  1. Faisal Ismail Bahnasi, Nagham Mohammed Abdullah, Mohamed Ibrahim Abu-Hassan
    Compendium of Oral Science, 2014;1(1):24-29.
    MyJurnal
    Objectives: To evaluate the effect of light-cure devices and curing times on the shear bond strength (SBS) of orthodontic brackets.

    Material and Methods: 60-extracted human premolars were divided into 6-groups of 10-teeth each and bonded with stainless-steel brackets by using 3M Unitek Transbond XT composite. Specimens were cured with halogen, LED and plasma arc lights with two different times for each. The specimens were subjected to shear force till debond with a crosshead speed of 1mm/min and tested after 5min. The stress was calculated and data were subjected to statistical analysis.

    Results: one-way ANOVA and Dunnett T3 post hoc comparison test were used. There were no significant differences between the 6 groups (p < 0.05).

    Conclusions: all curing light methods with loading force after 5 min achieved SBS more than the normal range; therefore, arch wire can be inserted at the same visit using any of tested curing light device or curing time.
    Matched MeSH terms: Resin Cements
  2. Al-Makramani BMA, Razak AAA, Abu-Hassan MI, Al-Sanabani FA, Albakri FM
    Open Access Maced J Med Sci, 2018 Mar 15;6(3):548-553.
    PMID: 29610618 DOI: 10.3889/oamjms.2018.111
    BACKGROUND: The selection of the appropriate luting cement is a key factor for achieving a strong bond between prepared teeth and dental restorations.

    AIM: To evaluate the shear bond strength of Zinc phosphate cement Elite, glass ionomer cement Fuji I, resin-modified glass ionomer cement Fuji Plus and resin luting cement Panavia-F to Turkom-Cera all-ceramic material.

    MATERIALS AND METHODS: Turkom-Cera was used to form discs 10mm in diameter and 3 mm in thickness (n = 40). The ceramic discs were wet ground, air - particle abraded with 50 - μm aluminium oxide particles and randomly divided into four groups (n = 10). The luting cement was bonded to Turkom-Cera discs as per manufacturer instructions. The shear bond strengths were determined using the universal testing machine at a crosshead speed of 0.5 mm/min. The data were analysed using the tests One Way ANOVA, the nonparametric Kruskal - Wallis test and Mann - Whitney Post hoc test.

    RESULTS: The shear bond strength of the Elite, Fuji I, Fuji Plus and Panavia F groups were: 0.92 ± 0.42, 2.04 ± 0.78, 4.37 ± 1.18, and 16.42 ± 3.38 MPa, respectively. There was the statistically significant difference between the four luting cement tested (p < 0.05).

    CONCLUSION: the phosphate-containing resin cement Panavia-F exhibited shear bond strength value significantly higher than all materials tested.

    Matched MeSH terms: Resin Cements
  3. Al-Khadim Aws H., Abdullah H., Al-Ani Sarah T.
    MyJurnal
    Introduction: The purpose of this in vitro study was to evaluate the effect of thermocycling on the compressive strength of selected luting cements. Material and methods: 5 types of luting cements were tested. A total of thirty cylindrical specimens measuring 6mm in height and 4mm in diameter were prepared for each type of cement which were then divided into two groups ie Group 1: Exposure, and Group 2: Control. Both groups were stored in distilled water at 37°C for 24 hours. Group 1 was subjected to 500 cycles in a thermocycling baths of 5ºC and 55ºC with 20 seconds in each bath. Group 2 was not exposed to thermocycling procedure. The compressive strength for each cement type was determined by using a universal testing machine. Results: Resin adhesive cement had the highest compressive strength; followed by conventional glass ionomer cement (GIC) whilst resin modified GIC was the least. Thermocycling had no significant effect on the compressive strength of RelyXTM ARC and Fuji I (p>0.05), but a significant effect on Fuji I CAPSULE, Fuji CEM, Fuji Plus CAPSLUE (p
    Matched MeSH terms: Resin Cements
  4. Zalina Laili, Muhamad Samudi Yasir, Mohd Abdul Wahab Yusof
    Sains Malaysiana, 2017;46:1617-1623.
    The influence of water-to-cement ratio (w/c) on the compressive strength of cement-biochar-spent resins matrix was
    investigated. Spent resins waste from nuclear reactor operation was solidified using cement with w/c ranging from 0.35
    to 0.90 by weight. In this study, biochar was used as a cement admixture. Some properties of spent resins and biochar
    were determined prior to the formulation study. Compressive strength of harden cement-biochar-spent resins matrix
    was determined at 28 days. The compressive strength of cement-biochar-spent resins matrix was found to depend on the
    w/c and the amount of spent resins added to the formulation. The immersion test of cement-biochar-spent resins matrix
    showed no significant effects of cracking and swelling. The compressive strength of the cement-biochar-spent resins
    matrix increased after two weeks in water immersion test.
    Matched MeSH terms: Resin Cements
  5. Omar H, Atta O, El-Mowafy O, Khan SA
    J Dent, 2010;38 Suppl 2:e95-9.
    PMID: 20493232 DOI: 10.1016/j.jdent.2010.05.006
    To determine the effect of thickness of porcelain veneers constructed from CAD-CAM on their final color when two resin cements were used.
    Matched MeSH terms: Resin Cements/chemistry
  6. Al-Makramani BM, Razak AA, Abu-Hassan MI
    J Contemp Dent Pract, 2008;9(2):33-40.
    PMID: 18264523
    The objective of this study is to investigate the effect of different luting agents on the fracture strength of Turkom-Cera all-ceramic copings.
    Matched MeSH terms: Resin Cements*
  7. Lui JL
    Dent Traumatol, 2001 Oct;17(5):227-30.
    PMID: 11678543
    The composite reinforcement technique has been used clinically to salvage damaged root-filled teeth compromised by caries, trauma, developmental abnormalities, internal resorption and iatrogenic causes. This clinical case report describes the use of the technique to reattach a fractured fragment in a compromised endodontically treated root besides reinforcing it for continued function in the mouth. Factors of clinical importance related to this additional application; including reattachment of tooth fragments, post crown retention, coronal microleakage and fracture resistance and strength, are also briefly discussed.
    Matched MeSH terms: Resin Cements/chemistry
  8. Caglar I, Ates SM, Boztoprak Y, Aslan YU, Duymus ZY
    Niger J Clin Pract, 2018 Aug;21(8):1000-1007.
    PMID: 30074001 DOI: 10.4103/njcp.njcp_300_17
    Objective: The aim of this study was to investigate the different surface treatments on the bond strength of self-adhesive resin cement to high-strength ceramic.

    Materials and Methods: Ninety aluminum oxide ceramic (Turkom-Ceramic Sdn. Bhd., Kuala Lumpur, Malaysia) specimens were produced and divided into nine groups to receive the following surface treatments: control group, no treatment (Group C), sandblasting (Group B), silica coating (Group S), erbium: yttrium-aluminum-garnet (Er:YAG) laser irradiation at 150 mJ 10 Hz (Group L1), Er:YAG laser irradiation at 300 mJ 10 Hz (Group L2), sandblasting + L1 (Group BL1), sandblasting + L2 (Group BL2), silica coating + L1 (Group SL1), and silica coating + L2 (Group SL2). After surface treatments, surface roughness (SR) values were measured and surface topography was evaluated. Resin cement was applied on the specimen surface, and shear bond strength (SBS) tests were performed. Data were statistically analyzed using one-way ANOVA and Tukey's multiple comparisons at a significance level of P < 0.05.

    Results: Group S, SL1, and SL2 showed significantly increased SR values compared to the control group (P < 0.05); therefore, no significant differences were found among the SR values of Groups B, BL1, BL2, L1, and L2 and the control group (P > 0.05). Group S showed the highest SBS values, whereas the control group showed the lowest SBS values.

    Conclusion: Silica coating is the most effective method for resin bonding of high strength ceramic, but Er:YAG laser application decreased the effectiveness.

    Matched MeSH terms: Resin Cements/chemistry*
  9. Aldossary MS, Abu Hajia SS, Santini A
    Int Orthod, 2018 12;16(4):638-651.
    PMID: 30385291 DOI: 10.1016/j.ortho.2018.09.005
    OBJECTIVE: To measure Total Light Energy (TLE) Transmission through six makes of ceramic orthodontic brackets alone and bracket-plus-adhesive samples, using the MARC™-Resin Calibrator (RC).

    METHODS: Six makes, three each monocrystalline (M) and polycrystalline (P) were used; PureSapphire (M), SPA Aesthetic (M), Ghost (M), Mist (P), Reflections (P), and Dual Ceramic (P). The Ortholux™ Light Curing Unit (LCU) was used to cure the orthodontic adhesive Transbond™XT. The LCU's tip irradiance was measured and TLE transmitted through the ceramic bracket was obtained, then adhesive added to the bracket, and transmitted TLE measured through bracket-plus-adhesive samples. The LCU was set at five seconds as recommended for curing adhesive through ceramic brackets.

    RESULTS: Mean tip irradiance was 1859.2±16.2mW/cm2. The TLE transmitted through brackets alone ranged 1.7 to 3.9J/cm2, in the descending order: Ghost>Pure Sapphire>Reflections>Mist>SPA Aesthetics>Dual Ceramic. The TLE transmitted through bracket-plus-adhesive samples ranged 1.6 to 3.7J/cm2, in the descending order: Ghost>Mist>Reflections>Pure Sapphire>SPA Aesthetics>Dual Ceramic. TLE was reduced with the addition of adhesive (range -0.1 to -0.7J/cm2). There was a significant difference for Pure Sapphire, Reflections, and Mist (P<0.05), but not for SPA Aesthetics, Ghost, and Dual Ceramic. There was no overall significant difference between the monocrystalline and polycrystalline makes. The two best makes were of the monocrystalline type, concerning TLE transmission, but with the exception of polycrystalline Dual Ceramic; the next worst make was a monocrystalline bracket, SPA Aesthetics.

    CONCLUSION: Light energy attenuation through ceramic orthodontic brackets is make-dependent, with no overall difference between monocrystalline and polycrystalline brackets. Light energy is further attenuated with the addition of resin-based orthodontic adhesive.

    Matched MeSH terms: Resin Cements/chemistry
  10. Razak AA, Abu-Hassan MI, Al-Makramani BM, Al-Sanabani FA, Al-Shami IZ, Almansour HM
    J Contemp Dent Pract, 2016 Nov 01;17(11):920-925.
    PMID: 27965501
    AIM: The aim of this study was to evaluate the effect of surface treatments on shear bond strength (SBS) of Turkom-Cera (Turkom-Ceramic (M) Sdn. Bhd., Puchong, Malaysia) all-ceramic material cemented with resin cement Panavia-F (Kuraray Medical Inc., Okayama, Japan).

    MATERIALS AND METHODS: Forty Turkom-Cera ceramic disks (10 mm × 3 mm) were prepared and randomly divided into four groups. The disks were wet ground to 1000-grit and subjected to four surface treatments: (1) No treatment (Control), (2) sandblasting, (3) silane application, and (4) sandblasting + silane. The four groups of 10 specimens each were bonded with Panavia-F resin cement according to manufacturer's recommendations. The SBS was determined using the universal testing machine (Instron) at 0.5 mm/min crosshead speed. Failure modes were recorded and a qualitative micromorphologic examination of different surface treatments was performed. The data were analyzed using the one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests.

    RESULTS: The SBS of the control, sandblasting, silane, and sandblasting + silane groups were: 10.8 ± 1.5, 16.4 ± 3.4, 16.2 ± 2.5, and 19.1 ± 2.4 MPa respectively. According to the Tukey HSD test, only the mean SBS of the control group was significantly different from the other three groups. There was no significant difference between sandblasting, silane, and sandblasting + silane groups.

    CONCLUSION: In this study, the three surface treatments used improved the bond strength of resin cement to Turkom-Cera disks.

    CLINICAL SIGNIFICANCE: The surface treatments used in this study appeared to be suitable methods for the cementation of glass infiltrated all-ceramic restorations.

    Matched MeSH terms: Resin Cements/chemistry
  11. Daood U, Fawzy A
    J Mech Behav Biomed Mater, 2023 Apr;140:105737.
    PMID: 36827934 DOI: 10.1016/j.jmbbm.2023.105737
    The aim is to evaluate the development of an experimental multi-mode/Universal resin-based dentin adhesive modified with synthetic Mg2+ doped hydroxyapatite crystals (HAp) having self-remineralization and antibiofilm properties. HAp doped with Mg2+ was prepared by the precipitation method. Experimental adhesives were subjected to degree of conversion and X-ray diffraction test for size and crystal structure. Bond strength was tested, and electron microscopy (SEM/TEM) imaging of resin-dentin interface was done along with nanoleakage, nanoindentation, confocal and Raman analyses. S. mutans was analysed using CLSM images against modified adhesive specimens. Nucleating abilities within the resin-dentin specimens are determined by measuring Ca2+. Alkaline phosphatase, Runx2, and Ocn transcripts are amplified using quantitative polymerase chain reaction (q-PCR). A calcium assay is performed to quantify level of mineralisation. When compared to control adhesives, the 0.5% Hap/Mg2+ containing experimental dentin adhesive demonstrated improved interaction with dentin. The preservation of uniform intact hybrid layer with the absence of nanoleakage indicated dentin bond integrity with 0.5% HAP/Mg2+ modified adhesive. Self-remineralization and antibiofilm potentials are supported.
    Matched MeSH terms: Resin Cements/chemistry
  12. Reza F, Ibrahim NS
    Eur J Dent, 2015 2 26;9(1):74-79.
    PMID: 25713488 DOI: 10.4103/1305-7456.149646
    OBJECTIVE: Fiber post is cemented to a root canal to restore coronal tooth structure. This research aims to evaluate the effect of ultraviolet (UV) irradiation on bond strength of fiber post with resin cement.

    MATERIALS AND METHODS: A total of 40 of the two types of fiber posts, namely, FRC Prostec (FRC) and Fiber KOR (KOR), were used for the experiment. UV irradiation was applied on top of the fiber post surface for 0, 15, 20, and 30 min. The irradiated surface of the fiber posts (n = 5) were immediately bonded with resin cement (Rely X U200) after UV irradiation. Shear bond strength (SBS) MPa was measured, and the dislodged area of post surfaces was examined with scanning electron microscopes. Changes in surface roughness (Ra) of the FRC group after UV irradiation were observed (n = 3) using atomic force microscopy. Data of SBS were statistically analyzed using one-way analysis of variance, followed by multiple comparisons (P < 0.05).

    RESULTS: SBS was significantly higher for 20 min of UV irradiation of the FRC group while significantly higher SBS was observed with 15 min of UV irradiation of the KOR group. Resin cement was more evident (cohesive failure) on the dislodged post surface of the UV treated groups compared with the control. The surface roughness of the FRC post was Ra = 175.1 nm and Ra = 929.2 nm for the control and the 20 min group, respectively.

    CONCLUSIONS: Higher surface roughness of the UV irradiated group indicated formation of mechanical retention on the fiber post surface. Evidence of cohesive failure was observed which indicated higher SBS of fiber post with the UV irradiated group.

    Matched MeSH terms: Resin Cements
  13. Saman SA, Chang KH, Abdullah AFL
    J Forensic Sci, 2021 Mar;66(2):608-618.
    PMID: 33202056 DOI: 10.1111/1556-4029.14625
    Abuse of solvent-based adhesives jeopardizes world population, especially the young generation. Adhesive-related exhibits encountered in forensic cases might need to be determined if they could have come from a particular source or to establish link between cases or persons. This study was aimed to discriminate solvent-based adhesives, especially to aid forensic investigation of glue sniffing activities. In this study, thirteen brands with three samples each, totaling at 39 adhesive samples, were analyzed using attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy followed by chemometric methods. Experimental output showed that adhesive samples utilized in this study were less likely to change in their ATR-FTIR profiles over time, at least up to 2 months. No interference from plastic materials was noticed based on ATR-FTIR profile comparison. Physical examination could differentiate the samples into two groups, namely contact adhesives and cement adhesives. A principal component analysis-score linear discriminative analysis (PC-score LDA) model resulted in 100% and 98.6% correct classification in discriminating the two groups of adhesive samples, forming seven discriminative clusters. Test set with adhesive samples applied glass slide and plastic substrates also demonstrated a 100% correct classification into their respective groups. As a conclusion, the method allowed for discrimination of adhesive samples based on the spectral features, displaying relationship among samples. It is hoped that this comparative information is beneficial to trace the possible source of solvent-based adhesives, whenever they are recovered from a crime scene, for forensic investigation.
    Matched MeSH terms: Resin Cements
  14. Fawzy AS, Daood U, Matinlinna JP
    Dent Mater, 2019 07;35(7):979-989.
    PMID: 31003759 DOI: 10.1016/j.dental.2019.04.001
    OBJECTIVE: This study introduced the potential and proof-of-concept of high intensity focused ultrasound (HIFU) technology for dentin-surface treatment for resin-dentin bonding without acid-aided demineralization. This new strategy could provide a way to enhance interface-integrity and bond-durability by changing the nature of dentin-substrate; bonded-interface structure and properties; and minimizing denuded-collagen exposure.

    METHODS: The interaction between HIFU waves and dentin-surface in terms of structural, mechanical and chemical variations were investigated by SEM, TEM, AFM, nano-indentation and Raman-analysis. The bonding between HIFU-treated dentin and two-step, etch-and-rinse, adhesive was preliminary explored by characterizing dentin-bound proteases activities, resin-dentin interfacial morphology and bond-durability with HIFU exposure at different time-points of 60, 90 and 120 s compared to conventional acid-etching technique.

    RESULTS: With the increase in HIFU exposure-time from 60-to-120 s, HIFU waves were able to remove the smear-layer, expose dentinal-tubules and creating textured/rough dentin surface. In addition, dentin surfaces showed a pattern of interlocking ribbon-like minerals-coated collagen-fibrils protruding from the underlaying amorphous dentin-background with HIFU exposure for 90 s and 120 s. This characteristic pattern of dentin-surface showing inorganic-minerals associated/aligned with collagen-fibrils, with 90-to-120 s HIFU-treatment, was confirmed by the Raman-analysis. HIFU-treated specimens showed higher nano-indentation properties and lower concentrations of active MMP-2 and Cathepsin-K compared to the acid-etched specimens. The resin-dentin bonded interface revealed the partial/complete absence of the characteristic hybrid-layer formed with conventional etch-and-rinse bonding strategy. Additionally, resin-infiltration and resin-tags formation were enhanced with the increase in HIFU exposure-time to 120 s. Although, all groups showed significant decrease in bond-strength after 12 months compared to 24 h storage in artificial saliva, groups exposed to HIFU for 90 s and 120 s showed significantly higher μTBS compared to the control acid-etched group.

    SIGNIFICANCE: The implementation of HIFU-technology for dental hard-tissues treatment could be of potential significance in adhesive/restorative dentistry owing to its ability of controlled, selective and localised combined tissue alteration/ablation effects.

    Matched MeSH terms: Resin Cements
  15. Fu C, Deng S, Koneski I, Awad MM, Akram Z, Matinlinna J, et al.
    J Mech Behav Biomed Mater, 2020 12;112:104082.
    PMID: 32979607 DOI: 10.1016/j.jmbbm.2020.104082
    OBJECTIVE: To investigate the effect of blue light photoactivated riboflavin modified universal adhesives on dentin collagen biodegradation resistance, dentin apparent elastic modulus, and resin-dentin bond strength with interfacial morphology.

    METHODS: Dentin slabs were treated with 0.1% riboflavin-5-phosphate modified (powder added slowly while shaking and then sonicated to enhance the dispersion process) Universal Adhesive Scotch Bond and Zipbond™ along with control (non-modified) and experimental adhesives, photoactivated with blue light for 20s. Hydroxyproline (HYP) release was assessed after 1-week storage. Elastic-modulus testing was evaluated using universal testing machine at 24 h. Resin-dentin interfacial morphology was assessed with scanning electron-microscope, after 6-month storage. 0.1% rhodamine dye was added into each adhesive and analyzed using CLSM. Detection of free amino groups was carried out using ninhydrin and considered directly proportional to optical absorbance. Collagen molecular confirmation was determined using spectropolarimeter to evaluate and assess CD spectra. For molecular docking studies with riboflavin (PDB ID file), the binding pocket was selected with larger SiteScore and DScore using Schrodinger PB software. After curing, Raman shifts in Amide regions were obtained at 8 μm levels. Data were analyzed using Two-way analysis of variance (ANOVA, p ≤ 0.05) and Tukey-Kramer multiple comparison post hoc tests.

    RESULTS: At baseline, bond strength reduced significantly (p ≤ 0.05) in control specimens. However, at 6 months' storage, UVA Zipbond™ had significantly higher μTBS. Resin was able to diffuse through the porous demineralized dentin creating adequate hybrid layers in both 0.1%RF modified adhesives in CLSM images. In riboflavin groups, hybrid layer and resin tags were more pronounced. The circular dichroism spectrum showed negative peaks for riboflavin adhesive specimens. Best fitted poses adopted by riboflavin compound are docked with MMP-2 and -9 proteases. Amide bands and CH2 peaks followed the trend of being lowest for control UA Scotch bond adhesive specimens and increasing in Amides, proline, and CH2 intensities in 0.1%RF modified adhesive specimens. All 0.1%RF application groups showed statistically significant (p resin-dentin interfacial integrity and bond strength of universal adhesive to dentin.

    Matched MeSH terms: Resin Cements
  16. Lim, Siau Peng, Fazal Reza, Zaihan Ariffin
    MyJurnal
    The purpose of this study was to evaluate hardness (indicator for polymerization) and thickness of two types of resin cement at coronal, middle and apical level of tooth root canal. Ten extracted maxillary incisors were instrumented and post space was prepared for cementation of titanium post. Samples were divided into two groups and each group was cemented either of the two types of resin cements; Panavia F [dual-cured (PF)] and Rely X Luting 2 [self-cured (RL)]. The teeth were longitudinally sectioned; hardness and thickness was measured using Vickers hardness tester and a microscope (Leica DMLM). SEM observations along the cement line at the 3 different root levels were performed. Statistical analysis was performed to test significance of differences in hardness and thickness of the two types of cement (t-test; p= 0.05) and at different levels of the same type (one-way ANOVA followed by multiple comparison; p= 0.05). Significant difference of hardness was found at the apical level between the two groups and between the coronal and apical level of PF (p0.05). Moreover, voids were more obvious within the dual-cured group of cement. Dual-cured resin cement was found to be less polymerized than self-cured type at apical level. Increased thicknesses of resin cements in comparison to post space size were observed in both groups. Use of metallic post with resin cements needs further evaluation.
    Matched MeSH terms: Resin Cements
  17. Rajeev V, Arunachalam R, Nayar S, Arunima PR, Ganapathy S, Vedam V
    Eur J Dent, 2017 4 25;11(1):58-63.
    PMID: 28435367 DOI: 10.4103/ejd.ejd_113_16
    OBJECTIVE: This in vitro study was designed to assess shear bond strength (SBS) of ormocer flowable (OF) resin as a luting agent, ormocer as an indirect veneer material with portrayal of modes of failures using scanning electron microscope (SEM).

    MATERIALS AND METHODS: Sixty maxillary central incisors were divided into Group I, II, and III with 20 samples each based on luting cement used. They were OF, self-adhesive (SA) cement, and total etch (TE) cement. These groups were subdivided into "a" and "b" of ten each based on the type of veneering materials used. Veneer discs were fabricated using Ormocer restorative (O) and pressable ceramic (C). Specimens were thermocycled and loaded under universal testing machine for SBS. The statistical analysis was done using one-way ANOVA post hoc Tukey honest significant difference method.

    RESULTS: A significant difference was observed between the Groups I and II (P < 0.05). The highest mean bond strength when using ormocer veneer was obtained with the Group Ia (19.11 ± 1.92 Mpa) and lowest by Group IIa (8.1 ± 1.04 Mpa), whereas the highest mean bond strength while using ceramic veneer was of similar range for Group Ib (18.04 ± 4.08 Mpa) and Group IIIb (18.07 ± 1.40 Mpa). SEM analysis revealed OF and TE presented mixed type of failure when compared with SA where failure mode was totally adhesive.

    CONCLUSION: OF was found equally efficient like TE. Bond strength of ormocer as a veneer was not inferior to ceramic making it one of the promising additions in the field of dentistry.

    Matched MeSH terms: Resin Cements
  18. Annuar, W.A., Abdullah, H.
    Ann Dent, 2003;10(1):-.
    MyJurnal
    This study is conducted to compare two resin luting cements (Rely XTMARC,3M and Compolute™ESPE) on their microleakage with one composite inlay system (Filtek™ Z250 Universal Restorative Materials, 3M). Thirty conventional inlays, Class II MOIDO cavity with gingival margin I mm above the cementoenamel junction, were prepared in premolar teeth. The composite inlays were fabricated directly on the prepared teeth using layering technique. Fifteen of the inlays were cemented with RelyTMX ARC and fifteen with Compolute™ (ESPE). The specimens were kept at 370 C for 10 days before thermocycling and immersed in methylene blue 2% solution for 24 hours. The teeth were sectioned mesio-distally. The site and degree of leakage of each section was scored using a visual scoring system under a stereomicroscope at a magnification of 1.5X. Results showed that there was no significant difference in'leakage extent (p>O.05), between Rely X™ARC and Compolute™. For both materials, leakage occurred most commonly within the enamel surface and between the cement-tooth interfaces. None of the leakage occurred between inlay - cement interface. There is no significant difference in the extent of leakage between Rely XTMARC compared to Compolute™.
    Matched MeSH terms: Resin Cements
  19. Mohamed Abdulmunem, Hadijah Binti Abdullah, Noor Hayaty Binti Abu Kasim, Ali Dabbagh
    Sains Malaysiana, 2015;44:1189-1194.
    The aim of this study was to investigate the simultaneous influence of various dental posts and cementation materials on the fracture resistance and failure mode of the endodontically-treated teeth. Sixty endodontically treated upper central incisors were randomly divided into two main groups, each consisted of three subgroups restored with titanium, fiber and stainless steel posts. The posts in the first and second groups were luted with zinc phosphate and composite resin cements, respectively. Composite cores were built-up over the specimens and then retained with nickel-chromium crowns. Specimens were thermocycled and then loaded at 135o until failures were observed. The obtained data of fracture resistances and failure modes were analyzed using Two-way ANOVA and the Chi-Square tests, respectively. The results showed that the zinc phosphate cement resulted in relatively higher fracture resistances. However, luting of dental posts with composite resin provided more restorable failures in endodontically-treated teeth. Moreover, the teeth restored by fiber posts exhibited desirable fracture resistances with more restorable failure modes, compared with those restored by titanium or stainless steel posts.
    Matched MeSH terms: Resin Cements
  20. Mohd Zainal Abidin R, Luddin N, Shamsuria Omar N, Mohamed Aly Ahmed H
    J Clin Pediatr Dent, 2015;39(3):235-40.
    PMID: 26208068 DOI: 10.17796/1053-4628-39.3.235
    To compare the cytotoxicity of conventional GIC and Resin Modified GIC (RMGIC) polymerized at 2 different times on stem cells from human exfoliated deciduous teeth (SHED).
    Matched MeSH terms: Resin Cements/toxicity*
Filters
Contact Us

Please provide feedback to Administrator (afdal@afpm.org.my)

External Links