The rapid growth of electronic systems and devices operating within the gigahertz (GHz) frequency range has increased electromagnetic interference. In order to eliminate or reduce the spurious electromagnetic radiation levels more closely in different applications, there is strong research interest in electromagnetic absorber technology. Moreover, there is still a lack of ability to absorb electromagnetic radiation in a broad frequency range using thin thickness. Thus, this study examined the effect of incorporating magnetic and dielectric materials into the polymer matrix for the processing of radar absorbing materials. The experiment evaluated the sample preparation with different weight percentages of multi-walled carbon nanotubes (MWCNT) mixed with Ni0.5Zn0.5Fe2O4 (Nickel-Zinc-Ferrite) loaded into epoxy (P) as a matrix. The prepared samples were analysed by examining the reflectivity measurements in the 8 – 18 GHz frequency range and conducting a morphological study using scanning electron microscopy analyses. The correlation of the results showed that different amounts of MWCNT influenced the performance of the microwave absorber. As the amount of MWCNTs increased, the reflection loss (RL) peak shifted towards a lower frequency range and the trend was similar for all thicknesses. The highest RL was achieved when the content of MWCNTs was 2 wt% with a thickness of 2 mm with an RL of – 14 dB at 16 GHz. The 2.5 GHz bandwidth corresponded to the RL below -10 dB (90% absorption) in the range of 14.5 – 17 GHz. This study showed that the proposed experimental route provided flexible absorbers with suitable absorption values by mixing only 2 wt% of MWCNTs.
Carbon nanotube reinforced aluminium matrix composites (Al-CNTs) have been widely used in aerospace and automotive industries where high quality and strength is required. The enhanced mechanical properties of Al-CNTs are closely related to processing technique due to challenges within production of these composite materials. In the current review, solid state processing techniques used for synthesizing Al-CNTs have been reviewed to provide an insight into the features and capabilities of each technique regarding the incorporation of CNT reinforcements. To conclude, the mechanical performance of Al-CNT composites is mainly decided by the capability of each technique in the dispersion of CNTs within the aluminum matrix.
This paper reports an alternative method for making glass-ceramic from disposal waste water
sludge and soda lime silica (SLS) glass. The glass ceramic samples were prepared from a mixture
of wastewater sludge and SLS glasses, melted at 1375°C for 3 hours and quenched by pouring into
water to obtain a coarse frit. The frit glass was then crushed and sieved to 106μm before it was
pressed to a pellet. The sintering process was performed at various temperatures between 700-
1000°C for 2 hours and morphologically characterized with XRD, SEM, and EDX. Overall results
showed the crystalline phase of diopside sodian-critobalite glass-ceramic is depending on thermal
treatment process and making them attractive to industrial uses such as in construction, tiling, and
glass-ceramic applications.