AIM: To introduce modifications of the stamp technique that make it applicable to restore Class II composite restorations.
MATERIALS AND METHODS: The traditional materials and tools used for direct composite restorations are needed with no additional instruments. Clinical illustrations and step-by-step description are provided in this paper.
RESULTS AND CONCLUSION: Using the stamp technique to restore Class II cavities is achievable, simple and practical, and result in a very accurate anatomical restoration.
Materials and Methods: A maxillary first premolar typodont tooth was prepared to receive lithium disilicate onlay. Mesio-occluso-distal cavity was prepared with palatal cusp reduction and collar preparation. In the proximal box, gingival seat was placed 1 mm coronal to the cementoenamel junction and mesiodistal width of the seat was kept to 1 mm. Thirty stone models were prepared from thirty rubber base impressions and divided into two groups, based on the technique of fabrication of onlays: (1) Group CL (CAD/CAM lithium disilicate) and (2) Group PL (Pressable lithium disilicate). Fifteen onlays per each group were fabricated by following the manufacturer instructions. Marginal fit of all the samples were analyzed by using stereomicroscope with Image Analysis software. Statistical analysis was done by t-test.
Results: Statistical significant difference was found between both the groups. The lowest marginal discrepancy (41.46 μm) was measured for Group CL (CAD/CAM lithium disilicate) specimens, and the highest (55.95 μm) discrepancy was observed on the Group PL (Pressable lithium disilicate) specimens.
Conclusion: Although there was a statistically significant difference between the two groups, marginal gap of both the groups were in clinically acceptable levels.
Objectives: The aim of this study is to evaluate the efficacy of dentin bonding agent (DBA) in preventing coronal discoloration caused by four different root canal sealers- MTA Fillapex, Sealapex, Zical and Z. O. B seal at different time intervals by measuring chromatic alterations using digital images analysis method.
Methodology: Ninety mandibular premolars were collected and sectioned at 1 mm below the cementoenamel junction. Standard access cavity preparations of dimensions (depth-3 mm, width-0.8 mm, and length-3 mm) were prepared with a No. 245 bur through the cervical access. Following the standard irrigation protocol, specimens were then randomly divided into nine groups (four groups without DBA [1-4] +4 groups with DBA [5-8] +1 negative control [9]). In Groups 1-4, four different root canal sealers (MTA Fillapex, Sealapex, Zical, and Z.O.B seal) were applied to the walls of the pulp chamber. For Groups 5-8, the samples were etched with 37% phosphoric acid and DBA application was done before the respective root canal sealer application. The cervical access in all specimens was sealed using glass ionomer cement. Digital photographs were taken under standard lighting and environmental conditions at different time intervals: preprocedural, postprocedural, and after 1, 2, 3, and 4 months. These images were analyzed using Adobe Photoshop CS6 from which laboratory values and subsequently Delta E values were obtained.
Results: Statistical analysis performed using repeated measures ANOVA and post hoc Tukey's tests show that the groups with DBA application had significantly lower mean Delta E values (P < 0.05) compared to the groups without DBA application.
Conclusion: DBAs applied to the dentinal walls of the pulp chamber before obturation can effectively reduce the sealer-induced coronal discoloration.
AIM: The present work aims to gain knowledge about dentists' opinions and experiences on assessing the risk factor related to the development of root caries and to help identify any overlooked factors that may contribute to less efficacious clinical outcomes.
METHODOLOGY: A questionnaire related to root surface caries was distributed among practicing dentists in nine different countries, namely the United Kingdom, Libya, Jordan, Saudi Arabia, Egypt, Brazil, India, Malaysia, and Iraq. Questionnaire responses were analyzed, and the results were compared among the groups.
RESULTS: Dentists around the world ranked the oral hygiene status of patients as the most important factor in the development of root surface caries. Patients with poor oral hygiene, active periodontal disease, reduced salivary flow, and gingival recession are perceived to have a higher risk of developing new root surface caries. There is a greater focus on prevention in the UK and greater levels of untreated dental disease in other countries, especially those recovering from civil wars.
CONCLUSION: This work identified some overlooked factors that may have contributed to the less efficacious clinical outcomes reported in the literature. It is hoped that this deep dive into risk factors coupled with the findings presented in Part I of this study will be used as a basis for a more comprehensive investigation into the management of patients with root surface caries.
Materials and Methods: An audit at the department of endodontics at dental specialty centre kingdom of Saudi Arabia was carried out. The audit was conducted by developing endodontics treatment and success predictors based on evidence, that can be measured for endodontic care. A total of 12 months' data was examined from the previous dental records. Ten clinical cards were which included root canal treatment were selected. The audit was carried out for a minimum of 50 teeth and a maximum of 200 teeth. The radiographs of record cards were studied and a single dentist completed the audit tool.
Results: The vitality test was performed in 1.98% cases, intra-canal medicament was used and named in 3.96% cases, 3.96% the teeth were extracted due to endodontic failure. Further, in 6.93% of the cases that were identified had certain spaces but overall root canal filling was evaluated as satisfactory.
Conclusion: The vitality test, type of intracanal medicament, and assessment of root canal filling were not done, but there was an overall performance of predictors for endodontic treatment.
Materials and Methods: Twenty-five enamel slabs were divided into three treatment groups: light-activated bleaching, laser-activated bleaching, and control. The baseline data were recorded for enamel microhardness (Vickers microhardness [VMH]) and surface roughness (Roughness average, Ra). The specimens were cured for 10 min upon hydrogen peroxide application for the light-activated bleaching group and activated with a laser source, 8 cycles, 10 s per cycle for the laser-activated group. The changes in VMH and Ra at days 1, 7, and 28 were evaluated. Kruskal-Wallis, Friedman, Wilcoxon, and Mann-Whitney tests were used to analyze both VMH and Ra between the treatment groups at different time intervals.
Results: There were a significant reduction in VMH values and significant differences between days 1, 7, and 28 against the baseline in the light-activated bleaching group (P = 0.001). The Ra values revealed significant differences in both light- (P = 0.001) and laser-activated (P = 0.033) groups.
Conclusion: Light activation of a bleaching agent caused a reduction in enamel microhardness and an increase in surface roughness when compared to laser activation.
Objective: The objective of this study is to determine the antimicrobial effects of MP, AV, and MP + AV in comparison with Ca(OH)2 against E. faecalis, as an intracanal medicament.
Materials and Methods: Antimicrobial activity of MP, AV, MP + AV, Ca(OH)2, and dimethyl sulfoxide was tested against E. faecalis using antimicrobial sensitivity testing, minimum inhibitory concentration (MIC), and minimum bactericidal concentration (MBC). The results were analyzed by Kruskal-Wallis test with Mann-Whitney post hoc test and repeated measures analysis of variance with Bonferroni post hoc test (P < 0.05).
Results: For agar well-diffusion method, MP + AV gave maximum inhibition zone diameter (mean: 8.11 ± 0.015 mm), MP (mean: 6.21 ± 0.046 mm, Ca(OH)2 (mean: 5.5 ± 0.006), and AV (mean: 5.05 ± 0.012) with P < 0.05. MIC for MP + AV was 2 mg/ml, MP at 8 mg/ml, Ca(OH)2 at 8 mg/ml, and AV at 16 mg/ml. The MBC for MP + AV is at 4 mg/ml, MP at 16 mg/ml, Ca(OH)2 at 16 mg/ml, and AV at 32 mg/ml.
Conclusion: The combination of MP and AV consistently showed better antimicrobial activity compared to MP and AV alone against E. faecalis. The findings suggest that MP and AV used in combination may be an ideal intracanal medicament in FET and PET.
Materials and Methods: A total of 40 extracted human maxillary anterior teeth were selected, disinfected, and decoronated to obtain a standardized length of 10 mm. The teeth were prepared with Protaper universal rotary files until size F4 using 2.5% NaOCl as an irrigant during instrumentation. The teeth were then randomly divided into four groups of 10 samples each based on the irrigating solutions used during final wash sequence as follows: Group A - (2.5% NaOCl and 2% CHX), Group B - (2.5% NaOCl followed by 70% Isopropyl Alcohol and 2% CHX), Group C - (2.5% NaOCl followed by 6.25% sodium metabisulfite and 2% CHX), and Group D - (2.5% NaOCl followed by 3.86% sodium Thiosulfate and 2% CHX). The roots were sectioned longitudinally and the canal surface was evaluated under dental operating microscope (×16) for the presence of orange-brown precipitate. The results were tabulated as per scoring criteria and statistically analyzed.
Statistical Analysis Used: One-way ANOVA test and post hoc Tukey's test.
Results: The lowest mean score was observed in Group C, followed by Group D and Group B, respectively. In comparison, there was a statistically significant (P < 0.001) difference in results between Group C and the other experimental groups. However, there was no statistically significant difference between Group B and Group D.
Conclusion: Sodium metabisulfite was found to be very effective in preventing the formation of orange-brown precipitate.