ZnO nanorods were synthesized using a low-cost sol-gel spin coating technique. The synthesized nanorods were consisted of hexagonal phase having c-axis orientation. SEM images reflected perpendicular ZnO nanorods forming bridging network in some areas. The impact of different hydrogen concentrations on the Pd-sensitized ZnO nanorods was investigated using an impedance spectroscopy (IS). The grain boundary resistance (Rgb) significantly contributed to the sensing properties of hydrogen gas. The boundary resistance was decreased from 11.95 to 3.765 kΩ when the hydrogen concentration was increased from 40 to 360 ppm. IS gain curve showed a gain of 6.5 for 360 ppm of hydrogen at room temperature. Nyquist plot showed reduction in real part of impedance at low frequencies on exposure to different concentrations of hydrogen. Circuit equivalency was investigated by placing capacitors and resistors to identify the conduction mechanism according to complex impedance Nyquist plot. Variations in nanorod resistance and capacitance in response to the introduction of various concentrations of hydrogen gas were obtained from the alternating current impedance spectra.
The effects of different post-deposition annealing ambients (oxygen, argon, forming gas (95% N2 + 5% H2), and nitrogen) on radio frequency magnetron-sputtered yttrium oxide (Y2O3) films on n-type gallium nitride (GaN) substrate were studied in this work. X-ray photoelectron spectroscopy was utilized to extract the bandgap of Y2O3 and interfacial layer as well as establishing the energy band alignment of Y2O3/interfacial layer/GaN structure. Three different structures of energy band alignment were obtained, and the change of band alignment influenced leakage current density-electrical breakdown field characteristics of the samples subjected to different post-deposition annealing ambients. Of these investigated samples, ability of the sample annealed in O2 ambient to withstand the highest electric breakdown field (approximately 6.6 MV/cm) at 10-6 A/cm2 was related to the largest conduction band offset of interfacial layer/GaN (3.77 eV) and barrier height (3.72 eV).
Band gap change in doped ZnO is an observed phenomenon that is very interesting from the fundamental point of view. This work is focused on the preparation of pure and single phase nanostructured ZnO and Cu as well as Mn-doped ZnO for the purpose of understanding the mechanisms of band gap narrowing in the materials. ZnO, Zn0.99Cu0.01O and Zn0.99Mn0.01O materials were prepared using a wet chemistry method, and X-ray diffraction (XRD) results showed that all samples were pure and single phase. UV-visible spectroscopy showed that materials in the nanostructured state exhibit band gap widening with respect to their micron state while for the doped compounds exhibited band gap narrowing both in the nano and micron states with respect to the pure ZnO materials. The degree of band gap change was dependent on the doped elements and crystallite size. X-ray photoelectron spectroscopy (XPS) revealed that there were shifts in the valence bands. From both UV-visible and XPS spectroscopy, it was found that the mechanism for band gap narrowing was due to the shifting of the valance band maximum and conduction band minimum of the materials. The mechanisms were different for different samples depending on the type of dopant and dimensional length scales of the crystallites.
We demonstrate a systematic computational analysis of the measured optical and charge transport properties of the spray pyrolysis-grown ZnO nanostructures, i.e. nanosphere clusters (NSCs), nanorods (NRs) and nanowires (NWs) for the first time. The calculated absorbance spectra based on the time-dependent density functional theory (TD-DFT) shows very close similarity with the measured behaviours under UV light. The atomic models and energy level diagrams for the grown nanostructures were developed and discussed to explain the structural defects and band gap. The induced stresses in the lattices of ZnO NSCs that formed during the pyrolysis process seem to cause the narrowing of the gap between the energy levels. ZnO NWs and NRs show homogeneous distribution of the LUMO and HOMO orbitals all over the entire heterostructure. Such distribution contributes to the reduction of the band gap down to 2.8 eV, which has been confirmed to be in a good agreement with the experimental results. ZnO NWs and NRs exhibited better emission behaviours under the UV excitation as compared to ZnO NSCs and thin film as their visible range emissions are strongly quenched. Based on the electrochemical impedance measurement, the electrical models and electrostatic potential maps were developed to calculate the electron lifetime and to explain the mobility or diffusion behaviours in the grown nanostructure, respectively.
Generation of hybrid nanostructures has been attested as a promising approach to develop high-performance sensing substrates. Herein, hybrid zinc oxide (ZnO) nanorod dopants with different gold (Au) thicknesses were grown on silicon wafer and studied for their impact on physical, optical and electrical characteristics. Structural patterns displayed that ZnO crystal lattice is in preferred c-axis orientation and proved the higher purities. Observations under field emission scanning electron microscopy revealed the coverage of ZnO nanorods by Au-spots having diameters in the average ranges of 5-10 nm, as determined under transmission electron microscopy. Impedance spectroscopic analysis of Au-sputtered ZnO nanorods was carried out in the frequency range of 1 to 100 MHz with applied AC amplitude of 1 V RMS. The obtained results showed significant changes in the electrical properties (conductance and dielectric constant) with nanostructures. A clear demonstration with 30-nm thickness of Au-sputtering was apparent to be ideal for downstream applications, due to the lowest variation in resistance value of grain boundary, which has dynamic and superior characteristics.
A biosensor for measuring the antidiabetic potential of medicinal plants was developed by covalent immobilization of α-glucosidase (AG) enzyme onto amine-functionalized multi-walled carbon nanotubes (MWCNTs-NH2). The immobilized enzyme was entrapped in freeze-thawed polyvinyl alcohol (PVA) together with p-nitrophenyl-α-D-glucopyranoside (PNPG) on the screen-printed carbon electrode at low pH to prevent the premature reaction between PNPG and AG enzyme. The enzymatic reaction within the biosensor is inhibited by bioactive compounds in the medicinal plant extracts. The capability of medicinal plants to inhibit the AG enzyme on the electrode correlates to the potential of the medicinal plants to inhibit the production of glucose from the carbohydrate in the human body. Thus, the inhibition indicates the antidiabetic potential of the medicinal plants. The performance of the biosensor was evaluated to measure the antidiabetic potential of three medicinal plants such as Tebengau (Ehretis laevis), Cemumar (Micromelum pubescens), and Kedondong (Spondias dulcis) and acarbose (commercial antidiabetic drug) via cyclic voltammetry, amperometry, and spectrophotometry. The cyclic voltammetry (CV) response for the inhibition of the AG enzyme activity by Tebengau plant extracts showed a linear relation in the range from 0.423-8.29 μA, and the inhibition detection limit was 0.253 μA. The biosensor exhibited good sensitivity (0.422 μA/mg Tebengau plant extracts) and rapid response (22 s). The biosensor retains approximately 82.16 % of its initial activity even after 30 days of storage at 4 °C.
Lubricant oils take significant part in current health and environmental considerations since they are an integral and indispensable component of modern technology. Antioxidants are probably the most important additives used in oils because oxidative deterioration plays a major role in oil degradation. Zeolite nanoparticles (NPs) have been proven as another option as green antioxidants in oil formulation. The anti-oxidative behavior of zeolite NPs is obvious; however, the phenomenon is still under investigation. Herein, a study of the effect of extra-framework cations stabilized on Linde Type L (LTL) zeolite NPs (ca. 20 nm) on inhibition of oxidation in palm oil-based lubricant oil is reported. Hydrophilic LTL zeolites with a Si/Al ratio of 3.2 containing four different inorganic cations (Li(+), Na(+), K(+), Ca(2+)) were applied. The oxidation of the lubricant oil was followed by visual observation, colorimetry, fourier transform infrared (FTIR) spectroscopy, (1)H NMR spectroscopy, total acid number (TAN), and rheology analyses. The effect of extra-framework cations to slow down the rate of oil oxidation and to control the viscosity of oil is demonstrated. The degradation rate of the lubricant oil samples is decreased considerably as the polarizability of cation is increased with the presence of zeolite NPs. More importantly, the microporous zeolite NPs have a great influence in halting the steps that lead to the polymerization of the oils and thus increasing the lifetime of oils.
Protein corona has became a prevalent subject in the field of nanomedicine owing to its diverse role in determining the efficiency, efficacy, and the ultimate biological fate of the nanomaterials used as a tool to treat and diagnose various diseases. For instance, protein corona formation on the surface of nanoparticles can modify its physicochemical properties and interfere with its intended functionalities in the biological microenvironments. As such, much emphasis should be placed in understanding these complex phenomena that occur at the bio-nano interface. The main aim of this review is to present different factors that are influencing protein-nanoparticle interaction such as physicochemical properties of nanoparticle (i.e., size and size distribution, shape, composition, surface chemistry, and coatings) and the effect of biological microenvironments. Apart from that, the effect of ignored factors at the bio-nano interface such as temperature, plasma concentration, plasma gradient effect, administration route, and cell observer were also addressed.
This paper presents a unique synergistic behavior between a graphene oxide (GO) and graphene nanoplatelet (GnP) composite in an aqueous medium. The results showed that GO stabilized GnP colloid near its isoelectric point and prevented rapid agglomeration and sedimentation. It was considered that a rarely encountered charge-dependent electrostatic interaction between the highly charged GO and weakly charged GnP particles kept GnP suspended at its rapid coagulation and phase separation pH. Sedimentation and transmission electron microscope (TEM) micrograph images revealed the evidence of highly stable colloidal mixtures while zeta potential measurement provided semi-quantitative explanation on the mechanism of stabilization. GnP suspension was confirmed via UV-vis spectral data while contact angle measurement elucidated the close resemblance to an aqueous solution indicating the ability of GO to mediate the flocculation prone GnP colloids. About a tenfold increase in viscosity was recorded at a low shear rate in comparison to an individual GO solution due to a strong interaction manifested between participating colloids. An optimum level of mixing ratio between the two constituents was also obtained. These new findings related to an interaction between charge-based graphitic carbon materials would open new avenues for further exploration on the enhancement of both GO and GnP functionalities particularly in mechanical and electrical domains.
A green sonochemical method was developed for preparing silver nanoparticles (Ag-NPs) in different concentrations of kappa carrageenan (κ-carrageenan). The κ-carrageenan was used as a natural eco-friendly stabilizer, and ultrasonic irradiation was used as a green reducing agent. The number of Ag-NPs increased with increasing κ-carrageenan concentrations. Formation of Ag/κ-carrageenan was determined by UV-visible spectroscopy where the surface plasmon absorption maximum was observed at 402 to 420 nm. The X-ray diffraction (XRD) analysis showed that the Ag-NPs are of a face-centered cubic structure. The Fourier transform infrared (FT-IR) spectrum indicated the presence of Ag-NPs in κ-carrageenan. Transmission electron microscopy (TEM) image for the highest concentration of κ-carrageenan showed the distribution of Ag-NPs with an average particle size near to 4.21 nm. Scan electron microscopy (SEM) images illustrated the spherical shape of the Ag-NPs. The use of photo irradiation provides a green and economic feature to this work.
We report the growth of gallium-based compounds, i.e., gallium oxynitride (GaON) and gallium oxide (Ga2O3) on multilayer graphene (MLG) on insulator using a mixture of ammonium nitrate (NH4NO3) and gallium nitrate (Ga(NO3)3) by electrochemical deposition (ECD) method at room temperature (RT) for the first time. The controlling parameters of current density and electrolyte molarity were found to greatly influence the properties of the grown structures. The thicknesses of the deposited structures increase with the current density since it increases the chemical reaction rates. The layers grown at low molarities of both solutions basically show grain-like layer with cracking structures and dominated by both Ga2O3 and GaON. Such cracking structures seem to diminish with the increases of molarities of one of the solutions. It is speculated that the increase of current density and ions in the solutions helps to promote the growth at the area with uneven thicknesses of graphene. When the molarity of Ga(NO3)3 is increased while keeping the molarity of NH4NO3 at the lowest value of 2.5 M, the grown structures are basically dominated by the Ga2O3 structure. On the other hand, when the molarity of NH4NO3 is increased while keeping the molarity of Ga(NO3)3 at the lowest value of 0.8 M, the GaON structure seems to dominate where their cubic and hexagonal arrangements are coexisting. It was found that when the molarities of Ga(NO3)3 are at the high level of 7.5 M, the grown structures tend to be dominated by Ga2O3 even though the molarity of NH4NO3 is made equal or higher than the molarity of Ga(NO3)3. When the grown structure is dominated by the Ga2O3 structure, the deposition process became slow or unstable, resulting to the formation of thin layer. When the molarity of Ga(NO3)3 is increased to 15 M, the nanocluster-like structures were formed instead of continuous thin film structure. This study seems to successfully provide the conditions in growing either GaON-dominated or Ga2O3-dominated structure by a simple and low-cost ECD. The next possible routes to convert the grown GaON-dominated structure to either single-crystalline GaN or Ga2O3 as well as Ga2O3-dominated structure to single-crystalline Ga2O3 structure have been discussed.
Ni-catalyzed Si-based heterostructure nanowires grown on crystal Si substrates by hot-wire chemical vapor deposition (HWCVD) were studied. The nanowires which included NiSi nanowires, NiSi/Si core-shell nanowires, and NiSi/SiC core-shell nanowires were grown by varying the filament temperature T f from 1150 to 1850 °C. At a T f of 1450 °C, the heterostructure nanowires were formed by crystalline NiSi and crystalline Si that were attributed to the core and shell of the nanowires, respectively. The morphology of the nanowires showed significant changes with the increase in the filament temperature to 1850 °C. Moreover, the effect of hydrogen heat transfer from the filament temperature demonstrated significant phase changes from NiSi to Ni2Si with increase in the filament temperature. The increased filament temperature also enhanced reactions in the gas phase thus generating more SiC clusters and consequently formed the NiSi/SiC heterostructure core-shell nanowires at T f of 1850 °C. This paper discusses the role of filament temperatures on the growth and constituted phase change of the nanowires as well as their electrical characteristics.
The dissociation of zinc ions (Zn(2+)) from vapor-phase zinc acetylacetonate, Zn(C5H7O2)2, or Zn(acac)2 and its adsorption onto graphene oxide via atomic layer deposition (ALD) were studied using a quantum mechanics approach. Density functional theory (DFT) was used to obtain an approximate solution to the Schrödinger equation. The graphene oxide cluster model was used to represent the surface of the graphene film after pre-oxidation. In this study, the geometries of reactants, transition states, and products were optimized using the B3LYB/6-31G** level of theory or higher. Furthermore, the relative energies of the various intermediates and products in the gas-phase radical mechanism were calculated at the B3LYP/6-311++G** and MP2/6-311 + G(2df,2p) levels of theory. Additionally, a molecular orbital (MO) analysis was performed for the products of the decomposition of the Zn(acac)2 complex to investigate the dissociation of Zn(2+) and the subsequent adsorption of H atoms on the C5H7O2 cluster to form acetylacetonate enol. The reaction energies were calculated, and the reaction mechanism was accordingly proposed. A simulation of infrared (IR) properties was performed using the same approach to support the proposed mechanism via a complete explanation of bond forming and breaking during each reaction step.
The use of templating method to synthesize the vanadyl 2,9,16,23-tetraphenoxy-29H,31H-phthalocyanine (VOPcPhO):[6,6]-phenyl C71 butyric acid methyl ester (PC71BM) composite nanotubes is presented here. VOPcPhO is a p-type material and PC71BM is an n-type material which acts as an electron donor and electron acceptor, respectively. Both materials have been studied due to their potential applications as solar energy converter and organic electronics. High-resolution transmission electron microscope (HRTEM) and field emission scanning electron microscope (FESEM) images have shown the replication of the porous template diameter of approximately 200 nm with a superior incorporation of both VOPcPhO and PC71BM. VOPcPhO:PC71BM composite nanotubes showed the significant properties improvement if compared over their bulk heterojunction counterpart. UV-vis spectra of composite nanotubes show a shift to a longer wavelength at the absorption peaks. Significant quenching has been attained by the photoluminescence spectra of VOPcPhO:PC71BM composite nanotubes which supports the redshift of UV-vis absorption spectra. Presumably, the photo-induced charge transfer and charge carrier dissociation can be enhanced from the VOPcPhO:PC71BM composite nanotubes rather than the bulk heterojunction.
A seed/catalyst-free growth of ZnO on graphene by thermal evaporation of Zn in the presence of O2 gas was further studied. The effects of substrate positions and graphene thicknesses on the morphological, structural, and optical properties were found to be very pronounced. By setting the substrate to be inclined at 90°, the growth of ZnO nanostructures, namely, nanoclusters and nanorods, on single-layer (SL) graphene was successfully realized at temperatures of 600°C and 800°C, respectively. For the growth on multilayer (ML) graphene at 600°C with an inclination angle of 90°, the grown structures show extremely thick and continuous cluster structures as compared to the growth with substrate's inclination angle of 45°. Moreover, the base of nanorod structures grown at 800°C with an inclination angle of 90° also become thicker as compared to 45°, even though their densities and aspect ratios were almost unchanged. Photoluminescence (PL) spectra of the grown ZnO structures were composed of the UV emission (378-386 nm) and the visible emission (517-550 nm), and the intensity ratio of the former emission (I UV) to the latter emission (I VIS) changed, depending on the temperature. The structures grown at a low temperature of 600°C show the highest value of I UV/I VIS of 16.2, which is almost two times higher than the structures grown on SL graphene, indicating fewer structural defects. The possible growth mechanism was proposed and described which considered both the nucleation and oxidation processes. From the results obtained, it can be concluded that temperature below 800°C, substrate position inclined at 90° towards the gas flow, and ML graphene seems to be preferable parameters for the growth of ZnO structures by thermal evaporation because these factors can be used to overcome the problem of graphene's oxidation that takes place during the growth.
Hydrothermal zinc oxide (ZnO) thick films were successfully grown on the chemical vapor deposition (CVD)-grown thick ZnO seed layers on a-plane sapphire substrates using the aqueous solution of zinc nitrate dehydrate (Zn(NO3)2). The use of the CVD ZnO seed layers with the flat surfaces seems to be a key technique for obtaining thick films instead of vertically aligned nanostructures as reported in many literatures. All the hydrothermal ZnO layers showed the large grains with hexagonal end facets and were highly oriented towards the c-axis direction. Photoluminescence (PL) spectra of the hydrothermal layers were composed of the ultraviolet (UV) emission (370 to 380 nm) and the visible emission (481 to 491 nm), and the intensity ratio of the former emission (I UV) to the latter emission (I VIS) changed, depending on both the molarity of the solution and temperature. It is surprising that all the Hall mobilities for the hydrothermal ZnO layers were significantly larger than those for their corresponding CVD seed films. It was also found that, for the hydrothermal films grown at 70°C to 90°C, the molarity dependences of I UV/I VIS resembled those of mobilities, implying that the mobility in the film is affected by the structural defects. The highest mobility of 166 cm(2)/Vs was achieved on the hydrothermal film with the carrier concentration of 1.65 × 10(17) cm(-3) grown from the aqueous solution of 40 mM at 70°C.
Wood-based industry is one of the main drivers of economic growth in Malaysia. Forest being the source of various lignocellulosic materials has many untapped potentials that could be exploited to produce sustainable and biodegradable nanosized material that possesses very interesting features for use in wood-based industry itself or across many different application fields. Wood-based products sector could also utilise various readily available nanomaterials to enhance the performance of existing products or to create new value added products from the forest. This review highlights recent developments in nanotechnology application in the wood-based products industry.
The enzyme-linked immunosorbent assay (ELISA) has been widely used for disease surveillance and drug screening due to its relatively higher accuracy and sensitivity. Fine-tuning the ELISA is mandatory to elevate the specific detection of biomolecules at a lower abundance. Towards this end, higher molecular capture on the polystyrene (PS) ELISA surface is crucial for efficient detection, and it could be attained by immobilizing the molecules in the correct orientation. It is highly challenging to immobilize protein molecules in a well-aligned manner on an ELISA surface due to charge variations. We employed a 3-(aminopropyl) triethoxysilane (APTES)- and glutaraldehyde (GLU)-coupled PS surface chemical strategy to demonstrate the high performance with ELISA. A potassium hydroxide treatment followed by an equal ratio of 1% APTES and GLU attachment was found to be optimal, and a longer incubation with GLU favored maximum sensitivity. p24 is a vital early secreting antigen for diagnosing human immunodeficiency virus (HIV), and it has been used for efficient detection with the above chemistry. Three different procedures were followed, and they led to the improved detection of the HIV-p24 antigen at 1 nM, which is a 30-fold higher level compared to a conventional ELISA surface. The surface chemical functionalization shown here also displays a higher specificity with human serum and HIV-TAT. The above approach with the designed surface chemistry could also be recommended for disease diagnosis on other sensing surfaces involving the interaction of the probe and the analyte in heterogeneous test samples.
Passive alkaline-direct ethanol fuel cells (alkaline-DEFCs) appear to be suitable for producing sustainable energy for portable devices. However, ethanol crossover is a major challenge for passive alkaline-DEFC systems. This study investigated the performance of a crosslinked quaternized poly (vinyl alcohol)/graphene oxide (QPVA/GO) composite membrane to reduce ethanol permeability, leading in enhancement of passive alkaline-DEFC performance. The chemical and physical structure, morphology, ethanol uptake and permeability, ion exchange capacity, water uptake, and ionic conductivity of the composite membranes were characterized and measured to evaluate their applicability in fuel cells. The transport properties of the membrane were affected by GO loading, with an optimal loading of 15 wt.% and doped with 1 M of KOH showing the lowest ethanol permeability (1.49 × 10-7 cm2 s-1 and 3.65 × 10-7 cm2 s-1 at 30 °C and 60 °C, respectively) and the highest ionic conductivity (1.74 × 10-2 S cm-1 and 6.24 × 10-2 S cm-1 at 30 °C and 60 °C, respectively). In the passive alkaline-DEFCs, the maximum power density was 9.1 mW cm-2, which is higher than commercial Nafion 117/KOH (7.68 mW cm-2) at 30 °C with a 2 M ethanol + 2 M KOH solution. For the 60 °C, the maximum power density of composite membrane achieved was 11.4 mW cm-2.
Modulated continuous wave (CW) lasers cause photothermal effect that leads to rapid optical absorption and generation of thermal waves around the irradiated nanostructures. In this work, we examined the effect of modulated CW laser irradiation on the particle fragmentation process to enhance the thermal diffusivity of nanofluids. A facile and cost-effective diode laser was applied to reduce the agglomerated size of Al2O3 nanoparticles in deionized water. The thermal wave generation, which was determined by the modulated frequency of the laser beam and the optical and thermal properties of the nanofluid, is also briefly discussed and summarized. The influence of laser irradiation time on nanoparticle sizes and their size distribution was determined by dynamic light scattering and transmission electron microscopy. The thermal diffusivity of the nanofluid was measured using the photopyroelectric method. The data obtained showed that the modulated laser irradiation caused the partial fragmentation of some agglomerated particles in the colloids, with an average diameter close to the original particle size, as indicated by a narrow distribution size. The reduction in the agglomerated size of the particles also resulted in an enhancement of the thermal diffusivity values, from 1.444 × 10-3 to 1.498 × 10-3 cm2/s in 0 to 30 min of irradiation time. This work brings new possibilities and insight into the fragmentation of agglomerated nanomaterials based on the photothermal study.