Aluminium substituted cobalt-copper Co1-xCuxFe2-xAlxO₄, (x ═ 0.8) nanoparticles are grown and sintered at different temperature in the range 600 to 900 °C. XRD analysis on nanoparticles prepared at sintered temperatures of 700 °C and 800 °C confirms the spinel structure and presence of hematite phase (alpha ferrite) in them. The dielectric behaviour of the prepared nano-particles is investigated. Although crystallinity improved with increase in sintering temperature and there was a dielectric loss at higher probe analyser frequency. The synthesized nanoparticles an average particle size of 20-24 nm while the FTIR absorption in regions of 586-595 cm-1 and 450-460 cm-1 indicated the presence of intrinsic vibrations of the tetrahedral and octahedral complexes respectively. Electrical resistivity as a function of temperature confirms the semiconducting nature of the Cu-Al substituted cobalt ferrite, and is attributed to the hopping mechanism between Fe2+ Fe3+ ions and Co2+ Cu2+, Co2+ Al3+. The lower values of dielectric constants and dielectric losses make Al-Cu doped cobalt ferrite, a potential material for microwave and radio wave absorber applications.
Herein, we report the effect of synthesis temperature on the morphologies, optical and electronic properties of magnesium oxide (MgO) nanostructures. The MgO nanostructures were synthesized at different temperatures, i.e., 100 °C, 300 °C, and 600 °C by simple chemical reaction process and their morphology, particle size, optical, and electrical properties were examined by different techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy and UV-Vis. spectroscopy. The morphological investigations revealed that various morphologies of MgO nanostructures, i.e., nanoparticles, nanosheet networks, and nanoneedles were synthesized at 100 °C, 300 °C, and 600 °C. The XRD results confirmed that with increasing the synthesis temperature, the crystallinity of the synthesized nanostructures increases. Further, the dielectric properties and AC conductivity at various frequencies for MgO nanostructures were studied which revealed that the dielectric losses decrease with increase in frequency and temperature. In addition, the observed band gap decreases from 4.89 eV to 4.438 eV (100 °C to 600 °C) representing its increase in the conductivity.
This paper presents the temperature characteristics of silicon nanowire transistors (SiNWTs) and examines the effect of temperature on transfer characteristics, threshold voltage, I(ON)/I(OFF) ratio, drain-induced barrier lowering (DIBL), and sub-threshold swing (SS). The (MuGFET) simulation tool was used to investigate the temperature characteristics of a transistor. The findings reveal the negative effect of higher working temperature on the use of SiNWTs in electronic circuits, such as digital circuits and amplifiers circuits, because of the lower I(ON)/I(OFF) ratio, higher DIBL, and higher SS at higher temperature. Moreover, the ON state is the optimum condition for using a transistor as a temperature nano-sensor.
Transparent nanostructured ZnO thin films were successfully deposited using sol-gel spin coating method on a quartz substrate. The 0.4 M ZnO solution gel was prepared using zinc acetate dihydrate (Zn(CH3COO)22H2O) as the precursor, 2-methoxyethanol as the solvent and monoethanolamine (MEA) as the stabilizer. The electrical and optical properties dependencies on the annealing temperature of the nanostructured ZnO thin films were investigated. It was found that as the annealing temperature increased, the particle size, conductivity and the peak of the UV emission also increased.
Silver-reduced graphene oxide (Ag-rGO) nanohybrid was synthesized by applying a slight modification to the Turkevich method using trisodium citrate as a reducing and stabilizing agent to catalyze the non-enzymatic electrochemical detection of hydrogen peroxide (H₂O₂). Spherical silver nanoparticles (AgNPs) with an average particle size of 2.2 nm surfaced on reduced graphene oxide (rGO) sheets. Cyclic voltammograms (CV) obtained from glassy carbon (GC) electrode coated with Ag-rGO nanohybrid (4 mM) exhibited a peak at an overpotential of -0.52 V, with a larger faradaic current for the reduction of H₂O₂. Using the modified electrode for the linear sweep voltammetry (LSV) detection of H₂O₂, the detection limit and sensitivity were determined to be 4.8 μM (S/N ═ 3) and 0.0262 μA μM-1, respectively. The sensor appeared selective and stable towards H₂O₂ in the presence of possible interference, and it also demonstrated good recoveries of H₂O₂ concentration in real water samples.
Magnetic nanoparticles in the hollow region of carbon nanotubes have attraction due to their changing physical electrical and magnetic properties. Nickel zinc ferrite plays an important role in many applications due to its superior magnetic properties. Ni0.8Zn0.2Fe2O4 single crystals were encapsulated in multiwall carbon nanotubes (MWCNTs). The magnetic nano crystals were prepared using a sol-gel self combustion method at the sintering temperature of 750 degrees C and were characterized by XRD, FESEM, TEM and VSM. Initial permeability, Q-factor and relative loss factor were measured by impedance vector network analyzer. XRD patterns were used for the phase identification. FESEM images show morphology and dimensions of the grains of Ni0.8Zn0.2Fe2O4 single crystals and Ni0.8Zn0.2Fe2O4 single crystals in MWCNTs. TEM images were used to investigate single crystal and encapsulation of Ni0.8Zn0.2Fe2O4 single crystals in the MWCNTs. VSM results confirmed super paramagnetic behaviour of encapsulated Ni0.8Zn0.2Fe2O4 single crystals. It was also attributed that encapsulated Ni0.8Zn0.2Fe2O4 single crystals in MWCNTs showed a higher initial permeability (51.608), Q-factor (67.069), and low loss factor (0.0002) as compared to Ni0.8Zn0.2Fe2O4 single crystals. The new encapsulated Ni0.8Zn0.2Fe2O4 single crystals in the MWCNTs may have potential applications in electronic and medical industries.
Undoped and Mn2+ doped CoAl2O4 (MnxCo1-xAl2O4; x = 0.0 to 1.0) spinel nanoparticles were successfully synthesized by a microwave heating method using glycine as the fuel. X-ray powder diffraction (XRD) was confirmed the cubic spinel structure. The average crystallite size of the samples was found to be in the range of 16.46 nm to 20.25 nm calculated by Scherrer's formula. The nano-sized particle-like morphology of the samples was confirmed by high resolution scanning electron microscopy (HR-SEM) and transmission electron microscopy (HR-TEM) analysis. Energy dispersive X-ray (EDX) results showed the pure form of spinel aluminate structure. The band gap energy (Eg) of pure CoAl2O4 was estimated to be 3.68 eV from UV-Visible diffuse reflectance spectroscopy (DRS), and the Eg values increased with increase of Mn2+ ions, due to the smaller grain size. The magnetic hysteresis (M-H) loop showed the superparamagnetic nature, and the magnetization and coercivity values increased with increasing Mn2+ ions, which was confirmed by vibrating sample magnetometer (VSM). All compositions of the nano-catalysts were tested as catalyst successfully for the conversion of benzyl alcohol into benzaldehyde and observed good catalytic activity.
Graphene oxide/Cuprous oxide (GO/Cu₂O) composite is a visible light photocatalyst for the degradation of dyes. A simple and efficient approach for preparing GO/Cu₂O composite adopted in this study involves reducing cuprous oxide precursors in the presence of graphene oxide using an aqueous solution of pulp derived from banana fruit. The GO/Cu₂O composite was characterized by Fourier transform infrared spectroscopy (FT-IR), Diffused reflectance Ultraviolet visible spectroscopy (DRS UV-Vis), Raman spectroscopy and Field Emission Scanning electron microscopy (FE-SEM). Cu₂O particles were distributed randomly on the graphene oxide sheets due to the template effect of GO. The results showed higher photocatalytic activity for the composite (band gap 2.13 eV), for the degradation of the organic dyes (Methylene blue and Rhodamine-B). The enhanced photocatalytic activity is due to effective charge transfer from GO to Cu₂O, and high specific surface area which improves the effective separation of the generated electron-hole pairs. Our present study is inspired by a facile, low cost, green production of (GO/Cu₂O) composite whose photocatalytic activity can be extended to degradation of all other water-born textile dyes.
Photocatalysts provide excellent potential for the full removal of organic chemical pollutants as an environmentally friendly technology. It has been noted that under UV-visible light irradiation, nanostructured semiconductor metal oxides photocatalysts can degrade different organic pollutants. The Sn6SiO8/rGO nanocomposite was synthesized by a hydrothermal method. The Sn6SiO8 nanoparticles hexagonal phase was confirmed by XRD and functional groups were analyzed by FT-IR spectroscopy. The bandgap of Sn6SiO8 nanoparticles (NPs) and Sn6SiO8/GO composites were found to be 2.7 eV and 2.5 eV, respectively. SEM images of samples showed that the flakes like morphology. This Sn6SiO8/rGO nanocomposite was testing for photocatalytic dye degradation of MG under visible light illumination and excellent response for the catalysts. The enhancement of photocatalytic performance was mainly attributed to the increased light absorption, charge separation efficiency and specific surface area, proved by UV-vis DRS. Further, the radical trapping experiments revealed that holes (h+) and superoxide radicals (·O-₂) were the main active species for the degradation of MG, and a possible photocatalytic mechanism was discussed.
Biosynthesis of nanoparticles has now become a novel trend in addressing some of the environmental issues by adopting eco-friendly approaches in manoeuvring nanoparticles for various applications. Plants and micro-organisms have been the potential sources of the biological mode of synthesizing nanoparticles as part of their bioremediation process. This principle has been harnessed for synthesizing nanoparticles either extra or intracellularly. In this line of phyto-mediated synthesis, eucalyptus buds have been used for synthesizing gold nanoparticles (Au NPs) under optimized laboratory conditions. The UV-visible spectrum of the Au NPs showed typical surface plasmon resonance at 550 nm (λmax) with a crystalline phase measuring <100 nm in size and monodispersed as revealed from XRD, FESEM, and AFM analyses. The biological role of phytochemical concoction in reducing and stabilizing the Au NPs was clearly identified from FT-IR studies. The antimicrobial effect of the Au NPs against clinically important pathogens viz. Staphylococcus sp., Pseudomonas sp., Bacillus sp. and E. coli determined using the disk diffusion method showed no significant antibacterial effect at all concentrations. Cytotoxicity studies were carried using Vero and HEp-2 cell lines and the 50% inhibition concentration (IC50) was determined to be 1.25 mg and 0.625 mg/mL respectively. Au NPs with potential antimicrobial and anti-proliferative effects could found profound implications in the field of nanomedicine once the toxicity in vivo has been investigated.
Herein, we report the synthesis of SnO, Cu₂O and SnO-Cu₂O mixed oxide thin films on fluorinedoped tin oxide (FTO) substrate by Aerosol-Assisted Chemical Vapour Deposition (AACVD) process using [Cu (dmae)₂(H₂O)] and [Sn (dmae) (OAc)]₂ as molecular precursors for SnO and Cu₂O, respectively at 400 °C. The X-ray diffraction (XRD) pattern can be ascribed to the tetragonal phase of SnO crystals with space group P4 and cubic phase of Cu₂O crystals with space group Pn- 3m/nmm, respectively. The surface morphology characteristics of SnO, Cu₂O and SnO-Cu₂Omixed oxide have been investigated using Field Emission Scanning Electron Microscope (FESEM) which revealed that the SnO was grown homogeneously in cubical shape while Cu₂O possess nano balls shaped morphologies. The UV band gap values of SnO-Cu₂O mixed oxide thin film was found to be 2.6 eV appropriate for photoelectrochemical (PEC) applications. The synthesized material was proposed for PEC applications and has shown enhanced catalytic performance in the presence of light.
The fabrication of TiO2 nanotubes (TNT) was carried out by electrochemical anodization of Ti in aqueous electrolyte containing NH4F. The effect of electrolyte pH, applied voltage, fluoride concentration and anodization duration on the formation of TNT was investigated. It was observed that self-organized TNT can be formed by adjusting the electrolyte to pH 2-4 whereby applied voltage of 10-20 V can be performed to produce highly ordered, well-organized TNT. At 20 V, TNT can be fabricated in the concentration range of 0.07 M to 0.20 M NH4F. Higher fluoride concentration leads to etching of Ti surface and reveals the Ti grain boundaries. The prepared TNT films also show an increase in depth and in size with time and the growth of TNT films reach a steady state after 120 minutes. The morphology and geometrical aspect of the TNT would be an important factor influencing the photoelectrochemical response, with higher photocurrent response is generally associated with thicker layer of TNT. Consequently, one can tailor the resulting TNT to desired surface morphologies by simply manipulating the electrochemical parameters for wide applications such as solar energy conversion and photoelectrocatalysis.
Novel decoration of high aspect ratio zinc oxide nanowires (ZnO NWs) with noble metals such as Ag and Au nanoparticles (NPs) was demonstrated in this work. A facile method of chemical deposition with good controllability, as well as good homogeneity would be a huge advantage towards large scale fabrication. The highlight of this work is the feasibility of multiple component decoration such as a hybrid (co-exist) Ag-Au NPs decorated ZnO NWs formation that could be beneficial towards the development of nanoarchitectured materials with the most desired properties. The local surface plasmon effect (LSPR) of Ag and Au NPs were confirmed using extinction spectra and significant photoelectrochemical conversion efficiency (PCE) enhancement of dye-sensitized solar cells (DSSCs) was achieved. The Ag-NPs and hybrid Ag-Au NPs decorated ZnO NWs marked an impressive 125 and 240% efficiency improvement against pure ZnO NWs. The improved dye light extinction resulted from the LSPR effect that had enabled greater electron generation leading to improved PCE. As the complex design of oxides' nanoarchitectures have reached a point of saturation, this novel method would enable further enhancement in their photoelectrochemical properties through decoration with noble metals via a simple chemical deposition route.
The development of electrical biosensor towards device miniaturization in order to achieve better sensitivity with enhanced electrical signal has certain limitations especially complexity in fabrication process and costs. In this paper, an alternative technique with minor modification in the device structure is presented for signal amplification by implementing ambipolar conduction in the biosensor itself. We demonstrated the field-effect transistor (FET)-based biosensor coupled back-gate for attaining a higher sensitivity with the detection of lower target abundance. To utilize the coupled back-gate as a pre-amplifier, silicon-on-insulator wafer with thicknesses of top-silicon and buried oxide (BOX) layers of 70 nm and 145 nm, respectively were desired. Titanium dioxide (TiO2) nanomaterial was deposited using sol-gel method on the channel which acts as a transducer. Surface functionalization on TiO2 thin film allowed an effective immobilization of anti-cardiac troponin I antibody to interact cardiac troponin I (cTnI). Binding events at each step was validated by X-ray photoelectron spectroscopy (XPS) analysis. Further, electrical characterization (Id-Vd) confirms the potentiality of FET-based biosensor to detect cTnI (represents acute myocardial infarction disease) with the concentration ranges from 10 μg/ml down to 1 fg/ml. The sensitivity of 459.2 nA (g/ml)-1 and lower detection limit of 1 fg/ml were achieved at Vbg = -5 V and Vd = 5 V. The designed device demonstrates its ability to detect lower level of cTnI with pre-amplified electrical signal by back-gate biasing.
We found that the gold nanoparticles with high-density and crystalline-shape, such as nanocubes, nanobricks, pentahedral nanorods, etc., can be realized on the surface by using a seed-mediated growth method with a unique seeding process, namely alcohothermal. By using a conventional growth solution that contains HAuCl4, cetyltrimethylammonium bromide, NaOH and ascorbic acid, gold nanoparticles with crystalline-morphology (gold nanocrystals) of yield up to ca. 95%, can be prepared. An alcohothermal seeding was carried out by a thermal reduction of gold ions from an alcoholic solution of gold salt on the surface through an annealing process at a moderate temperature, namely 250 degrees C. It is believed that the unique initial characteristic (presumably the structures) of the gold nanoseeds particles as the result of peculiar nanoseeds formation process, prepared using this approach, instead of a simple thermal restructuring of the as prepared nanoseeds as confirmed by the results of annealing treatment on the nanoseed prepared using the normal and in-situ reduction seeding, was as the driving factor for the projected growth of crystalline-shape gold nanoparticles on the surface. The crystalline-shape gold nanoparticles modified-surface should find a potential application in catalysis, sensors and SERS.
A newly synthesized free fatty acids from waste palm oil functionalized magnetic nanoparticles immobilized on the surface of graphene oxide (FFA@MNP-GO) was successfully synthesized and characterized in this research. The combinations of long alkyl chain of free fatty acid with graphene oxide that consists of large delocalized 77-electron systems and abundant of hydrophilic groups with hydroxyl, epoxide and carboxylic groups offer the determination of simultaneous wide range of polarities of organic pollutants in real matrices through hydrogen bonding, hydrophobic and 77-77 interactions. The fabricated adsorbent was successfully applied as a magnetic solid phase extraction (MSPE) adsorbent for the simultaneous separation of selected phthalate esters (PAEs) and polycyclic aromatic hydrocarbons (PAHs) in apple and cabbage extracts prior to their high performance liquid chromatography with diode-array detector (HPLC-DAD) determination. Factors affecting the extraction efficiency such as amount of adsorbent, desorption solvent, volume of desorption solvent, extraction time, desorption time, pH and sample volume were investigated and optimized. The results revealed that under optimal conditions, the detection limit of selected PAEs and PAHs were in the range of 0.56-0.97 ng mL-1 and 0.02-0.93 ng mL-1, respectively. The spiked recoveries of real apple and cabbage extracts for PAEs and PAHs were in the range of 81.5-117.6% with good relative standard deviation (RSD) (n = 5) less than 10% and 86.7-118.2% with acceptable RSDs (n = 5) ranging from 1.5 to 11.0%, respectively. This study reported for the first time the use of MSPE procedure for simultaneous determination of chosen PAHs and PAEs in real samples including apple and cabbage extracts by using new adsorbent, FFA@MNP-GO.
The fabrication of a network of glucose oxidase-horseradish peroxidase/tin oxide (GOx-HRP/SnO₂), immobilized onto a glassy carbon electrode (GCE) and its utilization as a biosensor for glucose detection is reported. The network established with GOx-HRP/SnO₂ possess high sensitivity and stability by performing the electrocatalytic features in the sensing of glucose. The turbidity of fabrication had been scanned and analyzed using UV-vis spectroscopy. The morphology and composition of the fabricated GOx-HRP/SnO₂ networks were characterized by scanning electron microscopy (SEM). Cyclic voltammetry and amperometry were employed to study the electrochemical properties of the proposed biosensor. The effect of applied electrode potential and pH were systemically investigated. The biosensor responds to glucose at work potential values between -400 mV, and exhibited a lower detection limit (0.025 mM) and long linear range (0.25 to 7.0 mM), and was resistant to common interferences.
Glycerol electro-oxidation offers a green route to produce the high value added chemicals. Here in, we report the glycerol electro-oxidation over a series of multi walled carbon nano tubes supported monometallic (Pt/CNT and Pd/CNT) and bimetallic (Pt-Pd/CNT) catalysts in alkaline medium. The cyclic voltammetry, linear sweep voltammetry and chronoamperometry measurements were used to evaluate the activity and stability of the catalysts. The Pt-Pd/CNT electrocatalyst exhibited the highest activity in terms of higher current density (129.25 A/m²) and electrochemical surface area (382 m²/g). The glycerol electro-oxidation products formed at a potential of 0.013 V were analyzed systematically by high performance liquid chromatography. Overall, six compounds were found including mesoxalic acid, 1,3-dihydroxyacetone, glyceraldehyde, glyceric acid, tartronic acid and oxalic acid. A highest mesoxalic acid selectivity of 86.42% was obtained for Pt-Pd/CNT catalyst while a maximum tartronic acid selectivity of 50.17% and 46.02% was achieved for Pd/CNT and Pt/CNT respectively. It was found that the introduction of Pd into Pt/CNT lattice facilitated the formation of C3 products in terms of maximum selectivity achieved (86.42%) while the monometallic catalysts (Pd/CNT and Pt/CNT) showed a poor performance in comparison to their counterpart.
A multiporous nanofiber (MPNFs) of SnO₂ and chitosan has been used for the immobilization of a redox protein, hemoglobin (Hb), onto the surface of glassy carbon electrode (GCE). The multiporous nanofiber of SnO₂ that has very high surface area is synthesized by using electrospinning technique through controlling the tin precursor concentration. Since the constructed MPNFs of SnO₂ exposes very high surface area, it increases the efficiency for biomolecule-loading. The morphology of fabricated electrodes is examined by SEM observation and the absorbance spectra of Hb/(MPNFs) of SnO₂ are studied by UV-Vis analysis. Cyclic Voltammetry and amperometry are employed to study and optimize the performance of the resulting fabricated electrode. After fabrication of the electrode with the Hb and MPNFs of SnO₂, a direct electron transfer between the protein's redox centre and the glassy carbon electrode was established. The modified electrode has showed a couple of redox peak located at -0.29 V and -0.18 V and found to be sensitive to H₂O₂. The fabricated electrode also exhibited an excellent electrocatalytic activity towards the reduction of H₂O₂. The catalysis currents increased linearly to the H₂O₂ concentration in a wide range of 5.0×10-6-1.5×10-4 M. Overall experimental results show that MPNFs of SnO₂ has a role towards the enhancement of the electroactivity of Hb at the electrode surface. Thus the MPNFs of SnO₂ is a very promising candidate for future biosensor applications.
Nanostructure materials are of interest in last few decades due to their unique size-dependent physio-chemical properties. In this paper, zinc oxide (ZnO) and barium doped ZnO nanodisks (NDs) were synthesized using sonochemical method and characterized by various techniques such as X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscope (SEM), UV-vis absorption and dielectric measurements. The XRD and FTIR studies confirm the crystalline nature of ZnO NDs, and the average crystallite size was found to be ~25 nm for pure ZnO and ~22 nm for Ba doped ZnO NDs. SEM study confirmed the spherical shaped ZnO NDs with average sizes in the range of 20-30 nm. The maximum absorbance was obtained in the 200-500 nm regions with a prominent peak absorbance were observed by UV-vis spectra. The corresponding band gap for ZnO NDs and Ba doped ZnO NDs were calculated using Tauc's plot and was found to be 3.12 and 3.04, respectively. The conductivity and dielectric measurements as a function of frequency have been studied.