Edible duck feet gelatin (DFG)-based biocomposites with different glycerol (GLY) contents (15%, 25%, and 35% of dried DFG) were prepared. Physicochemical, mechanical, barrier, and heat seal properties of DFG films were characterized and compared as an alternative to bovine gelatin film. Increasing glycerol from 15 to 35% decreased the TS and YM and EB and HS increased, in value of 42.54-7.27 and 1240-157.10MPa and 22.82-50.33% and 42.06-347.15N/m respectively. The water vapor permeability (WVP) and oxygen permeability (OP) of films were increased from 4.78 to 5.6×10-11gm-1Pa-1s-1 and from 3.97 to 33.99cm3mμ/m2 d kPa respectively. GAB model estimations showed monolayer water content of films increased with the increase of plasticizer content. Moisture sorption isotherm modelling exhibited a type II BET classification. Fourier transform infrared (FTIR) spectra showed shifted peak at approximately 1024cm-1, which was related to glycerol. The results show that the properties of DFG film are suitable for use as an alternative material to bovine gelatin film.
The objective of this study was to compare the morphological and chemical composition of bone graft (BG) and coral graft (CG) as well as their osteogenic differentiation potential using rabbit mesenchymal stem cells (rMSCs) in vitro. SEM analysis of BG and CG revealed that the pores in these grafts were interconnected, and their micro-CT confirmed pore sizes in the range of 107-315 µm and 103-514 µm with a total porosity of 92% and 94%, respectively. EDS analysis indicated that the level of calcium in CG was relatively higher than that in BG. FTIR of BG and CG confirmed the presence of functional groups corresponding to carbonyl, aromatic, alkyl, and alkane groups. XRD results revealed that the phase content of the inorganic layer comprised highly crystalline form of calcium carbonate and carbon. Atomic force microscopy analysis showed CG had better surface roughness compared to BG. In addition, significantly higher levels of osteogenic differentiation markers, namely, alkaline phosphatase (ALP), Osteocalcin (OC) levels, and Osteonectin and Runx2, Integrin gene expression were detected in the CG cultures, when compared with those in the BG cultures. In conclusion, our results demonstrate that the osteogenic differentiation of rMSCs is relatively superior in coral graft than in bone graft culture system.