Abstract:

Sort:

Degree of conversion and physicomechanical properties of newly developed flowable composite derived from rice husk using urethane dimethacrylate monomer

Azlisham NAF, Johari Y, Mohamad D, Yhaya MF, Mahmood Z

Proc Inst Mech Eng H, 2023 Dec;237(12):1339-1347.
PMID: 38014749 DOI: 10.1177/09544119231208222

This study evaluated the use of urethane dimethacrylate (UDMA) as a base monomer to prepare the newly developed flowable composite (FC) using nanohybrid silica derived from rice husk in comparison to bisphenol A-glycidyl methacrylate (Bis-GMA) on the degree of conversion and physicomechanical properties. The different loadings of base monomer to diluent monomer were used at the ratio of 40:60, 50:50, and 60:40. The bonding analysis confirmed the presence of nanohybrid silica in the newly developed FC. Independent t-test revealed a statistically significant increase in the degree of conversion, depth of cure and Vickers hardness of the UDMA-based FC, while surface roughness showed comparable results between the two base monomers. In conclusion, UDMA-based FC demonstrated superior performance with 60%-65% conversions, a significantly higher depth of cure exceeding 1 mm which complies with the Internal Standard of Organization 4049 (ISO 4049), and a substantial increase in Vickers hardness numbers compared to Bis-GMA-based FC, making UDMA a suitable alternative to Bis-GMA as a base monomer in the formulation of this newly developed FC derived from rice husk.

Matched MeSH terms: Polyurethanes
Fabrication of calix[4]arene/polyurethane for the adsorptive removal of cationic dye from aqueous solutions

Ishak S, Rosly NZ, Abdullah AH, Alang Ahmad SA

Environ Monit Assess, 2023 Oct 12;195(11):1303.
PMID: 37828347 DOI: 10.1007/s10661-023-11909-z

Calix[4]arene/polyurethane (C4PU) has been synthesized and characterized as an alternative adsorbent for the adsorption of methylene blue (MB) and malachite green (MG) dyes from the aqueous solution. C4PU was synthesized by reacting p-tert-butyl calix[4]arene with hexamethylene diisocyanate (HMDI) as the cross-linking agent. Different polymer ratios were synthesized, and C4PU-4 shows better adsorption than other ratios. The polymer was characterized by Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), Brunauer-Emmett-Teller (BET) analysis, and point of zero charges (pHPZC). The isotherms and kinetics of the adsorption of MB and MG were studied under a range of experimental conditions, including pH, adsorbent dosage, initial dye concentration, and contact time. The adsorption was determined by the adsorption percentage of MB and MG dyes from the solution. The Langmuir isotherm model best describes the adsorption process for both dyes, and it follows a pseudo-second-order kinetic model, with the maximum adsorption capacity (qmax) of MB and MG, respectively, was found to be 1.991 mg·g-1 and 2.240 mg·g-1.

Matched MeSH terms: Polyurethanes
Biodegradable and antithrombogenic chitosan/elastin blended polyurethane electrospun membrane for vascular tissue integration

Selvaras T, Alshamrani SA, Gopal R, Jaganathan SK, Sivalingam S, Kadiman S, et al.

J Biomed Mater Res B Appl Biomater, 2023 Jun;111(6):1171-1181.
PMID: 36625453 DOI: 10.1002/jbm.b.35223

Current commercialized vascular membranes to treat coronary heart disease (CHD) such as Dacron and expanded polytetrafluoroethylene (ePTFE) have been associated with biodegradable and thrombogenic issues that limit tissue integration. In this study, biodegradable vascular membranes were fabricated in a structure of electrospun nanofibers composed of polyurethane (PU), chitosan (CS) and elastin (0.5%, 1.0%, and 1.5%). The physicochemical properties of the membranes were analyzed, followed by the conduction of several test analyses. The blending of CS and elastin has increased the fiber diameter, pore size and porosity percentage with the appearance of identical chemical groups. The wettability of PU membranes was enhanced up to 39.6%, demonstrating higher degradation following the incorporation of both natural polymers. The PU/CS/elastin electrospun membranes exhibited a controlled release of CS (Higuchi and first-order mechanisms) and elastin (Higuchi and Korsmeyer-Peppas mechanisms). Delayed blood clotting time was observed through both activated partial thromboplastin time (APTT) and partial thromboplastin time (PT) analyses where significantly delay of 26.8% APTT was recorded on the PU membranes blended with CS and elastin, in comparison with the PU membranes, supporting the membrane's antithrombogenic properties. Besides, these membranes produced a minimum of 2.6 ± 0.1 low hemolytic percentage, projecting its hemocompatibility to be used as vascular membrane.

Matched MeSH terms: Polyurethanes/chemistry
Fulltext Polyurethane Elastomer Layered Nanocomposite Material for Sports Grounds and the Preparation Method Thereof

Ren C, Su Z, Su Y, Wang L

Biomed Res Int, 2022;2022:5152911.
PMID: 36093408 DOI: 10.1155/2022/5152911

Polyurethane, as a rubber material, can relieve the load on the ground and provide seismic design for the venue, which is of great significance for sports venues. In order to improve the seismic resistance and abrasion resistance of materials for sports fields and reduce accidents in sports, this article has carried out research on the polyurethane elastomer layered nanocomposites for sports fields and their preparation. Today's world is a challenging era of science and technology. The fields of biotechnology, information, medicine, energy, environment, and national defense and security are closely related to the development of high tech, and the requirements for materials are becoming increasingly diversified. Polymer nanocomposite coating has the dual characteristics of organic and inorganic components. It not only retains the advantages of a polymer but also endows it with versatility. It meets the current application needs. It is a hot spot in today's research. Among them, there are two major problems in the composite process of nanomaterials and polymers: dispersion and compatibility. How to improve the dispersion of nanoparticles and enhance the compatibility between nanoparticles and polymers is an urgent problem to be solved. In the method part, this article introduces a small amount of polyurethane and polyurethane elastomers formed after polyurethane modification and introduces layered compounds and nanocomposites and introduces several models involved in nanomaterials in terms of algorithms. In the analysis part, this paper conducts a comprehensive analysis of the hard segment mass fraction, mechanical properties, thermal decomposition behavior, degradation mechanism, and dynamic mechanical properties. With the increase of GO content, the tensile strength increases significantly and the elongation at break becomes smaller and smaller. When the GO content increases from 0% to 2%, the tensile properties of the WPU film increase from 2.6 MPa to 7.9 MPa and the fracture of the elongation decreased from 201.7% to 62.8%. This shows that the increase in GO content will make the composite material harder and brittle. It can be seen from the experimental results that the preparation of the polyurethane elastomer layered nanocomposite material designed in this paper has a good application effect on sports venues.

Matched MeSH terms: Polyurethanes
Compression and tension behavior of the prosthetic foam materials polyurethane, EVA, Pelite™ and a combination of polyurethane and EVA: a preliminary study

Lutfi SNN, Abd Razak NA, Ali S, Gholizadeh H

Biomed Tech (Berl), 2021 Jun 25;66(3):317-322.
PMID: 34062632 DOI: 10.1515/bmt-2019-0110

Materials with low-strength and low-impedance properties, such as elastomers and polymeric foams are major contributors to prosthetic liner design. Polyethylene-Light (Pelite™) is a foam liner that is the most frequently used in prosthetics but it does not cater to all amputees' limb and skin conditions. The study aims to investigate the newly modified Foam Liner, a combination of two different types of foams (EVA + PU + EVA) as the newly modified Foam Liner in terms of compressive and tensile properties in comparison to Pelite™, polyurethane (PU) foam, and ethylene-vinyl acetate (EVA) foam. Universal testing machine (AGS-X, Shimadzu, Kyoto, Japan) has been used to measure the tensile and compressive stress. Pelite™ had the highest compressive stress at 566.63 kPa and tensile stress at 1145 kPa. Foam Liner fell between EVA and Pelite™ with 551.83 kPa at compression and 715.40 kPa at tension. PU foam had the lowest compressive stress at 2.80 kPa and tensile stress at 33.93 kPa. Foam Liner has intermediate compressive elasticity but has high tensile elasticity compared to EVA and Pelite™. Pelite™ remains the highest in compressive and tensile stiffness. Although it is good for amputees with bony prominence, constant pressure might result in skin breakdown or ulcer. Foam Liner would be the best for amputees with soft tissues on the residual limbs to accommodate movement.

Matched MeSH terms: Polyurethanes*
Bio-based Poly(hydroxy urethane)s: Synthesis and Pre/Post-Functionalization

Mhd Haniffa MAC, Munawar K, Ching YC, Illias HA, Chuah CH

Chem Asian J, 2021 Jun 01;16(11):1281-1297.
PMID: 33871151 DOI: 10.1002/asia.202100226

New and emerging demand for polyurethane (PU) continues to rise over the years. The harmful isocyanate binding agents and their integrated PU products are at the height of environmental concerns, in particular PU (macro and micro) pollution and their degradation problems. Non-isocyanate poly(hydroxy urethane)s (NIPUs) are sustainable and green alternatives to conventional PUs. Since the introduction of NIPU in 1957, the market value of NIPU and its hybridized materials has increased exponentially in 2019 and is expected to continue to rise in the coming years. The secondary hydroxyl groups of these NIPU's urethane moiety have revolutionized them by allowing for adequate pre/post functionalization. This minireview highlights different strategies and advances in pre/post-functionalization used in biobased NIPU. We have performed a comprehensive evaluation of the development of new ideas in this field to achieve more efficient synthetic biobased hybridized NIPU processes through selective and kinetic understanding.

Matched MeSH terms: Polyurethanes/chemical synthesis*; Polyurethanes/chemistry
Fulltext Effect of Cellulose Nanofibrils on the Properties of Jatropha Oil-Based Waterborne Polyurethane Nanocomposite Film

Amri MR, Guan CT, Osman Al-Edrus SS, Md Yasin F, Mohamad SF

Polymers (Basel), 2021 Apr 30;13(9).
PMID: 33946517 DOI: 10.3390/polym13091460

The objective of this work was to study the influence of cellulose nanofibrils (CNF) on the physical, mechanical, and thermal properties of Jatropha oil-based waterborne polyurethane (WBPU) nanocomposite films. The polyol to produce polyurethane was synthesized from crude Jatropha oil through epoxidation and ring-opening method. The chain extender, 1,6-hexanediol, was used to improve film elasticity by 0.1, 0.25, and 0.5 wt.% of CNF loading was incorporated to enhance film performance. Mechanical performance was studied using a universal test machine as specified in ASTM D638-03 Type V and was achieved by 0.18 MPa at 0.5 wt.% of CNF. Thermal gravimetric analysis (TGA) was performed to measure the temperature of degradation and the chemical crosslinking and film morphology were studied using Fourier-transform infrared spectroscopy (FTIR) and field emission scanning electron microscopy (FESEM). The results showed that when the CNF was incorporated, it was found to enhance the nanocomposite film, in particular its mechanical and thermal properties supported by morphology. Nanocomposite film with 0.5 wt.% of CNF showed the highest improvement in terms of tensile strength, Young's modulus, and thermal degradation. Although the contact angle decreases as the CNF content increases, the effect on the water absorption of the film was found to be relatively small (<3.5%). The difference between the neat WPBU and the highest CNF loading film was not more than 1%, even after 5 days of being immersed in water.

Matched MeSH terms: Polyurethanes
Fulltext Chemical and Thermo-Mechanical Properties of Waterborne Polyurethane Dispersion Derived from Jatropha Oil

Saalah S, Abdullah LC, Aung MM, Salleh MZ, Awang Biak DR, Basri M, et al.

Polymers (Basel), 2021 Mar 05;13(5).
PMID: 33807622 DOI: 10.3390/polym13050795

Nowadays, there is a significant trend away from solvent-based polyurethane systems towards waterborne polyurethane dispersions due to government regulations requiring manufacturers to lower total volatile organic compounds, as well as consumer preference for more environmentally friendly products. In this work, a renewable vegetable oil-based polyol derived from jatropha oil was polymerized with isophorone diisocyanate and dimethylol propionic acid to produce anionic waterborne polyurethane dispersion. Free standing films with up to 62 wt.% bio-based content were successfully produced after evaporation of water from the jatropha oil-based waterborne polyurethane (JPU) dispersion, which indicated good film formation. The chemical and thermo-mechanical properties of the JPU films were characterized. By increasing the OH numbers of polyol from 161 mgKOH/g to 217 mgKOH/g, the crosslinking density of the JPU was significantly increased, which lead to a better storage modulus and improved hydrophobicity. Overall, JPU produced from polyol having OH number of 217 mgKOH/g appears to be a promising product for application as a binder for wood and decorative coatings.

Matched MeSH terms: Polyurethanes
Fulltext Optimisation of Epoxide Ring-Opening Reaction for the Synthesis of Bio-Polyol from Palm Oil Derivative Using Response Surface Methodology

Kamairudin N, Hoong SS, Abdullah LC, Ariffin H, Biak DRA

Molecules, 2021 Jan 27;26(3).
PMID: 33513686 DOI: 10.3390/molecules26030648

The development of bio-polyol from vegetable oil and its derivatives is gaining much interest from polyurethane industries and academia. In view of this, the availability of methyl oleate derived from palm oil, which is aimed at biodiesel production, provides an excellent feedstock to produce bio-polyol for polyurethane applications. In this recent study, response surface methodology (RSM) with a combination of central composite rotatable design (CCRD) was used to optimise the reaction parameters in order to obtain a maximised hydroxyl value (OHV). Three reaction parameters were selected, namely the mole ratio of epoxidised methyl oleate (EMO) to glycerol (1:5-1:10), the amount of catalyst loading (0.15-0.55%) and reaction temperature (90-150 °C) on a response variable as the hydroxyl value (OHV). The analysis of variance (ANOVA) indicated that the quadratic model was significant at 98% confidence level with (p-value > 0.0001) with an insignificant lack of fit and the regression coefficient (R2) was 0.9897. The optimum reaction conditions established by the predicted model were: 1:10 mole ratio of EMO to glycerol, 0.18% of catalyst and 120 °C reaction temperature, giving a hydroxyl value (OHV) of 306.190 mg KOH/g for the experimental value and 301.248 mg KOH/g for the predicted value. This result proves that the RSM model is capable of forecasting the relevant response. FTIR analysis was employed to monitor the changes of functional group for each synthesis and the confirmation of this finding was analysed by NMR analysis. The viscosity and average molecular weight (MW) were 513.48 mPa and 491 Da, respectively.

Matched MeSH terms: Polyurethanes/chemistry
Recent advances in tissue engineering scaffolds based on polyurethane and modified polyurethane

Naureen B, Haseeb ASMA, Basirun WJ, Muhamad F

Mater Sci Eng C Mater Biol Appl, 2021 Jan;118:111228.
PMID: 33254956 DOI: 10.1016/j.msec.2020.111228

Organ repair, regeneration, and transplantation are constantly in demand due to various acute, chronic, congenital, and infectious diseases. Apart from traditional remedies, tissue engineering (TE) is among the most effective methods for the repair of damaged tissues via merging the cells, growth factors, and scaffolds. With regards to TE scaffold fabrication technology, polyurethane (PU), a high-performance medical grade synthetic polymer and bioactive material has gained significant attention. PU possesses exclusive biocompatibility, biodegradability, and modifiable chemical, mechanical and thermal properties, owing to its unique structure-properties relationship. During the past few decades, PU TE scaffold bioactive properties have been incorporated or enhanced with biodegradable, electroactive, surface-functionalised, ayurvedic products, ceramics, glass, growth factors, metals, and natural polymers, resulting in the formation of modified polyurethanes (MPUs). This review focuses on the recent advances of PU/MPU scaffolds, especially on the biomedical applications in soft and hard tissue engineering and regenerative medicine. The scientific issues with regards to the PU/MPU scaffolds, such as biodegradation, electroactivity, surface functionalisation, and incorporation of active moieties are also highlighted along with some suggestions for future work.

Matched MeSH terms: Polyurethanes*
Development of thermal insulation sandwich panels containing end-of-life vehicle (ELV) headlamp and seat waste

Wong YC, Mahyuddin N, Aminuddin AMR

Waste Manag, 2020 Dec;118:402-415.
PMID: 32947219 DOI: 10.1016/j.wasman.2020.08.036

Recycling automotive waste has increasingly become an alternative solution towards producing sustainable materials given the rising issue of raw material shortages and waste management challenges at global level. The improper end-of-life vehicle (ELV) waste management poses detrimental impacts on the environment. This paper proposes a novel method to develop thermal insulation sandwich panels using ELV waste, motivated by the critical needs of creating high-performance thermal insulation for buildings. Six sandwich panels (P1-P6) of different weight and ratio of shredded ELV particles were manufactured. The sandwich panels structure was made of three layers: a core, and a glass face sheet bonded to each side. The core structure composed of Polycarbonate (PC) from headlamp lenses and polyurethane (PU) from seat, bonded using resin casting approach. Thermal conductivity of the samples was measured using guarded hot-plate apparatus. Results corroborated that thermal conductivity of ELV-based sandwich panels reduced remarkably compared to panel without ELVs, recorded at 15.51% reduction. Composition gives the best thermal performance was made of mixed ELV core materials of ratio 50%PC:50%PU, it has a thermal conductivity value of 0.1776 W/mK. The transparency data were obtained using Haze-gard plus haze meter. The best luminous transmittance value was exhibited by P2 (100% PC), 67.47%. The best clarity value and haze value were shown by P6 (25% PC: 75% PU), 55.13% and 52.6% respectively. ELV waste can be recycled to develop useful sustainable thermal insulation to improve thermal and optical transparency performance of buildings as a substitute for conventional materials which have a relevance for future façade concepts.

Matched MeSH terms: Polyurethanes
Development and physicochemical analysis of genipin-crosslinked gelatine sponge as a potential resorbable nasal pack

Selvarajah J, Mh Busra MF, Bin Saim A, Bt Hj Idrus R, Lokanathan Y

J Biomater Sci Polym Ed, 2020 09;31(13):1722-1740.
PMID: 32458725 DOI: 10.1080/09205063.2020.1774841

Nasal injury following nasal surgery is an adverse consequence, and prompt treatment should be initiated. Nasal packing, either non-absorbable or absorbable, are commonly used after nasal surgery to prevent bleeding and promote wound healing. In the current study, a novel gelatine sponge crosslinked with genipin was evaluated for suitability to be used as nasal packing and compared to one of the frequently used commercial nasal packing made up of polyurethane. Gelatine at 7% and 10% (w/v) concentration were crosslinked with varying concentrations of genipin, 0.5%, 0.25%, and 0.2% (v/v). The gelatine sponges were further characterised by its water uptake ability, biodegradation, water vapour transmission rate, porosity, contact angle, chemical composition, crosslinking degree, and mechanical properties. The gelatine sponges absorbed five times more water than their dry weight and were degraded within five days. The water vapour transmission rate of the gelatine sponges was 1187.7 ± 430.2 g/(m-2 day) for 7% gelatine and 779.4 ± 375.5 g/(m-2 day) for 10% gelatine. Crosslinking of gelatine with genipin resulted in lower porosity and did not affect the wettability of gelatine sponge (contact angle: 95.3 ± 12.1° for 7% gelatine and 88.4 ± 7.2° for 10% gelatine). In terms of biodegradability, the gelatine sponges took 24-48 h to degrade completely. Genipin crosslinking improved the degradation resistance and mechanical strength of gelatine sponge. The physical and chemical properties of the gelatine sponge, i.e. biodegradability and mechanical durability, support its potential as nasal packing.

Matched MeSH terms: Polyurethanes
Fulltext A Green Approach to Modify Surface Properties of Polyurethane Foam for Enhanced Oil Absorption

Ng ZC, Roslan RA, Lau WJ, Gürsoy M, Karaman M, Jullok N, et al.

Polymers (Basel), 2020 Aug 21;12(9).
PMID: 32825561 DOI: 10.3390/polym12091883

The non-selective property of conventional polyurethane (PU) foam tends to lower its oil absorption efficiency. To address this issue, we modified the surface properties of PU foam using a rapid solvent-free surface functionalization approach based on the chemical vapor deposition (CVD) method to establish an extremely thin yet uniform coating layer to improve foam performance. The PU foam was respectively functionalized using different monomers, i.e., perfluorodecyl acrylate (PFDA), 2,2,3,4,4,4-hexafluorobutyl acrylate (HFBA), and hexamethyldisiloxane (HMDSO), and the effect of deposition times (1, 5 and 10 min) on the properties of foam was investigated. The results showed that all the modified foams demonstrated a much higher water contact angle (i.e., greater hydrophobicity) and greater absorption capacities compared to the control PU foam. This is due to the presence of specific functional groups, e.g., fluorine (F) and silane (Si) in the modified PU foams. Of all, the PU/PHFBAi foam exhibited the highest absorption capacities, recording 66.68, 58.15, 53.70, and 58.38 g/g for chloroform, acetone, cyclohexane, and edible oil, respectively. These values were 39.19-119.31% higher than that of control foam. The promising performance of the PU/PHFBAi foam is due to the improved surface hydrophobicity attributed to the original perfluoroalkyl moieties of the HFBA monomer. The PU/PHFBAi foam also demonstrated a much more stable absorption performance compared to the control foam when both samples were reused for up to 10 cycles. This clearly indicates the positive impact of the proposed functionalization method in improving PU properties for oil absorption processes.

Matched MeSH terms: Polyurethanes
Fulltext Production of Biodegradable Palm Oil-Based Polyurethane as Potential Biomaterial for Biomedical Applications

Yeoh FH, Lee CS, Kang YB, Wong SF, Cheng SF, Ng WS

Polymers (Basel), 2020 Aug 17;12(8).
PMID: 32824514 DOI: 10.3390/polym12081842

Being biodegradable and biocompatible are crucial characteristics for biomaterial used for medical and biomedical applications. Vegetable oil-based polyols are known to contribute both the biodegradability and biocompatibility of polyurethanes; however, petrochemical-based polyols were often incorporated to improve the thermal and mechanical properties of polyurethane. In this work, palm oil-based polyester polyol (PPP) derived from epoxidized palm olein and glutaric acid was reacted with isophorone diisocyanate to produce an aliphatic polyurethane, without the incorporation of any commercial petrochemical-based polyol. The effects of water content and isocyanate index were investigated. The polyurethanes produced consisted of > 90% porosity with interconnected micropores and macropores (37-1700 µm) and PU 1.0 possessed tensile strength and compression stress of 111 kPa and 64 kPa. The polyurethanes with comparable thermal stability, yet susceptible to enzymatic degradation with 7-59% of mass loss after 4 weeks of treatment. The polyurethanes demonstrated superior water uptake (up to 450%) and did not induce significant changes in pH of the medium. The chemical changes of the polyurethanes after enzymatic degradation were evaluated by FTIR and TGA analyses. The polyurethanes showed cell viability of 53.43% and 80.37% after 1 and 10 day(s) of cytotoxicity test; and cell adhesion and proliferation in cell adhesion test. The polyurethanes produced demonstrated its potential as biomaterial for soft tissue engineering applications.

Matched MeSH terms: Polyurethanes
Fulltext Comparative Study of Aromatic and Cycloaliphatic Isocyanate Effects on Physico-Chemical Properties of Bio-Based Polyurethane Acrylate Coatings

Mudri NH, Abdullah LC, Aung MM, Salleh MZ, Awang Biak DR, Rayung M

Polymers (Basel), 2020 Jul 03;12(7).
PMID: 32635384 DOI: 10.3390/polym12071494

Crude jatropha oil (JO) was modified to form jatropha oil-based polyol (JOL) via two steps in a chemical reaction known as epoxidation and hydroxylation. JOL was then reacted with isocyanates to produce JO-based polyurethane resin. In this study, two types of isocyanates, 2,4-toluene diisocyanate (2,4-TDI) and isophorone diisocyanate (IPDI) were introduced to produce JPUA-TDI and JPUA-IPDI respectively. 2,4-TDI is categorised as an aromatic isocyanate whilst IPDI is known as a cycloaliphatic isocyanate. Both JPUA-TDI and JPUA-IPDI were then end-capped by the acrylate functional group of 2-hydroxyethyl methacrylate (HEMA). The effects of that isocyanate structure were investigated for their physico, chemical and thermal properties. The changes of the functional groups during each synthesis step were monitored by FTIR analysis. The appearance of urethane peaks was observed at 1532 cm-1, 1718 cm-1 and 3369 cm-1 while acrylate peaks were detected at 815 cm-1 and 1663 cm-1 indicating that JPUA was successfully synthesised. It was found that the molar mass of JPUA-TDI was doubled compared to JPUA-IPDI. Each resin showed a similar degradation pattern analysed by thermal gravimetric analysis (TGA). For the mechanical properties, the JPUA-IPDI-based coating formulation exhibited a higher hardness value but poor adhesion compared to the JPUA-TDI-based coating formulation. Both types of jatropha-based polyurethane acrylate may potentially be used in an ultraviolet (UV) curing system specifically for clear coat surface applications to replace dependency on petroleum-based chemicals.

Matched MeSH terms: Polyurethanes
Fulltext Performance Analysis of Jatropha Oil-Based Polyurethane Acrylate Gel Polymer Electrolyte for Dye-Sensitized Solar Cells

Rayung M, Aung MM, Su'ait MS, Chuah Abdullah L, Ahmad A, Lim HN

ACS Omega, 2020 Jun 23;5(24):14267-14274.
PMID: 32596563 DOI: 10.1021/acsomega.9b04348

Biobased polymers are useful materials in substituting conventional petroleum-derived polymers because of their good properties, ready availability, and abundance in nature. This study reports a new jatropha oil-based gel polymer electrolyte (GPE) for use in dye-sensitized solar cells (DSSCs). The GPE was prepared by mixing jatropha oil-based polyurethane acrylate (PUA) with different concentrations of lithium iodide (LiI). The GPE was characterized by infrared spectroscopy, thermal analysis, lithium nuclear magnetic resonance analysis, electrochemical analysis, and photocurrent conversion efficiency. The highest room-temperature ionic conductivity of 1.88 × 10-4 S cm-1 was obtained at 20 wt % of LiI salt. Additionally, the temperature-dependent ionic conductivity of the GPE exhibited Arrhenius behavior with an activation energy of 0.42 eV and a pre-exponential factor of 1.56 × 103 S cm-1. The electrochemical stability study showed that the PUA GPE was stable up to 2.35 V. The thermal stability of the gel electrolyte showed an improvement after the addition of the salt, suggesting a strong intermolecular interaction between PUA and Li, which leads to polymer-salt complexation, as proven by Fourier transform infrared spectroscopy analysis. A DSSC has been assembled using the optimum ionic conductivity gel electrolyte which indicated 1.2% efficiency under 1 sun condition. Thus, the jatropha oil-based GPE demonstrated favorable properties that make it a promising alternative to petroleum-derived polymer electrolytes in DSSCs.

Matched MeSH terms: Polyurethanes
Fulltext Characterization and Performance Evaluation of Cellulose Acetate-Polyurethane Film for Lead II Ion Removal

Iqhrammullah M, Marlina M, Khalil HPSA, Kurniawan KH, Suyanto H, Hedwig R, et al.

Polymers (Basel), 2020 Jun 09;12(6).
PMID: 32526903 DOI: 10.3390/polym12061317

Global pollution from toxic metal waste has resulted in increased research on toxic metal adsorption. A cellulose acetate-polyurethane (CA-PU) film adsorbent was successfully prepared in this research. The cellulose acetate-polyurethane film adsorbent was prepared with a polycondensation reaction between cellulose acetate and methylene diphenyl diisocyanate. The CA-PU bond formation was confirmed by functional group analysis obtained from Fourier transform infrared (FTIR) spectroscopy. The obtained film was characterized for improved tensile and thermal properties with the addition of methylene diphenyl diisocyanate (MDI). The adsorption ability of the obtained film was evaluated with laser-induced breakdown spectroscopy (LIBS). The best film adsorbent from the LIBS was selected and studied for adsorption isotherm. The FTIR analysis confirmed the formation of the CA-PU bond from the polycondensation between cellulose acetate and the methylene diphenyl diisocyanate. The result showed that the addition of methylene diphenyl diisocyanate (MDI) resulted in the urethane network's growth. The characterization result showed an improvement in the morphology, thermal stability, and tensile strength of the film. The LIBS studies showed improvement in the adsorption of Pb2+ with CA-PU compared with the neat CA. The isotherm studies revealed that Pb2+ adsorption by cellulose acetate-polyurethane film adsorbent was heterogeneously dependent on the Freundlich isotherm model (R2 = 0.97044). Overall, the polycondensation method proposed by this study enhanced the Pb2+ removal, and was comparable to those reported in previous studies.

Matched MeSH terms: Polyurethanes
Evaluating the toxicity of polyurethane during marine clay stabilisation

Saleh S, Ahmad K, Mohd Yunus NZ, Hezmi MA

Environ Sci Pollut Res Int, 2020 Jun;27(17):21252-21259.
PMID: 32266626 DOI: 10.1007/s11356-020-08549-y

In civil engineering, many geotechnical and forensic projects employ polyurethane (PU) for ground improvement, and the results have shown to be effective in terms of time and cost savings. However, similar to many other chemical stabilisers, the use of PU for soil stabilisation may have environmental repercussions. Therefore, this paper utilised a toxicity characteristic leaching procedure (TCLP) to investigate the potential for ground contamination resulting from the application of PU for the stabilisation of marine clay. Furthermore, the hazardousness of PU during the stabilisation of marine clay was investigated by testing its reactivity, ignitability, corrosivity and physical properties. The results reveal that the quantity of heavy metals present in PU is far below the regulatory limits. The results further confirm that PU is odourless and non-corrosive and that it is non-cyanide and non-sulphide-bearing. However, PU is capable of igniting. Overall, the potential application of PU for ground improvement is promising due to its environmental friendliness.

Matched MeSH terms: Polyurethanes
Fulltext Filler-Modified Castor Oil-Based Polyurethane Foam for the Removal of Aqueous Heavy Metals Detected Using Laser-Induced Breakdown Spectroscopy (LIBS) Technique

Iqhrammullah M, Marlina, Hedwig R, Karnadi I, Kurniawan KH, Olaiya NG, et al.

Polymers (Basel), 2020 Apr 13;12(4).
PMID: 32294999 DOI: 10.3390/polym12040903

The use of polymeric material in heavy metal removal from wastewater is trending. Heavy metal removal from wastewater of the industrial process is of utmost importance in green/sustainable manufacturing. Production of absorbent materials from a natural source for industrial wastewater has been on the increase. In this research, polyurethane foam (PUF), an adsorbent used by industries to adsorb heavy metal from wastewater, was prepared from a renewable source. Castor oil-based polyurethane foam (COPUF) was produced and modified for improved adsorption performance using fillers, analyzed with laser-induced breakdown spectroscopy (LIBS). The fillers (zeolite, bentonite, and activated carbon) were added to the COPUF matrix allowing the modification on its surface morphology and charge. The materials were characterized using Fourier-transform infrared (FTIR), scanning electron microscopy (SEM), and thermal gravimetry analysis (TGA), while their adsorption performance was studied by comparing the LIBS spectra. The bentonite-modified COPUF (B/COPUF) gave the highest value of the normalized Pb I (405.7 nm) line intensity (2.3), followed by zeolite-modified COPUF (Z/COPUF) (1.9), and activated carbon-modified COPUF (AC/COPUF) (0.2), which indicates the adsorption performance of Pb2+ on the respective materials. The heavy metal ions' adsorption on the B/COPUF dominantly resulted from the electrostatic attraction. This study demonstrated the potential use of B/COPUF in adsorption and LIBS quantitative analysis of aqueous heavy metal ions.

Matched MeSH terms: Polyurethanes
Fulltext Dynamic Hepatocellular Carcinoma Model Within a Liver Phantom for Multimodality Imaging

Ahmad MS, Suardi N, Shukri A, Nik Ab Razak NNA, Oglat AA, Makhamrah O, et al.

Eur J Radiol Open, 2020;7:100257.
PMID: 32944594 DOI: 10.1016/j.ejro.2020.100257

Introduction: Hepatocellular carcinoma (HCC) is one of the most common cancer in the world, and the effectiveness of its treatment lies in its detection in its early stages. The aim of this study is to mimic HCC dynamically through a liver phantom and apply it in multimodality medical imaging techniques including magnetic resonance imaging (MRI), computed tomography (CT), and ultrasound.
Methods and materials: The phantom is fabricated with two main parts, liver parenchyma and HCC inserts. The liver parenchyma was fabricated by adding 2.5 wt% of agarose powder combined with 2.6 wt% of wax powder while the basic material for the HCC samples was made from polyurethane solution combined with 5 wt% glycerol. Three HCC samples were inserted into the parenchyma by using three cylinders implanted inside the liver parenchyma. An automatic injector is attached to the input side of the cylinders and a suction device connected to the output side of the cylinders. After the phantom was prepared, the contrast materials were injected into the phantom and imaged using MRI, CT, and ultrasound.
Results: Both HCC samples and liver parenchyma were clearly distinguished using the three imaging modalities: MRI, CT, and ultrasound. Doppler ultrasound was also applied through the HCC samples and the flow pattern was observed through the samples.
Conclusion: A multimodal dynamic liver phantom, with HCC tumor models have been fabricated. This phantom helps to improve and develop different methods for detecting HCC in its early stages.

Matched MeSH terms: Polyurethanes