METHODS: This study was conducted between the years 2014 to 2016 at the Tissue Engineering Centre, UKM Medical Centre. OTC-I was extracted from ovine tendon, and fabricated into 3D scaffolds in the form of sponge, hydrogel and film. A polystyrene surface coated with OTC-I was used as the 2D culture condition. Genipin was used to crosslink the OTC-I. A non-coated polystyrene surface was used as a control. The mechanical strength of OTC-I scaffolds was evaluated. Attachment, proliferation and morphological features of HDF were assessed and compared between conditions.
RESULTS: The mechanical strength of OTC-I sponge was significantly higher than that of the other scaffolds. OTC-I scaffolds and the coated surface significantly enhanced HDF attachment and proliferation compared to the control, but no differences were observed between the scaffolds and coated surface. In contrast, the morphological features of HDF including spreading, filopodia, lamellipodia and actin cytoskeletal formation differed between conditions.
CONCLUSION: OTC-I can be moulded into various scaffolds that are biocompatible and thus could be suitable as scaffolds for developing tissue substitutes for clinical applications and in vitro tissue models. However, further study is required to determine the effect of morphological properties on the functional and molecular properties of HDF.
Methods: Autologous whole blood collected 72 h before surgery was processed to prepare platelet concentrates and cryoprecipitate. In a closed system, calcium was added to the cryoprecipitate to release autologous thrombin and generate a firm fibrin clot. The fibrin clot, platelets and calcium were then placed in a conical flask in which a PRF glue formed. The protocol was validated through determination of pre- and post-platelet counts and fibrinogen amounts in the product.
Results: Platelets were recovered with 68% efficiency during the preparation. Essentially no platelets or fibrinogen were found in the supernatant of the PRF glue, suggesting that nearly all had been incorporated in a PRF glue having a relatively large (8 cm × 10 cm) size.
Conclusion: The protocol described here is a cost-effective, simple and closed system that can be used to produce large-size PRF glue to promote repair of major surgical defects.