METHODOLOGY: Three sodium-fluoride(NaF) concentration(0.01%w/v,0.1%w/v and 0.5%w/v respectively)and two poly-γ-glutamic acid(PGGA)concentration(1%w/v and 2%w/v respectively)were prepared in 0.1 M acetic acid(pH4.0)and deionized distilled water.For de/re-mineralisation study, tooth samples (18 teeth varnished, leaving a 2 mm2 window on the mid-buccal surfaces) were immersed in respective acidified NaF and PGGA solutions. The Ca2+ release/uptake was monitored with ISE over 72-hr with increasing pH every 24-h from 4.0 to 6.0.These teeth were later subjected to cross-sectional microhardness to determine integrated mineral recovery of enamel on increasing pH of respective acidified solution.In order to determine mechanism of PGGA,two concentrations of PGGA in deionized-water-solutions were used for tooth samples immersion followed by overnight drying then later subjected to Fourier Transform Infra-Red(FT-IR) analysis.The FT-IR analysis was also carried out on PGGA powder.For control,the experiment was repeated using hydroxyapatite(HAp)pellets.The density of PGGA solutions(1%and2%)was also measured to determine their dynamic viscosities.
RESULTS: The ISE and microhardness testing revealed statistically significant (ρ ≤ 0.05) dissolution inhibition and remineralisation potential for tooth sample treated with acidified 2%PGGA. From the FT-IR spectra, it was observed that the profiles of the enamel and HAp surfaces treated with 1%-and 2%-PGGA solutions were similar to those of PGGA powder.It was found that the viscosity of PGGA increases with increasing concentration.
CONCLUSION: The study implies that 2% PGGA is more effective than NaF as forms a coating layer to protect from demineralisation and promote remineralisation of the tooth surface.
Materials and Methods: Biodegradable polymeric microneedle arrays were fabricated out of poly lactic-co-glycolic acid (PLGA) using the micromolding technique under aseptic conditions, and the morphology of the microneedles was characterized using light microscopy. Sodium dodecyl sulfate-polyacrylamide gel electrophoresis was used to rule out drug-polymer interactions. Standard procedures were used to analyze the prepared microneedle arrays for in vitro drug release and to perform a microneedle insertion test. Enzyme-linked immunosorbent assay was used to quantify rHuKGF.
Results: The PLGA polymer was safe for use in the fabrication of rHuKGF microneedles as there was no interaction between the drug and the polymer. The fabricated rHuKGF microneedle arrays had fully formed microneedles with a height of 600 µm and a base of 300 µm. The drug from the microneedle patch was released in vitro within 30 minutes. The strength of the microneedles in the patch was good, as they were able to reach a depth of 381±3.56 µm into parafilm without any structural change or fracture.
Conclusion: Microneedle transdermal patches were successfully prepared for rHuKGF, and their evaluation suggested excellent quality and uniformity of patch characteristics. This can have potential applications in the therapeutic arena, offering advantages in terms of reduced dosing frequency, improved patient compliance, and bioavailability.
METHOD: Dichloromethane, methanol, and water extracts of the leaves and roots of M. pumilum var. alata, M. pumilum var. pumila, and M. pumilum var. lanceolata were tested using an in vitro xanthine oxidase inhibitory assay. Bioassay-guided fractionation and isolation were carried out on the most active extract using chromatographic techniques. The structures of the isolated compounds were determined using spectroscopic techniques.
RESULTS: The most active dichloromethane extract of M. pumilum var. pumila leaves (IC50 = 161.6 μg/mL) yielded one new compound, 3,7-dihydroxy-5-methoxy-4,8-dimethyl-isocoumarin (1), and five known compounds, viz. ardisiaquinone A (2), maesanin (3), stigmasterol (4), tetracosane (5), and margaric acid (6). The new compound was found to be the most active xanthine oxidase inhibitor with an IC50 value of 0.66 ± 0.01 μg/mL, which was not significantly different (p > 0.05) from that of the positive control, allopurinol (IC50 = 0.24 ± 0.00 μg/mL).
CONCLUSION: This study suggests that the new compound 3,7-dihydroxy-5-methoxy-4,8-dimethyl-isocoumarin (1), which was isolated from the dichloromethane extract of M. pumilum var. pumila leaves, could be a potential xanthine oxidase inhibitor.