In this study polymer electrolytes composed of poly(methyl methacrylate) (PMMA) as a host polymer and ethylene carbonate (EC) as a plasticizer complexed with different lithium salts, i.e. lithium tetrafluoroborate (LiBF4) and lithium triflate (LiCF3SO3) were prepared by the solution casting technique. The conductivities of the films were characterized by impedance spectroscopy. At room temperature, the highest conductivities were 4.07 × 10–7S cm–1 and 3.40 × 10–5 S cm–1 achieved, respectively from the films containing 30 wt% LiBF4 in the PMMA-EC-LiBF4 system and 35 wt% LiCF3SO3 in the PMMA-EC-LiCF3SO3 system. The conductivity-temperature dependence of the films seemed to obey the Arrhenius equation in which the ion transport in these materials was thermally assisted. Scanning electron microscopy analysis showed that the surface of PMMA-EC-LiCF3SO3 film was smooth and homogeneous, hence lithium ions could traverse through the PMMA-EC-LiCF3SO3 film more easily compared to the PMMA-EC-LiBF4 film. X-Ray diffraction studies revealed that complexation had occurred and the complexes formed were amorphous.
The aim of this work was to investigate the effect of glycerol concentration on mechanical
and physical properties of gellan gum (GG) biofilm. The biofilm was prepared using solvent
casting method and the effective glycerol concentration was found to be within 30-50%
w/w (based on GG weight). At 60 and 70 w/w% of glycerol, the films started to distort
because the films was flexible and brittle. As glycerol concentration was increased the tensile
strength (TS) and Youngs modulus (E) of films decreased. Somehow, elongation at break
(EAB), water vapor transmission rate (WVTR) and swelling of films was increased. Glycerol
plasticized GG biofilm was thermally stable and flexible, proposed its can be exploited as
film-forming material and with optimized glycerol concentration it has good mechanical and
physical properties for edible biofilm.
Poly (vinyl chloride) membrane electrodes that responded selectively towards the antimalarial drug chloroquine are described. The electrodes were based on the use of the lipophilic potassium tetrakis(4-chlorophenyl)borate as ion-exchanger and bis(2-ethylhexyl)adipate (BEHA), or trioctylphosphate (TOP) or dioctylphenylphosphonate (DOPP) as plasticizing solvent mediator. All electrodes produced good quality characteristics such as Nernstian- and rapid responses, and are minimally interfered with by the alkali and alkaline earth metal ions tested. The membranes were next applied to a flow-through device, enabling it to function as flow-injection analysis (FIA) detector. The performance of the sensor after undergoing the FIA optimization was further evaluated for its selectivity characteristics and lifetime. Results for the determination of chloroquine in synthetic samples that contained common tablet excipients such as glucose, starch, and cellulose, and other foreign species such as cations, citric acid or lactic acid were generally satisfactory. The sensor was also successfully used for the determination of the active ingredients in mock tablets, synthetic fluids and biological fluids. The sensor was applied for the determination of active ingredients and the dissolution profile of commercial tablets was also established.
The concern about our dependency on non-renewable resources and overwhelming environmental issues such as pollution caused by non-degradable packaging materials has prompted researchers to come up with alternatives to solve this problem. Thermoplastic polylactic acid (PLA) has been gaining interest due to its versatility and easy processability, thus this study was carried out to find out the properties of PLA reinforced with pineapple fibers. However, surface of the natural fibers need to be treated for better properties enhancement in the polymer matrices. Considering this, fibers were treated with 10% (w/v) concentration of potassium hydroxide (KOH) and then continued for mixing with PLA at a fixed ratio of plasticizer by using internal mixer, and then the composites were prepared into sheet via hot press. Characterization for the mechanical and morphological was conducted by using tensile testing and scanning electron microscopy, respectively. After the analysis, it is found that the surface treated pineapple fiber composite showed better elongation at break compared to untreated fiber composite. The enhance properties of PLA nanocomposites has potential to be used in various packaging materials.
A binary salt system utilizing lithium iodide (LiI) as the auxiliary component has been introduced to the N-phthaloylchitosan (PhCh) based gel polymer electrolyte consisting of ethylene carbonate (EC), dimethylformamide (DMF), tetrapropylammonium iodide (TPAI), and iodine (I2) in order to improve the performance of dye-sensitized solar cell (DSSC) with efficiency of 6.36%, photocurrent density, JSC of 17.29mAcm-2, open circuit voltage, VOC of 0.59V and fill factor, FF of 0.62. This efficiency value is an improvement from the 5.00% performance obtained by the DSSC consisting of only TPAI single salt system. The presence of the LiI in addition to the TPAI improves the charge injection rates and increases the iodide contribution to the total conductivity and both factors contribute to the increase in efficiency of the DSSC. The interaction behavior between polymer-plasticizer-salt was thoroughly investigated using EIS, FTIR spectroscopy and XRD.
Difficulty in swallowing tablets or capsules has been identified as one of the contributing factors to non-compliance of geriatric patients. Although orally disintegrating tablet was designed for fast disintegration in mouth, the fear of taking solid tablets and the risk of choking for certain patient populations still exist.
A study on the quality of water abstracted for potable use was conducted in the Selangor River basin from November 2008 to July 2009. Seven sampling sites representing the intake points of water treatment plants in the basin were selected to determine the occurrence and level of 15 organochlorine pesticides (OCPs), six phthalate esters (PAEs) and bisphenol A (BPA). Results indicated OCPs were still detected regularly in 66.1 % of the samples with the Σ(15)OCPs ranging from 0.6-25.2 ng/L. The first data on PAEs contamination in the basin revealed Σ(6)PAEs concentrations were between 39.0 and 1,096.6 ng/L with a median concentration of 186.0 ng/L while BPA concentration ranged from <1.2 to 120.0 ng/L. Although di-n-butyl phthalate was detected in all the samples, concentrations of di-ethyl(hexyl)phthalate were higher. Sampling sites located downstream recorded the highest concentrations, together with samples collected during the dry season. Comparison of the detected contaminants with the Department of Environment Water Quality Index (DOE-WQI) showed some agreement between the concentration and the current classification of stream water. While the results suggest that the sites were only slightly polluted and suitable to be used as drinking water source, its presence is cause for concern especially to the fragile firefly "Pteroptyx tener" ecosystem located further downstream.
The occurrence of 14 phthalate metabolites was found in human urine samples collected from seven Asian countries: China, India, Japan, Korea, Kuwait, Malaysia, and Vietnam. Phthalate metabolites were found in all samples, indicating widespread exposure of humans to phthalates in these Asian countries. The highest total (the sum of 14 phthalates) phthalate metabolite concentrations were found in samples collected from Kuwait (median: 1050 ng/mL), followed in decreasing order by samples from India (389 ng/mL), China (234 ng/mL), Vietnam (133 ng/mL), Japan (120 ng/mL), Korea (117 ng/mL), and Malaysia (94.9 ng/mL). The creatinine-adjusted median concentrations of total phthalates for urine samples from Kuwait, India, China, Vietnam, Japan, Korea, and Malaysia were 692, 506, 289, 119, 103, 104, and 169 μg/g creatinine, respectively. Monomethyl phthalate (mMP), monoethyl phthalate (mEP), mono (2-isobutyl phthalate) (miBP), mono-n-butyl phthalate (mBP), and metabolites of di-(2-ethylhexyl) phthalate (DEHP) were the dominant compounds, collectively accounting for >95% of the total concentrations in the samples from the seven countries. The profiles of urinary phthalate metabolite concentrations varied among the samples collected from the seven countries. Urine samples from Kuwait contained the highest concentrations of mEP (median: 391 ng/mL), mBP (94.1 ng/mL), and the metabolites of DEHP (202 ng/mL), whereas samples from China and Japan contained the highest concentrations of miBP (50.8 ng/mL) and mMP (17.5 ng/mL), respectively. mEP was the predominant metabolite in urine samples from India and Kuwait (accounting for 49% of the total), mBP and miBP were the predominant compounds in samples from China (52%), and DEHP metabolites were the predominant compounds in samples from Korea (46%) and Vietnam (52%). Based on the urinary concentrations of mEP, mBP, miBP, and DEHP metabolites of the samples from the seven Asian countries, we estimated daily intake rates of diethyl phthalate (DEP), dibutyl phthalate (DBP), and DEHP. The results indicated that people in the seven Asian countries are exposed to DEP, DBP, and DEHP at levels well below the reference doses (RfD) suggested as unsafe by the U.S. Environmental Protection Agency (EPA). The estimated exposure doses to DEHP in Kuwait, however, were above the RfD recommended by the EPA.
Phthalates have been blended in various compositions as plasticizers worldwide for a variety of purposes. Consequently, humans are exposed to a wide spectrum of phthalates that needs to be researched and understood correctly. The goal of this review is to focus on phthalate's internal exposure pathways and possible role of human digestion on liver toxicity. In addition, special focus was made on stem cell therapy in reverting liver toxicity. The known entry of higher molecular weight phthalates is through ingestion while inhalation and dermal pathways are for lower molecular weight phthalates. In human body, certain phthalates are digested through phase 1 (hydrolysis, oxidation) and phase 2 (conjugation) metabolic processes. The phthalates that are made bioavailable through digestion enter the blood stream and reach the liver for further detoxification, and these are excreted via urine and/or feces. Bis(2-ethylhexyl) phthalate (DEHP) is a compound well studied involving human metabolism. Liver plays a pivotal role in humans for detoxification of pollutants. Thus, continuous exposure to phthalates in humans may lead to inhibition of liver detoxifying enzymes and may result in liver dysfunction. The potential of stem cell therapy addressed herewith will revert liver dysfunction and lead to restoration of liver function properly.
Synthetic plastics are severely detrimental to the environment because non-biodegradable plastics do not degrade for hundreds of years. Nowadays, these plastics are very commonly used for food packaging. To overcome this problem, food packaging materials should be substituted with "green" or environmentally friendly materials, normally in the form of natural fiber reinforced biopolymer composites. Thermoplastic starch (TPS), polylactic acid (PLA) and polybutylene succinate (PBS) were chosen for the substitution, because of their availability, biodegradability, and good food contact properties. Plasticizer (glycerol) was used to modify the starch, such as TPS under a heating condition, which improved its processability. TPS films are sensitive to moisture and their mechanical properties are generally not suitable for food packaging if used alone, while PLA and PBS have a low oxygen barrier but good mechanical properties and processability. In general, TPS, PLA, and PBS need to be modified for food packaging requirements. Natural fibers are often incorporated as reinforcements into TPS, PLA, and PBS to overcome their weaknesses. Natural fibers are normally used in the form of fibers, fillers, celluloses, and nanocelluloses, but the focus of this paper is on nanocellulose. Nanocellulose reinforced polymer composites demonstrate an improvement in mechanical, barrier, and thermal properties. The addition of compatibilizer as a coupling agent promotes a fine dispersion of nanocelluloses in polymer. Additionally, nanocellulose and TPS are also mixed with PLA and PBS because they are costly, despite having commendable properties. Starch and natural fibers are utilized as fillers because they are abundant, cheap and biodegradable.
Starch is a biodegradable polymer produced in abundance from many renewable resources. This study examined the influence of citric acid (0-40% w/wt%) ) and water (0-40% w/wt%) as secondary additive and glycerol as plasticizer on the mechanical properties of bio-plastic starch (BPS) from Malaysian sago. The CA content varies from 0 to 40 w/wt% while water was also varied from 0 to 40 w/wt%. FT-IR spectroscopy showed that acid citric improve the properties of BPS and water give negative effects to the carbon hydrogenbond. It is obvious that the addition of the CA at 30 wt/wt% improve the mechanical property of BPS to more than 40% compare to the addition of water.
Antibacterial effect of modified sago starch-alginate edible film incorporating lemongrass oil at various concentrations was studied. Edible films were prepared from a mixture of modified sago starch and alginate. Lemongrass oil (0.1 - 0.4%, v/w) and glycerol (0 and 20%, w/w) were incorporated in the films to act as natural antimicrobial agent and plasticizer, respectively. The films were characterized for antibacterial activity against food pathogenic bacteria such as Escherichia coli O157:H7, Salmonella Enteritidis and Staphylococcus aureus. The edible film exhibited antibacterial activity against Escherichia coli O157:H7 and Salmonella Enteritidis by using agar diffusion assay method. For films tested against Escherichia coli O157:H7, the zone of inhibition increased significantly (p < 0.05) with addition of lemongrass oil at all levels both in the presence and absence of glycerol. The films also significantly (p < 0.05) inhibited the growth of Salmonella enteritidis only with 0.4% lemongrass oil (in the presence and absence of glycerol). However, the films containing lemongrass oil did not show any inhibition effect on Staphylococcus aureus.
Several blends of cellulose derived from bast part of kenaf (Hibiscus cannabinus L.) plant, with different thermoplastics, low density polyethylene (LDPE) and high density polyethylene (HDPE), were prepared by a melt blending machine. Polyethylene glycol (PEG) was used as plasticizer. Biodegradability of these blends was measured using soil burial test in order to study the rates of biodegradation of these polymer blends. It was found that the cellulose/LDPE and cellulose/HDPE blends were biodegradable in a considerable rate. The bio-composites with high content of cellulose had higher degradation rate. In addition, biodegradability of the bio-composites made up using PEG was superior to those of the bio-composites fabricated without PEG, due to the improved wetting of the plasticizer in the matrix polymer. The results were also supported by the scanning electron microscopy (SEM).
Starch blend films made from sago and mung bean were prepared by casting with glycerol as the plasticizer and subsequently exposed to ultraviolet (UV) irradiation for 2 h. The films were characterized by thickness, moisture sorption isotherms, X-ray diffraction and Fourier transform infrared (FTIR) spectroscopy. All films produced were colorless while incorporation of glycerol resulted in more flexible and manageable films. Moisture sorption isotherms for all films showed sigmoidal shape and the control films showed slightly higher curve than treated films. While for X-ray analysis, the control and treated films for all formulations showed similar pattern, however for treated films showed more crystalline character. UV radiation showed affect on X-ray diffraction and sorption isotherms; however the UV radiation did not affect the spectra pattern of FTIR.
The aim of this study was to investigate the functional properties of chicken skin gelatin films with varied concentrations of a hydrophilic plasticizer. Gelatin film solutions with different glycerol concentrations A(control), B(5%), C(10%), D(15%) and E(20%), were stirred at 45°C for 20min and oven dried at 45°C. Film characterization determination were included, tensile strength (TS), elongation at break (EAB), water vapor permeability (WVP), solubility, transparency, moisture content, Fourier Transform Infrared Spectroscopy (FTIR), and X-ray Diffraction (X-RD). Glycerol added resulted in improvement of TS and WVP properties. Film B (5% glycerol) demonstrated low EAB (106%), WVP (0.0175 g.mm/h.m2.k.Pa) and solubility (58.64%), but with high TS (3.64 MPa), moisture content (16.0%), UV light transmission (0.04%) and transparency (0.81) compared to films C, D and E. FTIR spectrum analyses demonstrated an aliphatic alcohol group only for Film E (20% glycerol). Hence, chicken skin gelatin film at 5% glycerol concentration showed the most promising potential for industrial food processing applications.
This study investigated consequent functional effects (mechanical and physical) on Gelatin/ CMC/Chitosan composite films from the addition of sorbitol. With glycerol as a plasticizer, solutions for Gelatin/CMC/Chitosan composite films containing graduated sorbitol concentrations (0%, 5%, 10%, 15%, 20%, 25% and 30%), were cast on a petri dish and oven dried at 45˚C. The fabricated films were then characterized for tensile strength, elongation at break (EAB) and puncture resistance (mechanical properties); as well as film thickness, water vapor permeability (WVP), thermal properties, light transmittance and transparency (UV and visible light transmission), biodegradability, and X-ray diffraction (physical properties). Results indicated that by increasing sorbitol concentration, melting point and tensile strength decreased overall (p
The potential of Averrhoa bilimbi pectin (ABP) as a source of biopolymer for edible film (EF) production was explored, and deep eutectic solvent (DES) (1% w/w) containing choline chloride-citric acid monohydrate at a molar ratio of 1:1 was used as the plasticizer. The EF-ABP3:1, which was produced from ABP with large branch size, showed a higher value of melting temperature (175.30 °C), tensile stress (7.32 MPa) and modulus (33.64 MPa). The EF-ABP3:1 also showed better barrier properties by obtaining the lowest water vapor transmission rates (1.10-1.18 mg/m2.s) and moisture absorption values (2.61-32.13%) depending on the relative humidity compared to other EF-ABPs (1.39-1.83 mg/m2.s and 3.48-51.50%, respectively) that have linear structure with smaller branch size. From these results, it was suggested that the galacturonic acid content, molecular weight, degree of esterification and pectin structure of ABP significantly influenced the properties of EFs. The interaction of highly branched pectin chains was stronger than the linear chains, thus reduced the effect of plasticizer and produced a mechanically stronger EF with better barrier properties. Hence, it was suggested that these EFs could be used as alternative degradable packaging/coating materials.
This study examines the effects of varying the concentrations of sorbitol (S) and glycerol (G) on the physical, morphological, thermal, and mechanical properties of Dioscorea hispida, starch-based films. In this context, the films of Dioscorea hispida starch were developed using solution casting technique with glycerol (G), sorbitol (S), and a mixture of sorbitol-glycerol (SG) as plasticizers at the ratios of 0, 30, 45, and 60 wt%. The films' moisture contents were increased when increasing the plasticizer contents. The tensile strengths were decreased, but elongations at break were increased; 7.38%-11.54% for G-plasticized films, 10.17%-15.76% for S-plasticized films, and 14.41%- 16.10% for SG-plasticized films with increasing plasticizer concentrations of the film samples. Varying plasticizer concentrations exhibited a minor effect on the S-plasticized film's thermal properties. Significant decrement in the glass transition temperatures of Dioscorea hispida starch films was observed when the plasticizer contents were raised from 30% to 60%. Significantly, the present work has shown that plasticized Dioscorea hispida starch can be considered a promising biopolymer for the applications of biodegradable films.
The physicochemical properties of κ-carrageenan films extracted from Eucheuma cottonii (E. cottonii) incorporated with different concentrations and types of plasticizers were studied. Glycerol, sorbitol, and polyethylene glycol-300 (PEG-300) in the range of 10-60% were used as plasticizers. The results showed that the thickness and moisture content (MC) of films increased significantly (p≤0.05) with the increase in plasticizer concentration. Sorbitol-plasticized films had the lowest values. Sorbitol-plasticized films have better mechanical properties and the lowest water vapor permeability (WVP), solubility and water uptake ratio (WUR) compared with glycerol and PEG-plasticized films (p≤0.05). Fourier transform infrared (FTIR) spectra showed the intermolecular reactions between κ-carrageenan and the plasticizers in the films. Scanning electron microscopy (SEM) observations indicated that sorbitol-plasticized films have a compact structure, even at the highest concentration. The melting temperature (Tm) of films decreased (p≤0.05) with an increase in the plasticizer concentration. Here, the glycerol-plasticized films had the lowest values. X-ray diffraction (XRD) showed broad and narrow peaks of the un-plasticized κ-carrageenan film at 2θ=20.0° and 2θ=8.4°, respectively. The intensity of the broad peak increased and the narrow peak disappeared as the concentration of plasticizers increased. In conclusion, films from E. cottonii successfully produced with sorbitol as the plasticizer exhibited good physical properties as packaging films.
The cellulose microfibers (CMF) from water hyacinth (WH) fiber as a filler in sago starch (SS) biocomposites was investigated. The CMF was isolated by pulping, bleaching and acid hydrolysis methods. The addition of CMF in sago matrix was varied i.e. 0, 5, 10, 15 and 20 wt%. Biocomposites were made by using solution casting and glycerol as a plasticizer. The biocomposites were also determined by tensile test, FTIR, X-Ray, thermogravimetric, SEM, and soil burial tests. The results show that the SS15CMF sample has the highest tensile strength of 10.23 MPa than those other samples. Scanning Electron Microscope (SEM) images show that the strong interaction was formed between CMF WH and matrix. Fourier Transform Infra-red (FTIR) indicated that the functional group of biocomposites was a hydrophilic cluster. The addition of CMF WH in sago starch biocomposites lead to the moisture barrier, crystallinity, and thermal stability increased; it is due to the pure sago starch film was more rapidly degraded than its biocomposites.