigate the effectiveness of freeze-dried bovine pericardium (FDBP) as a biomaterial in diaphragmatic herniorrhapy in dogs. Eight adult dogs were randomly selected and divided into two equal groups. In FDBP group, a diaphragmatic defect was induced and repaired with an identical size of FDBP. In the control group, a diaphragmatic wall was incised at three-side border creating a flap and sutured. Grossly, only mild intrathoracic adhesion was observed for most of the animals, and no herniation occured. Microscopically, the biomaterial incorporated into the host's tissue by ingrowth of young muscle fiber and massive new blood vessel formation in between the fibrous tissue.
The main objective of the study was to determine the biodegradability, resorption and osteoconductivity potency of coral implant. Coral blocks (CORAGRAF) were prepared from sea coral Porites species. The blocks were implanted in the right mandible of rabbit model. Implants were harvested at 2 and 4 weeks intervals and subjected for light and scanning electron microscopy. Dense hydroxyapatite (DHA) was implanted in the left mandible as a control. The results of this study demonstrated that CORAGRAF is a good implant material that can accelerates bone healing and be resorbed in an acceptable time. The mechanisms of the resorption seemed to be the same (crumbling process), a first step where the edge of the coral become powdery then a second step which could be phagocytosis and dissolution in extracellular fluid.