There is a great demand of Hydroxyapatite (HA) material in Orthopaedics and Dental applications due to its similarity to human bone. However, the lack of availability and due to high import cost of this material in Malaysia, research in producing synthetic HA locally is therefore timely. The use of local resources as the raw materials for the production of HA is also desirable in reducing the overall cost of HA. In this study, two HA materials were synthesised from different starting precursors, i.e. commercial pure Ca(OH)2 (HAS) and Ca(OH)2 directly from a local natural limestone deposit (HAL). Whereas a commercially available HA "Captal 60" (HAC) was used as reference. The synthesised powders obtained were fired at 1000 degrees C and at 1250 degrees C. Characterisation evaluations on bulk properties were carried out using XRD, SEM-EDX, ICP and FTIR. The results indicate that both HAS and HAL are comparable to HAC even at 1000 degrees C. Thus, the local natural limestone can be used to form HA. However, the overall appearance of these materials are quite different (HAC - blue, HAS - greenish and HAL - light green). The reasons for this and the subsequent mechanical and bioactive effects of these materials are currently being investigated.
The paper presents a method of producing synthetic Hydroxyapatite (HA) Ca10(PO4)6(OH)2 and other apatites for biological use by solid-state reaction. The solid-state reaction involves mix-grinding dry powders of beta-tricalcium phosphate powder (TCP) and either calcium hydroxide (Ca(OH)2) or calcium carbonate (CaCO3) or combination thereof, from pure commercial chemicals or derived from natural limestone or from seashells, of total calcium/phosphorus molar ratio between 1.5 to 2.0, to particle size of less than 10 microns, and firing the resultant powder to temperature between 600 degrees C - 1250 degrees C in atmosphere or in controlled atmospheric condition. The resultant apatites formed were characterised using XRD, SEM-EDX and FTIR. The presented reaction process was found to be much simpler compared to conventional methods of producing synthetic apatites since it involves only dry mix-grinding of the reactants before firing at high temperatures based on the required levels of purity. It can also produce synthetic apatites with good reproducibility in a shorter time. Thus the presented method has a great industrial value.
Hydroxyapatite (HA) has been earmarked as suitable for implantation within the human of its chemical makeup to human bone. In this paper, HA powders were synthesized via the precipitation method where phosphoric acid (H3PO4) was titrated into calcium hydroxide solution [Ca(OH)2]. Two parameters such as temperature and stirring rate were identified as factors that influenced the amount and purity of HA powder. Phase identification of the synthesized powder was done using X-Ray Diffraction (XRD). The results show that HA phase can be synthesized from this titration process of Ca(OH)2 and H3PO4 with yield amount of HA powder around 45 - 61 grams but with less than hundred percent purity. In order to study the effect of heat treatment to HA crystals structure, HA powder was calcined at 850 degrees C for 2 hours. It's found that the degree of crystallinity increases after calcination because of lattice expansion when the materials were heated at higher temperature
The standard bioglass composition GS45 as well as with excess silica GS50 or with the addition of 5% titanium oxide GS45+Ti5, were prepared by the polymeric route. The different glass components were added to the formed polymer. Firing at 700 degrees C gave an amorphous product with microporous texture that readily crystallizes out at 900 degrees C. The prepared materials were highly porous with two modes of pore system micro-pores and macro-pores with a size ranging between 100 microm to 0.006 microm and a porosity reaching 73%. The measured bulk density was between 0.36 to 1.1g/cm3. The fired material preserved the former structure of the polymer precursor. Biocompatibility was verified in vitro and vivo. IR of the specimens previously immersed in SBF revealed the formation of apatite like layer. While the histology sections of implants in rate femurs showed new bone tissue or bone trabeculae after 21 days.