AIM: To introduce modifications of the stamp technique that make it applicable to restore Class II composite restorations.
MATERIALS AND METHODS: The traditional materials and tools used for direct composite restorations are needed with no additional instruments. Clinical illustrations and step-by-step description are provided in this paper.
RESULTS AND CONCLUSION: Using the stamp technique to restore Class II cavities is achievable, simple and practical, and result in a very accurate anatomical restoration.
Materials and Methods: A total of 40 extracted human maxillary anterior teeth were selected, disinfected, and decoronated to obtain a standardized length of 10 mm. The teeth were prepared with Protaper universal rotary files until size F4 using 2.5% NaOCl as an irrigant during instrumentation. The teeth were then randomly divided into four groups of 10 samples each based on the irrigating solutions used during final wash sequence as follows: Group A - (2.5% NaOCl and 2% CHX), Group B - (2.5% NaOCl followed by 70% Isopropyl Alcohol and 2% CHX), Group C - (2.5% NaOCl followed by 6.25% sodium metabisulfite and 2% CHX), and Group D - (2.5% NaOCl followed by 3.86% sodium Thiosulfate and 2% CHX). The roots were sectioned longitudinally and the canal surface was evaluated under dental operating microscope (×16) for the presence of orange-brown precipitate. The results were tabulated as per scoring criteria and statistically analyzed.
Statistical Analysis Used: One-way ANOVA test and post hoc Tukey's test.
Results: The lowest mean score was observed in Group C, followed by Group D and Group B, respectively. In comparison, there was a statistically significant (P < 0.001) difference in results between Group C and the other experimental groups. However, there was no statistically significant difference between Group B and Group D.
Conclusion: Sodium metabisulfite was found to be very effective in preventing the formation of orange-brown precipitate.
AIM: The study aimed to evaluate the effect of placement of compactable glass fibers in reinforcing the endodontically treated teeth in a novel conservative manner.
SETTINGS AND DESIGN: Research laboratory, in vitro study.
MATERIALS AND METHODS: Seventy-five extracted maxillary premolars were procured. Fifteen teeth were left untreated (Group A) and the remaining teeth were endodontically treated followed by standardized mesio-occluso-distal preparation and randomly assigned to experimental groups (n = 15) as follows: (B) no restoration, (C) restoration with composite, (D) EverStick® POST followed by composite, and (E) vertical glass fibers within 3 mm of the coronal root canal space and buccopalatal flaring of the coronal fibers followed by composite. After conditioning and thermocycling, specimens were loaded under a universal testing machine to evaluate fracture resistance and fracture pattern of specimens.
STATISTICAL ANALYSIS USED: Obtained scores were statistically analyzed using one-way analysis of variance test for stress analysis, post hoc Tukey's test for intergroup comparison, and Chi-square test for analysis of favorable and unfavorable fracture.
RESULTS: The fracture resistance was highest to lowest as follows: Group A > E > C > D > B (P < 0.001).
CONCLUSION: EverStick®POST used in conservative manner improved fracture strength of teeth significantly.
Materials and Methods: A maxillary first premolar typodont tooth was prepared to receive lithium disilicate onlay. Mesio-occluso-distal cavity was prepared with palatal cusp reduction and collar preparation. In the proximal box, gingival seat was placed 1 mm coronal to the cementoenamel junction and mesiodistal width of the seat was kept to 1 mm. Thirty stone models were prepared from thirty rubber base impressions and divided into two groups, based on the technique of fabrication of onlays: (1) Group CL (CAD/CAM lithium disilicate) and (2) Group PL (Pressable lithium disilicate). Fifteen onlays per each group were fabricated by following the manufacturer instructions. Marginal fit of all the samples were analyzed by using stereomicroscope with Image Analysis software. Statistical analysis was done by t-test.
Results: Statistical significant difference was found between both the groups. The lowest marginal discrepancy (41.46 μm) was measured for Group CL (CAD/CAM lithium disilicate) specimens, and the highest (55.95 μm) discrepancy was observed on the Group PL (Pressable lithium disilicate) specimens.
Conclusion: Although there was a statistically significant difference between the two groups, marginal gap of both the groups were in clinically acceptable levels.
Objective: The objective of this study is to determine the antimicrobial effects of MP, AV, and MP + AV in comparison with Ca(OH)2 against E. faecalis, as an intracanal medicament.
Materials and Methods: Antimicrobial activity of MP, AV, MP + AV, Ca(OH)2, and dimethyl sulfoxide was tested against E. faecalis using antimicrobial sensitivity testing, minimum inhibitory concentration (MIC), and minimum bactericidal concentration (MBC). The results were analyzed by Kruskal-Wallis test with Mann-Whitney post hoc test and repeated measures analysis of variance with Bonferroni post hoc test (P < 0.05).
Results: For agar well-diffusion method, MP + AV gave maximum inhibition zone diameter (mean: 8.11 ± 0.015 mm), MP (mean: 6.21 ± 0.046 mm, Ca(OH)2 (mean: 5.5 ± 0.006), and AV (mean: 5.05 ± 0.012) with P < 0.05. MIC for MP + AV was 2 mg/ml, MP at 8 mg/ml, Ca(OH)2 at 8 mg/ml, and AV at 16 mg/ml. The MBC for MP + AV is at 4 mg/ml, MP at 16 mg/ml, Ca(OH)2 at 16 mg/ml, and AV at 32 mg/ml.
Conclusion: The combination of MP and AV consistently showed better antimicrobial activity compared to MP and AV alone against E. faecalis. The findings suggest that MP and AV used in combination may be an ideal intracanal medicament in FET and PET.
Materials and Methods: An audit at the department of endodontics at dental specialty centre kingdom of Saudi Arabia was carried out. The audit was conducted by developing endodontics treatment and success predictors based on evidence, that can be measured for endodontic care. A total of 12 months' data was examined from the previous dental records. Ten clinical cards were which included root canal treatment were selected. The audit was carried out for a minimum of 50 teeth and a maximum of 200 teeth. The radiographs of record cards were studied and a single dentist completed the audit tool.
Results: The vitality test was performed in 1.98% cases, intra-canal medicament was used and named in 3.96% cases, 3.96% the teeth were extracted due to endodontic failure. Further, in 6.93% of the cases that were identified had certain spaces but overall root canal filling was evaluated as satisfactory.
Conclusion: The vitality test, type of intracanal medicament, and assessment of root canal filling were not done, but there was an overall performance of predictors for endodontic treatment.
Objectives: The aim of this study is to evaluate the efficacy of dentin bonding agent (DBA) in preventing coronal discoloration caused by four different root canal sealers- MTA Fillapex, Sealapex, Zical and Z. O. B seal at different time intervals by measuring chromatic alterations using digital images analysis method.
Methodology: Ninety mandibular premolars were collected and sectioned at 1 mm below the cementoenamel junction. Standard access cavity preparations of dimensions (depth-3 mm, width-0.8 mm, and length-3 mm) were prepared with a No. 245 bur through the cervical access. Following the standard irrigation protocol, specimens were then randomly divided into nine groups (four groups without DBA [1-4] +4 groups with DBA [5-8] +1 negative control [9]). In Groups 1-4, four different root canal sealers (MTA Fillapex, Sealapex, Zical, and Z.O.B seal) were applied to the walls of the pulp chamber. For Groups 5-8, the samples were etched with 37% phosphoric acid and DBA application was done before the respective root canal sealer application. The cervical access in all specimens was sealed using glass ionomer cement. Digital photographs were taken under standard lighting and environmental conditions at different time intervals: preprocedural, postprocedural, and after 1, 2, 3, and 4 months. These images were analyzed using Adobe Photoshop CS6 from which laboratory values and subsequently Delta E values were obtained.
Results: Statistical analysis performed using repeated measures ANOVA and post hoc Tukey's tests show that the groups with DBA application had significantly lower mean Delta E values (P < 0.05) compared to the groups without DBA application.
Conclusion: DBAs applied to the dentinal walls of the pulp chamber before obturation can effectively reduce the sealer-induced coronal discoloration.
Materials and Methods: The prepared root canals of 80 teeth were contaminated with E. faecalis (n = 40) and S. epidermidis (n = 40) for 21 days to create biofilms. The samples in each group were allocated randomly into the following four subgroups (n = 10) according to the decontamination protocol: Group 1: 1% Pediocin, Group 2: 2% CHX, Group 3: Ca(OH)2, and Group 4: saline (negative control). At 5 days, the antimicrobial efficacy of the medicaments against E. faecalis and S. epidermidis was assessed by collecting dentin shavings from the canal walls created using Gates Glidden drill sizes 4 and 5, corresponding to a depth into the root canal walls of 200 μm and 400 μm, respectively. The total number of colony-forming units (CFUs) was counted. The Wilcoxon signed-rank test was used to compare the difference in CFUs between the two depths (P > 0.05).
Results: There was no bacterial growth in samples treated with pediocin, CHX, or Ca(OH)2 at either depth.
Conclusion: In this laboratory experimental model, pediocin exhibited the same antimicrobial properties against E. faecalis and S. epidermidis as CHX and Ca(OH)2.