In this study, the synthesis of Fe3O4@GO@g-C3N4 ternary nanocomposite for enhanced photocatalytic degradation of phenol has been investigated. The surface modification of Fe3O4 was performed through layer-by-layer electrostatic deposition meanwhile the heterojunction structure of ternary nanocomposite was obtained through sonicated assisted hydrothermal method. The photocatalysts were characterized for their crystallinity, surface morphology, chemical functionalities, and band gap energy. The Fe3O4@GO@g-C3N4 ternary nanocomposite achieved phenol degradation of ∼97%, which was significantly higher than that of Fe3O4@GO (∼75%) and Fe3O4 (∼62%). The enhanced photoactivity was due to the efficient charge carrier separation and desired band structure. The photocatalytic performance was further enhanced with the addition of hydrogen peroxide, in which phenol degradation up to 100% was achieved in 2 h irradiation time. The findings revealed that operating parameters have significant influences on the photocatalytic activities. It was found that lower phenol concentration promoted higher activity. In this study, 0.3 g of Fe3O4@GO@g-C3N4 was found to be the optimized photocatalyst for phenol degradation. At the optimized condition, the reaction rate constant was reported as 6.96 × 10-3 min-1. The ternary photocatalyst showed excellent recyclability in three consecutive cycles, which confirmed the stability of this ternary nanocomposite for degradation applications.
Ultrafiltration grade polysulfone-based mixed matrix membranes (MMMs) incorporated with two-dimensional boron nitride nanosheet (BNNS) was prepared via phase inversion method. The amount of BN incorporated was varied and the influence on membrane morphology, contact angle, surface charge, as well as water permeability and humic acid rejection were investigated. Results revealed that the addition of BN to the membrane matrix resulted in profound increase in water permeability (almost tripled to that of neat PSf) and humic acid rejection due to the increase in pore size and surface negative charge. Beyond the morphological changes imparted by the inclusion of BNNS, we postulated that the presence of BNNS within the membrane matrix also contribute to the enhancement in flux and rejection based on surface-slip and selective interlayer transport. Despite the favourable augmentation of water transport and filtration performance, the MMMs suffered with fouling problem due to the entrapment of foulant within the enlarged pores and the membrane valleys. Its inherent adsorptive character could be a disadvantage when utilized as membrane filler.