Displaying publications 1 - 20 of 30 in total

Abstract:
Sort:
  1. Zarina O, Radzali O
    Med J Malaysia, 2004 May;59 Suppl B:160-1.
    PMID: 15468867
    Hydroxyapatite powder was mechanochemically synthesized from calcium pyrophosphate (Ca2P2O7) and calcium carbonate (CaCO3) using a solid-state reaction. The two powders were mixed in distilled water, milled for 8 hours, dried and calcined at 1100 degrees C for 1 hour. The phase(s) formed was analyzed by x-ray diffraction (XRD). It was found that hydroxyapatite was not the only one formed. This result will be used as the starting point to produce a single-phase hydroxyapatite in terms of excess hydroxyl group in a mechanochemical reaction.
    Matched MeSH terms: Hydroxyapatites/chemical synthesis*
  2. Rusnah M, Andanastuti M, Idris B
    Med J Malaysia, 2004 May;59 Suppl B:158-9.
    PMID: 15468866
    The present paper reports on the influence of sintering temperature on the porosity and strength of porous hydroxyapatite (HA). HA powder was first prepared by the sol-gel precipitation method using calcium hydroxide and ortho-phosporic acid. The fine HA powder, measuring <50 microm was then mixed into a slurry with the addition of binder agent, being a mixture of sago and PVA. A small amount of sodium dodecyl sulphate was also used as a foaming agent. Porous HA samples were then prepared via slip casting technique. The surface morphology of the sintered samples was observed under scanning electron microscopy at 20 kV and the compositions were determined via SEM-EDX. A universal testing machine was used to determine the compaction strength of the sintered samples.
    Matched MeSH terms: Hydroxyapatites/analysis*
  3. Shamsuria O, Fadilah AS, Asiah AB, Rodiah MR, Suzina AH, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:174-5.
    PMID: 15468874
    The aim of this study was to evaluate the in vitro cytotoxicity of biomaterials; Hydroxyapatite (HA), Natural coral (NC) and Polyhydroxybutarate (PHB). Three different materials used in this study; HA (Ca10(PO4)6(OH)2), NC (CaCO3) and PHB (Polymer) were locally produced by the groups of researcher from Universiti Sains Malaysia. The materials were separately extracted in the complete culture medium (100mg/ml) for 72h and introduced to the osteoblast cells CRL-1543. The viability of osteoblast CRL-1543 cultivated with these extraction materials after 72h incubation period was compared to negative control with neutral red assay by using spectrophotometer at 540nm. The results showed the non-cytotoxicity of the materials. After 72h of incubation period, HA showed 123% viable cells, NC was 99.43% and PHB was 176.75%. In this study, cytotoxicity test dealt mainly with the substances that leached out from the biomaterial. The results obtained showed that the materials were not toxic and also promoted cells growth in the sense of biofunctionality.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  4. Rajab NF, Yaakob TA, Ong BY, Hamid M, Ali AM, Annuar BO, et al.
    Med J Malaysia, 2004 May;59 Suppl B:170-1.
    PMID: 15468872
    Hydroxyapatite is the main component of the bone which is a potential biomaterial substance that can be applied in orthopaedics. In this study, the biocompatibility of this biomaterial was assessed using an in vitro technique. The cytotoxicity and genotoxicity effect of HA2 and HA3 against L929 fibroblast cell was evaluated using the MTT Assay and Alkaline Comet Assay respectively. Both HA2 and HA3 compound showed low cytotoxicity effect as determined using MTT Assay. Cells viability following 72 hours incubation at maximum concentration of both HA2 and HA3 (200 mg/ml) were 75.3 +/- 8.8% and 86.7 +/- 13.1% respectively. However, the cytotoxicity effect of ZnSO4.7H2O as a positive control showed an IC50 values of 46 mg/ml (160 microM). On the other hand, both HA2 and HA3 compound showed a slight genotoxicity effect as determined using the Alkaline Comet Assay following incubation at the concentration 200 mg/ml for 72 hours. This assay has been widely used in genetic toxicology to detect DNA strand breaks and alkali-labile site. The percentage of the cells with DNA damage for both substance was 27.7 +/- 1.3% and 15.6 +/- 1.0% for HA2 and HA3 respectively. Incubation of the cells for 24 hours with 38 microg/ml (IC25) of positive control showed an increase in percentage of cells with DNA damage (67.5 +/- 0.7%). In conclusion, our study indicated that both hydroxyapatite compounds showed a good biocompatibility in fibroblast cells.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  5. Kannan TP, Nik Ahmad Shah NL, Azlina A, Samsudin AR, Narazah MY, Salleh M
    Med J Malaysia, 2004 May;59 Suppl B:168-9.
    PMID: 15468871
    The present study is aimed at finding the mutagenicity and cytotoxicity of dense form of synthetic hydroxyapatite (Source: School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia) in the blood of sheep. The biomaterial was implanted in the tibia of Malin, an indigenous sheep breed of Malaysia. Blood was collected from the sheep before implantation of the biomaterial, cultured and a karyological study was made. Six weeks after implantation, blood was collected from the same animal, cultured and screened for chromosome aberrations. The mitotic indices and karyological analysis indicated that the implantation of synthetic hydroxyapatite (dense form) did not produce any cytotoxicity or chromosome aberrations in the blood of sheep.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  6. Azlina A, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:166-7.
    PMID: 15468870
    In Malaysia, the field of genomics in toxicology is still in infancy. The purpose of this study is to focus on the use of toxicogenomics for determination of gene expressions changes in cultured human fibroblast cells treated with genotoxicology free biomaterial (using Ames test), a locally produced hyroxyapatite. Dose and time response is similar to Ames test with time interval up to 21 days. mRNA is extracted, followed with RT-PCR and polyacrilamide gel electrophoresis. Changes of the gene expressions compared to the non-treated fibroblast mRNA would suggest some gene interactions in the molecule level associated with the exposure of the fibroblast cell line to the biomaterials. Further analysis (cloning & sequencing) shall be carried out to investigate the genes involved as simple changes might not signified toxicity.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  7. Tan SA, Ahmad Fauzi MN, Luay BH, Radzali O
    Med J Malaysia, 2004 May;59 Suppl B:162-3.
    PMID: 15468868
    In this work, nanometer HA crystals have been synthesized via wet chemical precipitation and characterized. This research studies how key synthesis parameters affect the size and phase purity of the produced HA. Characterization work was carried out using X-ray powder diffraction method and scanning electron microscopy for phase identification and particle sizing, respectively.
    Matched MeSH terms: Hydroxyapatites/analysis; Hydroxyapatites/chemical synthesis*
  8. Best SM, Patel N, Porter AE, Bonfield W
    Med J Malaysia, 2004 May;59 Suppl B:129-30.
    PMID: 15468852
    Bone is unique in its ability to adapt structure to functional requirements, but as is all too obvious in an ever-ageing population it is susceptible to a number of degenerative diseases. Therefore there is an increasing need for materials for bone replacement. Clearly, the ideal material with which to replace bone, would be bone itself, but the major problem now facing us is that there is an insufficient supply of the natural bone to satisfy the clinical requirements. Hence, there is a need for the development of chemically synthesised bone graft substitutes
    Matched MeSH terms: Hydroxyapatites*
  9. Abdul Razak NH, Al-Salihi KA, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:119-20.
    PMID: 15468847
    Defects were created in the mandible of a rabbit model whereby the right side was implanted with hydroxyapatite (HA) while the left side was left empty to act as control. Both the implant and control sites were evaluated clinically and histologically at 4,12,20,22 weeks. Decalcified sections were studied under confocal laser scanning microscope. No reactive cells were evident microscopically in all sections. There was bone ingrowth as early as 4 weeks when viewed by the topographic method. Enhancement of osteoconduction was evident by the presence of abundant capillaries, perivascular tissue and osteoprogenitor cells of the host. At 22 weeks, the implanted defect showed mature bone formation filling almost the whole field. This study demonstrated that the dense HA exhibits excellent biocompatibility as noted by the complete absence of reactive cells. It also promotes osteoconduction.
    Matched MeSH terms: Hydroxyapatites*
  10. Khadijah K, Mashita M, Saidu MF, Fazilah F, Khalid KA
    Med J Malaysia, 2004 May;59 Suppl B:123-4.
    PMID: 15468849
    This study is to qualitatively evaluate a locally produced hydroxyapatite (HA), made by AMREC-SIRIM in an experimental animal bone defect using New Zealand White (NZW) rabbits. HA cylindrical blocks measuring 2.5 mm (D) x 1.0 mm (H) were implanted in the rabbits' left tibia. The tibias were harvested within one to three weeks post-implantation. The implantion site was cut into thin undecalcified sections of about 30 microm to 60 microm and stained with Toluidine Blue and Goldner's Masson Trichrome. Microscopic examinations using standard light microscopy of these slides were performed.
    Matched MeSH terms: Hydroxyapatites*
  11. Najafpour HD, Suzina AH, Nizam A, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:121-2.
    PMID: 15468848
    There was a significant increased in Absolute Contact Length measurements of endosteal bone growth along the Nickel-Titanium (NiTi) implant coated with the natural coral powder and Hydroxyapatite (HA) compared to the non-calcium coated implants. This study demonstrated that coated implants seemed to show earlier and higher osseointergration phenomena compared to non coated ones. Furthermore, there was significantly greater bone-to-implant contact at the apical 1/3rd of the coated implants.
    Matched MeSH terms: Hydroxyapatites*
  12. Shaari R, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:109-10.
    PMID: 15468842
    The present in vitro evaluation indicated that the value added hydroxyapatite (HA) was more toxic than pure HA but the toxicity of value added HA was slight compared to the positive control. In this testing, the conclusion can be made that value added HA is less biocompatible than commercialized pure HA. This toxicity may be caused by both the particle size and degradation (leaching). Further studies should be carried out to determine whether there is particle size effect or leaching effect when using powder as compared to the block materials. The in vivo evaluation should be done to assess the reaction to this value added HA as compared to the pure HA.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  13. Suzina AH, Azlina A, Shamsuria O, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:105-6.
    PMID: 15468840
    Mutagenicity of CORAGRAF (natural coral) and REKAGRAF (hydroxyapatite) was tested in Ames test with and without an external metabolic activation system (S9). The test revealed no mutagenic activity of both locally produced osseous substitutes.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  14. Hee SL, Nik Intan NI, Fazan F
    Med J Malaysia, 2004 May;59 Suppl B:77-8.
    PMID: 15468827
    There is a great demand of Hydroxyapatite (HA) material in Orthopaedics and Dental applications due to its similarity to human bone. However, the lack of availability and due to high import cost of this material in Malaysia, research in producing synthetic HA locally is therefore timely. The use of local resources as the raw materials for the production of HA is also desirable in reducing the overall cost of HA. In this study, two HA materials were synthesised from different starting precursors, i.e. commercial pure Ca(OH)2 (HAS) and Ca(OH)2 directly from a local natural limestone deposit (HAL). Whereas a commercially available HA "Captal 60" (HAC) was used as reference. The synthesised powders obtained were fired at 1000 degrees C and at 1250 degrees C. Characterisation evaluations on bulk properties were carried out using XRD, SEM-EDX, ICP and FTIR. The results indicate that both HAS and HAL are comparable to HAC even at 1000 degrees C. Thus, the local natural limestone can be used to form HA. However, the overall appearance of these materials are quite different (HAC - blue, HAS - greenish and HAL - light green). The reasons for this and the subsequent mechanical and bioactive effects of these materials are currently being investigated.
    Matched MeSH terms: Hydroxyapatites/analysis; Hydroxyapatites/chemical synthesis*
  15. Rusnah M, Andanastuti M, Idris B
    Med J Malaysia, 2004 May;59 Suppl B:83-4.
    PMID: 15468830
    The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.
    Matched MeSH terms: Hydroxyapatites/analysis*; Hydroxyapatites/chemical synthesis
  16. Sofia Beagem Mohd Noal, Roslinda Shamsudin, Tan, Lee Phin, Wan Khartini Wan Abdul Khodir
    MyJurnal
    Hydroxyapatite (HA) powder was synthesized via wet method using calcium nitrate hydrate (Ca(NO3)2.H2O) and diammonium hydrogen phosphate ((NH4)2HPO4) as raw materials. Powder obtained was milled using various milling speed ranging from 250 to 400 r.p.m. and sintered at 1300°C for 2hrs. Due to the nature of HA powder that decomposed at high temperature, XRD technique have been used in this work to determine the phase composition of the HA powder and also the crystallite size. The unmilled sample was used as the control group. Results show that sufficient heat supply generated from the milling process, initiates the decomposition of HA phase into ȕ-tricalcium phosphate (ȕ-TCP). Decomposition of HA starts to occur at the milling speed of 300 rpm, i.e the formation of ȕ-TCP was occurred at lower sintering temperature. It was believed that the decomposition of HA was associated with the formation of an intermediate phase, oxyapatite. Moreover, the crystallinity and particle size of the produced powder is very much affected by the milling speed and the stability of the HA. All milled powders possess spherical shape particle.
    Matched MeSH terms: Hydroxyapatites
  17. Mardziah CM, Sopyan I, Hamdi M, Ramesh S
    Med J Malaysia, 2008 Jul;63 Suppl A:79-80.
    PMID: 19024993
    Improvement of the mechanical properties of hydroxyapatite (HA) can be achieved by the incorporation of metal. In addition, incorporation of strontium ion into HA crystal structures has been proved effective to enhance biochemical properties of bone implant. In this research, strontium-doped HA powder was developed via a sol-gel method to produce extraordinarily fine strontium-doped HA (Sr-doped HA) powder. XRD measurement had shown that the powder contained hydroxyapatite phase only for all doping concentration except for 2%, showing that Sr atoms have suppressed the appearance of beta-TCP as the secondary phase. Morphological evaluation by FESEM measurement shows that the particles of the Sr-doped HA agglomerates are globular in shape with an average size of 1-2 microm in diameter while the primary particles have a diameter of 30-150 nm in average.
    Matched MeSH terms: Hydroxyapatites/chemistry*
  18. Cik Rohaida, C.H., Idris, B., Rusnah, M., Mohd Reusmaazran, Y., Narimah, A.B.
    MyJurnal
    Phase composition of calcium phosphate ceramic is a characteristic directly related to the biological response of implants due to the differences in mechanical and biochemical properties of these compounds. The biodegradation rate of biphasic calcium phosphate (BCP) can be controlled by altering the HA to β-TCP ratios. In this study the crystalline phase evolution of BCP synthesized via precipitation from aqueous solution of (NH4)2PO4 titrated into heated solution of Ca (NO3)2 was evaluated. The resulting powder was fabricated into porous scaffold using polyurethane foam method. Bulk powders were sintered from 700 - 1400°C to determine the most significant sintering temperature to obtain a stable and well crystallize BCP phases. The porous scaffolds were then sintered at selected temperature and the effects of various sintering times from 5,7,9,11,13 and 15 h were investigated. Bulk powders were characterized by dilatometer, IR analysis and XRD and porous scaffolds were analyzed by XRD and SEMEdx. RIR method was performed to show that the HA to β-TCP ratios were increased with increasing of sintering time and reached the maximum HA value at 11h. It is found that, the possibilities to manipulate the HA to β-TCP ratios in BCP porous scaffold by just controlling the sintering time of the scaffold without controlling the starting powder characteristics.
    Matched MeSH terms: Hydroxyapatites
  19. Baradaran S, Moghaddam E, Nasiri-Tabrizi B, Basirun WJ, Mehrali M, Sookhakian M, et al.
    Mater Sci Eng C Mater Biol Appl, 2015 Apr;49:656-668.
    PMID: 25686995 DOI: 10.1016/j.msec.2015.01.050
    The effect of the addition of an ionic dopant to calcium phosphates for biomedical applications requires specific research due to the essential roles played in such processes. In the present study, the mechanical and biological properties of Ni-doped hydroxyapatite (HA) and Ni-doped HA mixed with graphene nanoplatelets (GNPs) were evaluated. Ni (3wt.% and 6wt.%)-doped HA was synthesized using a continuous precipitation method and calcined at 900°C for 1h. The GNP (0.5-2wt.%)-reinforced 6% Ni-doped HA (Ni6) composite was prepared using rotary ball milling for 15h. The sintering process was performed using hot isostatic pressing at processing conditions of 1150°C and 160MPa with a 1-h holding time. The results indicated that the phase compositions and structural features of the products were noticeably affected by the Ni and GNPs. The mechanical properties of Ni6 and 1.5Ni6 were increased by 55% and 75% in hardness, 59% and 163% in fracture toughness and 120% and 85% in elastic modulus compared with monolithic HA, respectively. The in-vitro biological behavior was investigated using h-FOB osteoblast cells in 1, 3 and 5days of culture. Based on the osteoblast results, the cytotoxicity of the products was indeed affected by the Ni doping. In addition, the effect of GNPs on the growth and proliferation of osteoblast cells was investigated in Ni6 composites containing different ratios of GNPs, where 1.5wt.% was the optimum value.
    Matched MeSH terms: Hydroxyapatites/chemistry
  20. Ibrahim S, Sabudin S, Sahid S, Marzuke MA, Hussin ZH, Kader Bashah NS, et al.
    Saudi J Biol Sci, 2016 Jan;23(1):S56-63.
    PMID: 26858566 DOI: 10.1016/j.sjbs.2015.10.024
    Surface reactivity of bioactive ceramics contributes in accelerating bone healing by anchoring osteoblast cells and the connection of the surrounding bone tissues. The presence of silicon (Si) in many biocompatible and bioactive materials has been shown to improve osteoblast cell adhesion, proliferation and bone regeneration due to its role in the mineralisation process around implants. In this study, the effects of Si-biphasic calcium phosphate (Si-BCP) on bioactivity and adhesion of human osteoblast (hFOB) as an in vitro model have been investigated. Si-BCP was synthesised using calcium hydroxide (Ca(OH)2) and phosphoric acid (H3PO4) via wet synthesis technique at Ca/P ratio 1.60 of material precursors. SiO2 at 3 wt% based on total precursors was added into apatite slurry before proceeding with the spray drying process. Apatite powder derived from the spray drying process was pressed into discs with Ø 10 mm. Finally, the discs were sintered at atmospheric condition to obtain biphasic hydroxyapatite (HA) and tricalcium phosphate (TCP) peaks simultaneously and examined by XRD, AFM and SEM for its bioactivity evaluation. In vitro cell viability of L929 fibroblast and adhesion of hFOB cell were investigated via AlamarBlue® (AB) assay and SEM respectively. All results were compared with BCP without Si substitution. Results showed that the presence of Si affected the material's surface and morphology, cell proliferation and cell adhesion. AFM and SEM of Si-BCP revealed a rougher surface compared to BCP. Bioactivity in simulated body fluid (SBF) was characterised by pH, weight gain and apatite mineralisation on the sample surface whereby the changes in surface morphology were evaluated using SEM. Immersion in SBF up to 21 days indicated significant changes in pH, weight gain and apatite formation. Cell viability has demonstrated no cytotoxic effect and denoted that Si-BCP promoted good initial cell adhesion and proliferation. These results suggest that Si-BCP's surface roughness (164 nm) was significantly higher than BCP (88 nm), thus enhancing the adhesion and proliferation of the osteoblast.
    Matched MeSH terms: Hydroxyapatites
Filters
Contact Us

Please provide feedback to Administrator (afdal@afpm.org.my)

External Links