EXPERIMENT: Geological formations contain organic acids in minute concentrations, with the alkyl chain length ranging from C4 to C26. To fully understand the wetting characteristics of H2 in a natural geological picture, we aged mica mineral surfaces as a representative of the caprock in varying concentrations of organic molecules (with varying numbers of carbon atoms, lignoceric acid C24, lauric acid C12, and hexanoic acid C6) for 7 days. To comprehend the wettability of the mica/H2/brine system, we employed a contact-angle procedure similar to that in natural geo-storage environments (25, 15, and 0.1 MPa and 323 K).
FINDINGS: At the highest investigated pressure (25 MPa) and the highest concentration of lignoceric acid (10-2 mol/L), the mica surface became completely H2 wet with advancing (θa= 106.2°) and receding (θr=97.3°) contact angles. The order of increasing θa and θr with increasing organic acid contaminations is as follows: lignoceric acid > lauric acid > hexanoic acid. The results suggest that H2 gas leakage through the caprock is possible in the presence of organic acids at higher physio-thermal conditions. The influence of organic contamination inherent at realistic geo-storage conditions should be considered to avoid the overprediction of structural trapping capacities and H2 containment security.
Materials and methods: A novel bone scaffold has been developed using polyurethane (PE) added with wintergreen (WG) and titanium dioxide (TiO2). The developed nanocomposites were characterized through field emission scanning electron microscopy (FESEM), Fourier transform and infrared spectroscopy (FTIR), X-ray diffraction (XRD), contact angle measurement, thermogravimetric analysis (TGA), atomic force microscopy (AFM) and tensile testing. Furthermore, anticoagulant assays, cell viability analysis and calcium deposition were used to investigate the biological properties of the prepared hybrid nanocomposites.
Results: FESEM depicted the reduced fibre diameter for the electrospun PE/WG and PE/WG/TiO2 than the pristine PE. The addition of WG and TiO2 resulted in the alteration in peak intensity of PE as revealed in the FTIR. Wettability measurements showed the PE/WG showed decreased wettability and the PE/WG/TiO2 exhibited improved wettability than the pristine PE. TGA measurements showed the improved thermal behaviour for the PE with the addition of WG and TiO2. Surface analysis indicated that the composite has a smoother surface rather than the pristine PE. Further, the incorporation of WG and TiO2 improved the anticoagulant nature of the pristine PE. In vitro cytotoxicity assay has been performed using fibroblast cells which revealed that the electrospun composites showed good cell attachment and proliferation after 5 days. Moreover, the bone apatite formation study revealed the enhanced deposition of calcium content in the fabricated composites than the pristine PE.
Conclusion: Fabricated nanocomposites rendered improved physico-chemical properties, biocompatibility and calcium deposition which are conducive for bone tissue engineering.