A first-of-its-kind, eco-friendly quasi-solid bioelectrolyte derived from potato starch was prepared. Starch was chemically modified via phthaloylation to synthesize amorphous, hydrophobic starch derivative and the attachment of the phthaloyl group was confirmed via FTIR which showed phthalate ester peak at 1715cm-1; and 1H NMR peaks between 7.30-7.90ppm attributed to the aromatic protons of the phthaloyl group. The resulting starch derivative was then infused with ternary natural deep eutectic solvent (NADES) made from different molar ratios of choline chloride, urea and glycerol. Electrochemical Impedance Spectroscopy (EIS) revealed that the highest ionic conductivity was obtained by the system consisting of NADES with choline chloride:urea:glycerol in molar ratios of 4:6:2, with a magnitude of 2.86mScm-1, hence validating the prospects of the materials to be further experimented as an alternative electrolyte in various electrochemical devices.
Silver diammine fluoride (SDF) is known as a noninvasive, cost-effective, safe, and simple method of dental caries treatment. However, staining and discoloration seem inseparable with SDF and continue as a cosmetic concern. Research is ongoing to overcome these issues, for example, by using glutathione (G) or potassium iodide among others. Therefore, the study aimed to investigate the effects of incorporating different concentrations of capping agents on SDF chemistry and SDF-mediated tooth staining at different time points. Tannic acid (TA), gallic acid (GA), carboxymethyl chitosan (CM), and G at different concentrations (5, 10, and 15% w/v) were incorporated in 30% SDF. FTIR and UV-Vis spectroscopies of the prepared solutions was performed to evaluate chemical changes. Time-dependent color changes (ΔE) in bovine dentine specimens (6 × 6 × 1 ± 0.25 mm3) were measured spectrophotometrically at application/washup, 1 and 3 h, after 1, 2, 4, 7, and 14 days. Results showed suppression of FTIR peaks at 3,358 cm-1 and 1,215 cm-1 in capping agent-modified SDF indicative of a successful capping effect of the silver ions, which was corroborated by UV-Vis blueshift of ∼∆32 nm. The capping effect on SDF increased proportionally with the concentrations of TA, GA, CM, and G used. A more pronounced tooth staining reduction however was shown more in TA- and G- rather than in GA- and CM-modified SDF. At day 14, SDF showed the highest mean ΔE(50.14 ± 2.14), while 15% TA showed the lowest ΔE(30.14 ± 0.81). In conclusion, capping agent incorporation significantly reduced SDF-mediated tooth staining. This reduction in staining is more dependent on the respective capping agent functional groups than concentrations per se. The potential of capping agents to minimize tooth staining of SDF was TA>G>CM>GA.
A binary salt system utilizing lithium iodide (LiI) as the auxiliary component has been introduced to the N-phthaloylchitosan (PhCh) based gel polymer electrolyte consisting of ethylene carbonate (EC), dimethylformamide (DMF), tetrapropylammonium iodide (TPAI), and iodine (I2) in order to improve the performance of dye-sensitized solar cell (DSSC) with efficiency of 6.36%, photocurrent density, JSC of 17.29mAcm-2, open circuit voltage, VOC of 0.59V and fill factor, FF of 0.62. This efficiency value is an improvement from the 5.00% performance obtained by the DSSC consisting of only TPAI single salt system. The presence of the LiI in addition to the TPAI improves the charge injection rates and increases the iodide contribution to the total conductivity and both factors contribute to the increase in efficiency of the DSSC. The interaction behavior between polymer-plasticizer-salt was thoroughly investigated using EIS, FTIR spectroscopy and XRD.