Aluminium substituted cobalt-copper Co1-xCuxFe2-xAlxO₄, (x ═ 0.8) nanoparticles are grown and sintered at different temperature in the range 600 to 900 °C. XRD analysis on nanoparticles prepared at sintered temperatures of 700 °C and 800 °C confirms the spinel structure and presence of hematite phase (alpha ferrite) in them. The dielectric behaviour of the prepared nano-particles is investigated. Although crystallinity improved with increase in sintering temperature and there was a dielectric loss at higher probe analyser frequency. The synthesized nanoparticles an average particle size of 20-24 nm while the FTIR absorption in regions of 586-595 cm-1 and 450-460 cm-1 indicated the presence of intrinsic vibrations of the tetrahedral and octahedral complexes respectively. Electrical resistivity as a function of temperature confirms the semiconducting nature of the Cu-Al substituted cobalt ferrite, and is attributed to the hopping mechanism between Fe2+ Fe3+ ions and Co2+ Cu2+, Co2+ Al3+. The lower values of dielectric constants and dielectric losses make Al-Cu doped cobalt ferrite, a potential material for microwave and radio wave absorber applications.
The present study aims at engineering, fabrication, characterization, and qualifications of papain (PPN) conjugated SiO2-coated iron oxide nanoparticles 'IONPs@SiO2-PPN'. Initially fabricated iron oxide nanoparticles (IONPs) were coated with silica (SiO2) using sol-gel method to hinder the aggregation and to enhance biocompatibility. Next, PPN was loaded as an anticancer agent into the silica coated IONPs (IONPs@SiO2) for the delivery of papain to the HeLa cancer cells. This fabricated silica-coated based magnetic nanoparticle is introduced as a new physiologically-compatible and stable drug delivery vehicle for delivering of PPN to the HeLa cancer cell line. The IONPs@SiO2-PPN were characterized using FT-IR, AAS, FESEM, XRD, DLS, and VSM equipment. Silica was amended on the surface of iron oxide nanoparticles (IONPs, γ-Fe2O3) to modify its biocompatibility and stability. The solvent evaporation method was used to activate PPN vectorization. The following tests were performed to highlight the compatibility of our proposed delivery vehicle: in vitro toxicity assay, in vivo acute systemic toxicity test, and the histology examination. The results demonstrated that IONPs@SiO2-PPN successfully reduced the IC50 values compared with the native PPN. Also, the structural alternations of HeLa cells exposed to IONPs@SiO2-PPN exhibited higher typical hallmarks of apoptosis compared to the cells treated with the native PPN. The in vivo acute toxicity test indicated no clinical signs of distress/discomfort or weight loss in Balb/C mice a week after the intravenous injection of IONPs@SiO2 (10 mg kg-1). Besides, the tissues architectures were not affected and the pathological inflammatory alternations detection failed. In conclusion, IONPs@SiO2-PPN can be chosen as a potent candidate for further medical applications in the future, for instance as a drug delivery vehicle or hyperthermia agent.
A stable, biocompatible and exquisite SPIONs-PEG-HER targeting complex was developed. Initially synthesized superparamagnetic iron oxide nanoparticles (SPIONs) were silanized using 3-aminopropyltrimethoxysilane (APS) as the coupling agent in order to allow the covalent bonding of polyethylene glycol (PEG) to the SPIONs to improve the biocompatibility of the SPIONs. SPIONs-PEG were then conjugated with herceptin (HER) to permit the SPIONs-PEG-HER to target the specific receptors expressed over the surface of the HER2+ metastatic breast cancer cells. Each preparation step was physico-chemically analyzed and characterized by a number of analytical methods including AAS, FTIR spectroscopy, XRD, FESEM, TEM, DLS and VSM. The biocompatibility of SPIONs-PEG-HER was evaluated in vitro on HSF-1184 (human skin fibroblast cells), SK-BR-3 (human breast cancer cells, HER+), MDA-MB-231 (human breast cancer cells, HER-) and MDA-MB-468 (human breast cancer cells, HER-) cell lines by performing MTT and trypan blue assays. The hemolysis analysis results of the SPIONs-PEG-HER and SPIONs-PEG did not indicate any sign of lysis while in contact with erythrocytes. Additionally, there were no morphological changes seen in RBCs after incubation with SPIONs-PEG-HER and SPIONs-PEG under a light microscope. The qualitative and quantitative in vitro targeting studies confirmed the high level of SPION-PEG-HER binding to SK-BR-3 (HER2+ metastatic breast cancer cells). Thus, the results reflected that the SPIONs-PEG-HER can be chosen as a favorable biomaterial for biomedical applications, chiefly magnetic hyperthermia, in the future.