METHODS: Twelve fresh-frozen cadaveric knees were used. Five components of the quadriceps and the iliotibial band were loaded physiologically with 175N and 30N, respectively. The force required to displace the patella 10mm laterally and medially at 0°, 20°, 30°, 60° and 90° knee flexion was measured. Patellofemoral contact points at these knee flexion angles were marked. The trochlea cartilage geometry at these flexion angles was visualized by Computed Tomography imaging of the femora in air with no overlying tissue. The sulcus, medial and lateral facet angles were measured. The facet angles were measured relative to the posterior condylar datum.
RESULTS: The lateral facet slope decreased progressively with flexion from 23°±3° (mean±S.D.) at 0° to 17±5° at 90°. While the medial facet angle increased progressively from 8°±8° to 36°±9° between 0° and 90°. Patellar lateral stability varied from 96±22N at 0°, to 77±23N at 20°, then to 101±27N at 90° knee flexion. Medial stability varied from 74±20N at 0° to 170±21N at 90°. There were significant correlations between the sulcus angle and the medial facet angle with medial stability (r=0.78, p<0.0001).
CONCLUSIONS: These results provide objective evidence relating the changes of femoral profile geometry with knee flexion to patellofemoral stability.
OBJECTIVE: The aim of this study was to assess the safety and pullout strength of medial, partial nonthreaded thoracic pedicle screws compared with conventional screws.
SUMMARY OF BACKGROUND DATA: The perforation rate of the pedicle screws has been reported as high as 41%. Nerve injury and irritation can result from the compression of malpositioned screw on neural structures.
METHODS: Ten fresh cadavers were studied. Screws, 5.0 and 6.0 mm, were inserted from T1 to T6 and T7 to T12, respectively. Pedicle perforations and fractures were recorded upon screw insertion and final positioning (nonthreaded portion facing medially) after a wide laminectomy. Pullout strength of novel and conventional screws were then tested using an Instron machine in an artificial bone substitute.
RESULTS: A total of 240 thoracic pedicle screws were inserted. Of them, 88.8% (213 screws) were fully contained during screw insertion. There were 5.0% (12 screws) grade 1 medial perforations and 6.2% (15 screws) grade 1 lateral perforations during screw insertion. Upon final positioning, 93.8% (225 screws) were fully contained. All grade 1 medial perforations, which occurred during insertion, were converted to grade 0. No dural or nerve root injuries occurred. Pedicle split fractures were noted in 6.7% (16 screws). The use of medial, partial nonthreaded screws reduced the overall perforation rate from 11.2% to 6.2%. The mean pullout load for the 5 mm fully threaded screw versus medial, partial nonthreaded was 1419.3±106.1 N (1275.8-1538.8 N) and 1336.6±44.2 N (1293.0-1405.1 N) respectively, whereas 6 mm pullout load averaged 2126.0±134.8 N (1986.3-2338.3 N) and 2036.5±210.0 N (1818.4-2355.9 N). The difference was not statistically significant.
CONCLUSIONS: The use of medial, partial nonthreaded pedicle screws reduced the medial perforation rate from 5.0% to 0%; however, the pullout strength was not significantly reduced. The use of this novel screw can potentially reduce the incidence of nerve injury or irritation after medial pedicle perforations.
METHODS: Twenty-four studies met the inclusion criteria including 1761 cadaveric limbs.
RESULTS: The results were as following: (a) the mean palmaris longus tendon length was of 13.9 ± 2.6 cm, (b) the mean ratio palmaris longus tendon length/forearm length was of 0.545 ± 0.06, (c) the weighted correlation value was of 0.686, and (d) the mean palmaris longus tendon width was of 4.0 ± 1.7 mm. Only five studies reported a palmaris longus tendon length of more than 15 cm. The palmaris longus tendon length was shown to vary between ancestries; the Japanese had the shortest while Malaysian the longest palmaris longus tendons. All studies but one reported a palmaris longus tendon mean width of more than 3 mm where the minimal mean palmaris longus tendon width was of 2.5 mm.
CONCLUSION: While the requested length depends on the recipient site and/or type of reconstructive surgery, the palmaris longus tendon often met the required diameter for grafting. Our review demonstrated that while palmaris longus length varies between ancestries, its width is often adequate for grafting. In addition, the forearm length could be a good predictor of palmaris longus tendon length; such correlation could assist surgeons when planning to use palmaris longus tendon as a graft source.
QUESTION/PURPOSE: Does a controlled deep-freezing temperature during irradiation help preserve the compressive mechanical properties of human femoral cortical bone allografts?
METHODS: Cortical bone cube samples, each measuring 64 mm3, were cut from the mid-diaphyseal midshaft of five fresh-frozen cadaver femurs (four male donors, mean [range] age at procurement 42 years [42 to 43]) and were allocated via block randomization into one of three experimental groups (with equal numbers of samples from each donor allocated into each group). Each experimental group consisted of 20 bone cube samples. Samples irradiated in dry ice were subjected to irradiation doses ranging from 26.7 kGy to 27.1 kGy (mean 26.9 kGy) at a deep-freezing temperature below -40°C (the recommended long-term storage temperature for allografts). Samples irradiated in gel ice underwent irradiation doses ranging from 26.2 kGy and 26.4 kGy (mean 26.3 kGy) in a freezing temperature range between -40°C and 0°C. Acting as controls, samples in a third group were not subjected to gamma irradiation. The mechanical properties (0.2% offset yield stress, ultimate compression stress, toughness, and the Young modulus) of samples from each group were subsequently evaluated via axial compression loading to failure along the long axis of the bone. The investigators were blinded to sample group during compression testing.
RESULTS: The mean ultimate compression stress (84 ± 27 MPa versus 119 ± 31 MPa, mean difference 35 [95% CI 9 to 60]; p = 0.005) and toughness (3622 ± 1720 kJ/m3 versus 5854 ± 2900 kJ/m3, mean difference 2232 [95% CI 70 to 4394]; p = 0.009) of samples irradiated at a higher temperature range (-40°C to 0°C) were lower than in those irradiated at deep-freezing temperatures (below -40°C). The mean 0.2% offset yield stress (73 ± 28 MPa versus 109 ± 38 MPa, mean difference 36 [95% CI 11 to 60]; p = 0.002) and ultimate compression stress (84 ± 27 MPa versus 128 ± 40 MPa, mean difference 44 [95% CI 17 to 69]; p < 0.001) of samples irradiated at a higher temperature range (-40°C to 0°C) were lower than the nonirradiated control group samples. The mean 0.2% offset yield stress (73 ± 28 MPa versus 101 ± 28 MPa, mean difference 28 [95% CI 3 to 52]; p = 0.02; effect size = 1.0 [95% CI 0.8 to 1.2]) of samples irradiated at higher temperature range (-40°C to 0°C) were no different with the numbers available to those irradiated at deep-freezing temperature. The mean toughness (3622 ± 1720 kJ/m3 versus 6231 ± 3410 kJ/m3, mean difference 2609 [95% CI 447 to 4771]; p = 0.02; effect size = 1.0 [95% CI 0.8 to 1.2]) of samples irradiated at higher temperature range (-40°C to 0°C) were no different with the numbers available to the non-irradiated control group samples. The mean 0.2% offset yield stress, ultimate compression stress, and toughness of samples irradiated in deep-freezing temperatures (below -40°C) were not different with the numbers available to the non-irradiated control group samples. The Young modulus was not different with the numbers available among the three groups.
CONCLUSION: In this study, maintenance of a deep-freezing temperature below -40°C, using dry ice as a cooling agent, consistently mitigated the adverse effects of irradiation on the monotonic-compression mechanical properties of human cortical bone tissue. Preserving the mechanical properties of a cortical allograft, when irradiated in a deep-freezing temperature, may have resulted from attenuation of the deleterious, indirect effects of gamma radiation on its collagen architecture in a frozen state. Immobilization of water molecules in this state prevents radiolysis and the subsequent generation of free radicals. This hypothesis was supported by an apparent loss of the protective effect when a range of higher freezing temperatures was used during irradiation.
CLINICAL RELEVANCE: Deep-freezing temperatures below -40°C during gamma irradiation may be a promising approach to better retain the native mechanical properties of cortical bone allografts. A further study of the effect of deep-freezing during gamma radiation sterilization on sterility and other important biomechanical properties of cortical bone (such as, tensile strength, fracture toughness, and fatigue) is needed to confirm these findings.