Displaying publications 1 - 20 of 30 in total

Abstract:
Sort:
  1. Rusnah M, Andanastuti M, Idris B
    Med J Malaysia, 2004 May;59 Suppl B:158-9.
    PMID: 15468866
    The present paper reports on the influence of sintering temperature on the porosity and strength of porous hydroxyapatite (HA). HA powder was first prepared by the sol-gel precipitation method using calcium hydroxide and ortho-phosporic acid. The fine HA powder, measuring <50 microm was then mixed into a slurry with the addition of binder agent, being a mixture of sago and PVA. A small amount of sodium dodecyl sulphate was also used as a foaming agent. Porous HA samples were then prepared via slip casting technique. The surface morphology of the sintered samples was observed under scanning electron microscopy at 20 kV and the compositions were determined via SEM-EDX. A universal testing machine was used to determine the compaction strength of the sintered samples.
    Matched MeSH terms: Hydroxyapatites/analysis*
  2. Zarina O, Radzali O
    Med J Malaysia, 2004 May;59 Suppl B:160-1.
    PMID: 15468867
    Hydroxyapatite powder was mechanochemically synthesized from calcium pyrophosphate (Ca2P2O7) and calcium carbonate (CaCO3) using a solid-state reaction. The two powders were mixed in distilled water, milled for 8 hours, dried and calcined at 1100 degrees C for 1 hour. The phase(s) formed was analyzed by x-ray diffraction (XRD). It was found that hydroxyapatite was not the only one formed. This result will be used as the starting point to produce a single-phase hydroxyapatite in terms of excess hydroxyl group in a mechanochemical reaction.
    Matched MeSH terms: Hydroxyapatites/chemical synthesis*
  3. Tan SA, Ahmad Fauzi MN, Luay BH, Radzali O
    Med J Malaysia, 2004 May;59 Suppl B:162-3.
    PMID: 15468868
    In this work, nanometer HA crystals have been synthesized via wet chemical precipitation and characterized. This research studies how key synthesis parameters affect the size and phase purity of the produced HA. Characterization work was carried out using X-ray powder diffraction method and scanning electron microscopy for phase identification and particle sizing, respectively.
    Matched MeSH terms: Hydroxyapatites/analysis; Hydroxyapatites/chemical synthesis*
  4. Mardziah CM, Sopyan I, Hamdi M, Ramesh S
    Med J Malaysia, 2008 Jul;63 Suppl A:79-80.
    PMID: 19024993
    Improvement of the mechanical properties of hydroxyapatite (HA) can be achieved by the incorporation of metal. In addition, incorporation of strontium ion into HA crystal structures has been proved effective to enhance biochemical properties of bone implant. In this research, strontium-doped HA powder was developed via a sol-gel method to produce extraordinarily fine strontium-doped HA (Sr-doped HA) powder. XRD measurement had shown that the powder contained hydroxyapatite phase only for all doping concentration except for 2%, showing that Sr atoms have suppressed the appearance of beta-TCP as the secondary phase. Morphological evaluation by FESEM measurement shows that the particles of the Sr-doped HA agglomerates are globular in shape with an average size of 1-2 microm in diameter while the primary particles have a diameter of 30-150 nm in average.
    Matched MeSH terms: Hydroxyapatites/chemistry*
  5. Suzina AH, Azlina A, Shamsuria O, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:105-6.
    PMID: 15468840
    Mutagenicity of CORAGRAF (natural coral) and REKAGRAF (hydroxyapatite) was tested in Ames test with and without an external metabolic activation system (S9). The test revealed no mutagenic activity of both locally produced osseous substitutes.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  6. Rusnah M, Andanastuti M, Idris B
    Med J Malaysia, 2004 May;59 Suppl B:83-4.
    PMID: 15468830
    The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.
    Matched MeSH terms: Hydroxyapatites/analysis*; Hydroxyapatites/chemical synthesis
  7. Tariq U, Hussain R, Tufail K, Haider Z, Tariq R, Ali J
    Mater Sci Eng C Mater Biol Appl, 2019 Oct;103:109863.
    PMID: 31349467 DOI: 10.1016/j.msec.2019.109863
    Quick setting and poor injectability due to liquid-solid phase separation have limited the clinical use of brushite and monetite cements. The presence of certain ions in the cement during the setting reaction moderate the setting time and properties of the cement. This study reports the preparation of injectable bone cement by using biphasic calcium phosphate (BCP) extracted from femur lamb bone by calcination at 1450 °C. EDX analysis infers the presence of Mg and Na ions as trace elements in BCP. X-ray diffraction patterns of the prepared cement confirmed the formation of brushite (DCPD) along with monetite (DCPA) as a minor phase. DCPA phase diminished gradually with a decrease in powder to liquid ratio (PLR). Initial and final setting time of 5.3 ± 0.5 and 14.67 ± 0.5 min respectively are obtained and within the acceptable recommended range for orthopedic applications. Exceptional injectability of ≈90% is achieved for all prepared bone cement samples. A decrease in compressive strength was observed with increase in the liquid phase of the cement, which is attributed to the higher degree of porosity in the set cement. Immersion of bone cement in simulated body fluid (SBF) for up to 7 days resulted in the formation of apatite layer on the surface of cement with Ca/P ratio 1.71, which enhanced the compressive strength from 2.88 to 9.15 MPa. The results demonstrate that bone cement produced from BCP extracted from femur lamb bone can be considered as potential bone substitute for regeneration and repair of bone defects.
    Matched MeSH terms: Hydroxyapatites/chemistry*
  8. Sofia Beagem Mohd Noal, Roslinda Shamsudin, Tan, Lee Phin, Wan Khartini Wan Abdul Khodir
    MyJurnal
    Hydroxyapatite (HA) powder was synthesized via wet method using calcium nitrate hydrate (Ca(NO3)2.H2O) and diammonium hydrogen phosphate ((NH4)2HPO4) as raw materials. Powder obtained was milled using various milling speed ranging from 250 to 400 r.p.m. and sintered at 1300°C for 2hrs. Due to the nature of HA powder that decomposed at high temperature, XRD technique have been used in this work to determine the phase composition of the HA powder and also the crystallite size. The unmilled sample was used as the control group. Results show that sufficient heat supply generated from the milling process, initiates the decomposition of HA phase into ȕ-tricalcium phosphate (ȕ-TCP). Decomposition of HA starts to occur at the milling speed of 300 rpm, i.e the formation of ȕ-TCP was occurred at lower sintering temperature. It was believed that the decomposition of HA was associated with the formation of an intermediate phase, oxyapatite. Moreover, the crystallinity and particle size of the produced powder is very much affected by the milling speed and the stability of the HA. All milled powders possess spherical shape particle.
    Matched MeSH terms: Hydroxyapatites
  9. Wan Jusoh WN, Matori KA, Mohd Zaid MH, Zainuddin N, Ahmad Khiri MZ, Abdul Rahman NA, et al.
    Materials (Basel), 2021 Feb 18;14(4).
    PMID: 33670465 DOI: 10.3390/ma14040954
    Glass ionomer cement (GIC) is a well-known restorative material applied in dentistry. The present work aims to study the effect of hydroxyapatite (HA) addition into GIC based on physical, mechanical and structural properties. The utilization of waste materials namely clam shell (CS) and soda lime silica (SLS) glass as replacements for the respective CaO and SiO2 sources in the fabrication of alumino-silicate-fluoride (ASF) glass ceramics powder. GIC was formulated based on ASF glass ceramics, polyacrylic acid (PAA) and deionized water, while 1 wt.% of HA powder was added to enhance the properties of the cement samples. The cement samples were subjected to four different ageing times before being analyzed. In this study, the addition of HA caused an increment in density and compressive strength results along with ageing time. Besides, X-ray Diffraction (XRD) revealed the formation of fluorohydroxyapatite (FHA) phase in HA-added GIC samples and it was confirmed by Fourier Transform Infrared (FTIR) analysis which detected OH‒F vibration mode. In addition, needle-like and agglomeration of spherical shapes owned by apatite crystals were observed from Field Emission Scanning Electron Microscopy (FESEM). Based on Energy Dispersive X-ray (EDX) analysis, the detection of chemical elements in the cement samples were originated from chemical compounds used in the preparation of glass ceramics powder and also the polyacid utilized in initiating the reaction of GIC.
    Matched MeSH terms: Hydroxyapatites
  10. Kohli S, Bhatia S, Banavar SR, Al-Haddad A, Kandasamy M, Qasim SSB, et al.
    Sci Rep, 2023 Mar 13;13(1):4181.
    PMID: 36914760 DOI: 10.1038/s41598-023-31125-6
    To formulate a dental bleaching agent with strawberry extract that has potent bleaching properties and antimicrobial efficacy. Enamel specimens (3 × 3 × 2 mm3) were prepared. Quaternary Ammonium Silane (CaC2 enriched) was homogenized with fresh strawberries: Group 1: supernatant strawberry (10 g) extract 
    Matched MeSH terms: Hydroxyapatites
  11. Gupta R, Kewalramani R
    J Oral Biol Craniofac Res, 2021 03 10;11(2):330-333.
    PMID: 33786296 DOI: 10.1016/j.jobcr.2021.03.001
    Aim: To evaluate the microleakage of newer bioceramic root-end filling materials.

    Material and method: Sixty freshly extracted human single-rooted mandibular premolar teeth were selected for the study. Teeth with fractured root, cracks, anddilacerations were rejected. All teeth were cleaned with ultrasonic scalers. Standard access opening was done and root canal treatment was performed with rotary files followed by obturation. After storing in saline for a week apical 3 ​mm of the root was resected at 900 angles to the long axis of the root. Retro cavity preparation was done with ultrasonic tips. The teeth were divided into four groups of 15 specimens each. Group I - Biodentin, GroupII-Bioaggregate, Group III - MTA Plus, and Group IV - MTA. After the restoration of retro cavities of all the teeth as per manufacture instructions, two coats of nail varnish were applied to leave apical 3 ​mm. All teeth were stored in 2% methylene blue for 72 ​h followed by emersion in 65% nitric acid for the next 72 ​h for Dye extraction. The obtained supernatant solution was then centrifuged and optical density or absorbance was measured with a UV spectrophotometer.

    Result: Microleakage was found to be increasing in this order: Biodentin ​ ​0.01).

    Conclusion: All materials exhibit some amount of microleakage. Biodentin shows the least microleakage among all the bioceramic material groups. Hence, Biodentin and bioaggregate are better material of choice for the retrograde filling to prevent microleakage.

    Matched MeSH terms: Hydroxyapatites
  12. Shaari R, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:109-10.
    PMID: 15468842
    The present in vitro evaluation indicated that the value added hydroxyapatite (HA) was more toxic than pure HA but the toxicity of value added HA was slight compared to the positive control. In this testing, the conclusion can be made that value added HA is less biocompatible than commercialized pure HA. This toxicity may be caused by both the particle size and degradation (leaching). Further studies should be carried out to determine whether there is particle size effect or leaching effect when using powder as compared to the block materials. The in vivo evaluation should be done to assess the reaction to this value added HA as compared to the pure HA.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  13. Shamsuria O, Fadilah AS, Asiah AB, Rodiah MR, Suzina AH, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:174-5.
    PMID: 15468874
    The aim of this study was to evaluate the in vitro cytotoxicity of biomaterials; Hydroxyapatite (HA), Natural coral (NC) and Polyhydroxybutarate (PHB). Three different materials used in this study; HA (Ca10(PO4)6(OH)2), NC (CaCO3) and PHB (Polymer) were locally produced by the groups of researcher from Universiti Sains Malaysia. The materials were separately extracted in the complete culture medium (100mg/ml) for 72h and introduced to the osteoblast cells CRL-1543. The viability of osteoblast CRL-1543 cultivated with these extraction materials after 72h incubation period was compared to negative control with neutral red assay by using spectrophotometer at 540nm. The results showed the non-cytotoxicity of the materials. After 72h of incubation period, HA showed 123% viable cells, NC was 99.43% and PHB was 176.75%. In this study, cytotoxicity test dealt mainly with the substances that leached out from the biomaterial. The results obtained showed that the materials were not toxic and also promoted cells growth in the sense of biofunctionality.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  14. Khadijah K, Mashita M, Saidu MF, Fazilah F, Khalid KA
    Med J Malaysia, 2004 May;59 Suppl B:123-4.
    PMID: 15468849
    This study is to qualitatively evaluate a locally produced hydroxyapatite (HA), made by AMREC-SIRIM in an experimental animal bone defect using New Zealand White (NZW) rabbits. HA cylindrical blocks measuring 2.5 mm (D) x 1.0 mm (H) were implanted in the rabbits' left tibia. The tibias were harvested within one to three weeks post-implantation. The implantion site was cut into thin undecalcified sections of about 30 microm to 60 microm and stained with Toluidine Blue and Goldner's Masson Trichrome. Microscopic examinations using standard light microscopy of these slides were performed.
    Matched MeSH terms: Hydroxyapatites*
  15. Wahab NFAC, Kannan TP, Mahmood Z, Rahman IA, Ismail H
    Toxicol In Vitro, 2018 Mar;47:207-212.
    PMID: 29247761 DOI: 10.1016/j.tiv.2017.12.002
    Biphasic Calcium Phosphate (BCP) with a ratio of 20/80 Hydroxyapatite (HA)/Beta-tricalcium phosphate (β-TCP) promotes the differentiation of human dental pulp cells (HDPCs). In the current study, the genotoxicity of locally produced BCP of modified porosity (65%) with a mean pore size of 300micrometer (μm) was assessed using Comet and Ames assays. HDPCs were treated with BCP extract at three different inhibitory concentrations which were obtained based on cytotoxicity test conducted with concurrent negative and positive controls. The tail moment of HDPCs treated with BCP extract at all three concentrations showed no significant difference compared to negative control (p>0.05), indicating that BCP did not induce DNA damage to HDPCs. The BCP was evaluated using five tester strains of Salmonella typhimurium TA98, TA100, TA102, TA1537 and TA1538. Each strain was incubated with BCP extract with five different concentrations in the presence and absence of metabolic activation system (S9) mix. Concurrently, negative and positive controls were included. The average number of revertant colonies per plate treated with the BCP extract was less than double as compared to the number of revertant colonies in negative control plate and no dose-related increase was observed. Results from both assays suggested that the BCP of modified porosity did not exhibit any genotoxic effect under the present test conditions.
    Matched MeSH terms: Hydroxyapatites/adverse effects*; Hydroxyapatites/metabolism; Hydroxyapatites/chemistry
  16. Azlina A, Samsudin AR
    Med J Malaysia, 2004 May;59 Suppl B:166-7.
    PMID: 15468870
    In Malaysia, the field of genomics in toxicology is still in infancy. The purpose of this study is to focus on the use of toxicogenomics for determination of gene expressions changes in cultured human fibroblast cells treated with genotoxicology free biomaterial (using Ames test), a locally produced hyroxyapatite. Dose and time response is similar to Ames test with time interval up to 21 days. mRNA is extracted, followed with RT-PCR and polyacrilamide gel electrophoresis. Changes of the gene expressions compared to the non-treated fibroblast mRNA would suggest some gene interactions in the molecule level associated with the exposure of the fibroblast cell line to the biomaterials. Further analysis (cloning & sequencing) shall be carried out to investigate the genes involved as simple changes might not signified toxicity.
    Matched MeSH terms: Hydroxyapatites/toxicity*
  17. Ebrahimi S, Hanim YU, Sipaut CS, Jan NBA, Arshad SE, How SE
    Int J Mol Sci, 2021 Sep 06;22(17).
    PMID: 34502544 DOI: 10.3390/ijms22179637
    Recently, composite scaffolding has found many applications in hard tissue engineering due to a number of desirable features. In this present study, hydroxyapatite/bioglass (HAp/BG) nanocomposite scaffolds were prepared in different ratios using a hydrothermal approach. The aim of this research was to evaluate the adhesion, growth, viability, and osteoblast differentiation behavior of human Wharton's-jelly-derived mesenchymal stem cells (hWJMSCs) on HAp/BG in vitro as a scaffold for application in bone tissue engineering. Particle size and morphology were investigated by TEM and bioactivity was assessed and proven using SEM analysis with hWJMSCs in contact with the HAp/BG nanocomposite. Viability was evaluated using PrestoBlueTM assay and early osteoblast differentiation and mineralization behaviors were investigated by ALP activity and EDX analysis simultaneously. TEM results showed that the prepared HAp/BG nanocomposite had dimensions of less than 40 nm. The morphology of hWJMSCs showed a fibroblast-like shape, with a clear filopodia structure. The viability of hWJMSCs was highest for the HAp/BG nanocomposite with a 70:30 ratio of HAp to BG (HAp70/BG30). The in vitro biological results confirmed that HAp/BG composite was not cytotoxic. It was also observed that the biological performance of HAp70/BG30 was higher than HAp scaffold alone. In summary, HAp/BG scaffold combined with mesenchymal stem cells showed significant potential for bone repair applications in tissue engineering.
    Matched MeSH terms: Hydroxyapatites/chemistry*
  18. Cik Rohaida, C.H., Idris, B., Rusnah, M., Mohd Reusmaazran, Y., Narimah, A.B.
    MyJurnal
    Phase composition of calcium phosphate ceramic is a characteristic directly related to the biological response of implants due to the differences in mechanical and biochemical properties of these compounds. The biodegradation rate of biphasic calcium phosphate (BCP) can be controlled by altering the HA to β-TCP ratios. In this study the crystalline phase evolution of BCP synthesized via precipitation from aqueous solution of (NH4)2PO4 titrated into heated solution of Ca (NO3)2 was evaluated. The resulting powder was fabricated into porous scaffold using polyurethane foam method. Bulk powders were sintered from 700 - 1400°C to determine the most significant sintering temperature to obtain a stable and well crystallize BCP phases. The porous scaffolds were then sintered at selected temperature and the effects of various sintering times from 5,7,9,11,13 and 15 h were investigated. Bulk powders were characterized by dilatometer, IR analysis and XRD and porous scaffolds were analyzed by XRD and SEMEdx. RIR method was performed to show that the HA to β-TCP ratios were increased with increasing of sintering time and reached the maximum HA value at 11h. It is found that, the possibilities to manipulate the HA to β-TCP ratios in BCP porous scaffold by just controlling the sintering time of the scaffold without controlling the starting powder characteristics.
    Matched MeSH terms: Hydroxyapatites
  19. Farrahshaida Mohd Salleh, Abu Bakar Sulong, Muhammad Rafi Raza, Norhamidi Muhamad, Lim TF
    Sains Malaysiana, 2017;46:1651-1657.
    owder injection molding (PIM) is able to produce porous titanium alloy/hydroxyapatite composite through the space holder technique. Thermal debinding and sintering processes were the main challenges due to different properties of metal and ceramic in producing such composite. This study focused on the effect of different space holders on the physical and mechanical properties of debound and sintered porous titanium aloi/hydroxyapatite composite. The feedstock is containing of 80 wt. % of titanium alloy/hydroxyapatite with 20 wt. % of space holders such as sodium chloride (NaCl) and polymethylmethacrylate (PMMA), respectively. The binders were then removed from the injected samples by two stages of debinding; solvent and thermal debinding. The sintering was performed at three different temperatures 1100oC, 1200oC and 1300oC at a heating rate of 10oC /min and holding time of 5 h. It was found that the samples containing PMMA space holder was fractured after sintering. While, the samples containing NaCl space holder successfully formed pores and not fractured. At sintering temperature of 1300oC, the density, compressive strength and porosity volume percentages for the sintered sample containing NaCl space holder were 3.05 g/cm3, 91.7 MPa. and 11.9 vol%, respectively.
    Matched MeSH terms: Hydroxyapatites
  20. Beh CY, Cheng EM, Mohd Nasir NF, Eng SK, Abdul Majid MS, Ridzuan MJM, et al.
    Int J Biol Macromol, 2021 Jan 01;166:1543-1553.
    PMID: 33181217 DOI: 10.1016/j.ijbiomac.2020.11.034
    This paper provides a comprehensive analysis of the dielectric and physicochemical properties of the porous hydroxyapatite/cornstarch (HAp/Cs) composites in a new perspective. The porous composites have been characterized via SEM, FTIR, XRD and dielectric spectroscopy. The dielectric permittivity spectra were obtained in Ku-band (12.4-18.0 GHz) and it was correlated with the physicochemical properties of the porous HAp/Cs. Porous HAp/Cs composites exhibits low ε' and negative ε″, which influenced by the microstructural morphology, interaction between Hap and Cs, as well as crystalline features due to the various proportion of the HAp/Cs. The physicochemical effect of the composites results in the dielectric polarization and energy loss. This phenomenon indicates the presence of the three obvious relaxation responses in the ε' spectrum (13.2-14.0, 15.2-16.0, and 16.6-17.4 GHz) and the negative behaviours in the ε″ spectrum. The relationships between physicochemical and dielectric properties of the porous composite facilitate the development of the non-destructive microwave evaluation test for the porous composite.
    Matched MeSH terms: Hydroxyapatites/chemistry*
Filters
Contact Us

Please provide feedback to Administrator (afdal@afpm.org.my)

External Links