Hydrogen plays a crucial role in the future energy landscape owing to its high energy density. However, finding an ideal storage material is the key challenge to the success of the hydrogen economy. Various solid-state hydrogen storage materials, such as metal hydrides, have been developed to realize safe, effective, and compact hydrogen storage. However, low kinetics and thermodynamic stability lead to a high working temperature and a low hydrogen sorption rate of the metal hydrides. Using scaffolds made from porous materials like silica to confine the metal hydrides is necessary for better and improved hydrogen storage. Therefore, this article reviews porous silica-based scaffolds as an ideal material for improved hydrogen storage. The outcome showed that confining the metal hydrides using scaffolds based on porous silica significantly increases their storage capacities. It was also found that the structural modifications of the silica-based scaffold into a hollow structure further improved the storage capacity and increased the affinity and confinement ability of the metal hydrides, which prevents the agglomeration of metal particles during the adsorption/desorption process. Hence, the structural modifications of the silica material into a fibrous and hollow material are recommended to be crucial for further enhancing the metal hydride storage capacity.
The optical constants of Para-Toluene sulfonic acid-doped polyaniline (PANI), PANIchitosan composites, PANI-reduced graphene-oxide composites and a ternary composite comprising of PANI, chitosan and reduced graphene-oxide dispersed in diluted p-toluene sulfonic acid (PTSA) solution and N-Methyl-2-Pyrrolidone (NMP) solvent have been evaluated and compared. The optical constant values were extracted from the absorbance spectra of thin layers of the respective samples. The potential utilization of the materials as the active sensing materials of surface plasmon resonance biosensors has also been assessed in terms of the estimated value of the penetration depth through a dielectric medium. The results show a reasonable dependence of the optical constant parameters on the solvent type. Higher real part refractive index (n) and real part complex dielectric permittivity (ε') values were observed for the samples prepared using PTSA solution, while higher optical conductivity values were observed for the NMP-based samples due to their relatively higher imaginary part refractive index (k) and imaginary part complex dielectric permittivity (ε″) values. In addition, NMP-based samples show improvement in terms of the penetration depth through a dielectric medium by around 9.5, 1.6, 4.4 and 2.9 times compared to PTSA-based samples for the PANI, PANI-chitosan, PANI-RGO and the ternary composites, respectively. Based on these, it is concluded that preparation of these materials using different dispersion solvents could produce materials of different optical properties. Thus, the variation of the dispersion solvent will allow the flexible utilization of the PANI and the composites for diverse applications.