PURPOSE: The purpose of this in vitro study was to evaluate the SR, tensile strength (TS), and percentage elongation (% E) of different SEs subjected to outdoor weathering in the Malaysian climate.
MATERIAL AND METHODS: Type-II dumbbell-shaped specimens (N-120) (nonweathered=15, weathered=15) were made from 3 room-temperature vulcanized (A-2000, A-2006, and A-103) and 1 heat-temperature vulcanized (M-511) silicone (Factor II). For 6 months, weathered specimens were subjected to outdoor weathering inside a custom exposure rack. Simultaneously, the nonweathered specimens were kept in a dehumidifier. Subsequently, the SR was measured with a profilometer; TS and % E were measured by using a universal testing machine. Two-way ANOVA was used to compare the means of the tested properties of the nonweathered and weathered specimens, and pairwise comparison was carried out between the silicones (α=.05).
RESULTS: After outdoor weathering, the SR, TS, and % E were adversely affected by weathering in the Malaysian environment. Among the silicone materials, A-2000 showed the least TS changes (2.51 MPa), while A-2006 demonstrated significant changes in percentage elongation after outdoor weathering (266.5%). M-511 exhibited the highest mean value (2.50 μm) for SR changes. In addition, A-103 SE showed statistically significant differences in most pairwise comparisons for all 3 dependent variables.
CONCLUSIONS: Based on the evaluation of mechanical properties, A-103 can be suggested as a suitable silicone for maxillofacial prostheses fabricated for tropical climates. However, A-2000 can be a suitable alternative, although significant changes to surface roughness were detected after outdoor weathering.
OBJECTIVES: To determine the prevalence and severity of HAVS among tyre shop workers in Kelantan, Malaysia.
METHODS: A cross-sectional study involving 200 tyre shop workers from two districts in Kelantan was performed. Part one data were collected at the field using questionnaire, and hand-arm vibration was measured. Part two involved a set of hand clinical examinations. The workers were divided into high (≥5 m s-2 ) and low/moderate (<5 m s-2 ) exposure group according to their 8-hr time weighted average [A(8)] of vibration exposure. The differences between the two exposure group were then compared.
RESULTS: The prevalence of the vascular, neurological, and musculoskeletal symptoms was 12.5% (95% CI 10.16 to 14.84), 37.0% (95% CI 30.31 to 43.69), and 44.5% (95% CI 37.61 to 51.38) respectively. When divided according to their exposure statuses, there was a significant difference in the prevalence of HAVS for all three components of vascular, neurological, and musculoskeletal (22.68% vs 2.91%, 62.89% vs 12.62% and 50.52% and 38.83%) respectively. All the clinical examinations findings also significantly differed between the two groups with the high exposure group having a higher abnormal result.
CONCLUSION: Exposure to high A(8) of vibration exposure was associated with a higher prevalence of all three component of HAVS. There is a need for better control of vibration exposure in Malaysia.