The effect of TiO₂ nanoparticle (NP) content on the improvement of poly(9,9'-di-n-octylfluorenyl-2,7-diyl) (PFO)/Fluorol 7GA organic light emitting diode (OLED) performance is demonstrated here. The PFO/Fluorol 7GA blend with specific ratios of TiO₂ NPs was prepared via a solution blending method before being spin-coated onto an indium tin oxide (ITO) substrate to act as an emissive layer in OLEDs. A thin aluminum layer as top electrode was deposited onto the emissive layer using the electron beam chamber. Improvement electron injection from the cathode was achieved upon incorporation of TiO₂ NPs into the PFO/Fluorol 7GA blend, thus producing devices with intense luminance and lower turn-on voltage. The ITO/(PFO/Fluorol 7GA/TiO₂)/Al OLED device exhibited maximum electroluminescence intensity and luminance at 25 wt % of TiO₂ NPs, while maximum luminance efficiency was achieved with 15 wt % TiO₂ NP content. In addition, this work proved that the performance of the devices was strongly affected by the surface morphology, which in turn depended on the TiO₂ NP content.
Mesoporous TiO2 hollow spheres nanostructures with high surface areas were successfully prepared using a microwave method. The prepared hollow spheres have a size range between 200 and 500 nm. The spheres consisted of numerous smaller TiO2 nanoparticles with an average diameter of 8 nm. The particles had an essentially mesoporous structure with a pore size in the range of 2-50 nm. The results confirmed that the synthesised of anatase TiO2 nanoparticles with specific surface area approximately 172.3 m2/g. The effect of ultra violet and visible light irradiation and catalyst dosage on the TiO2 photocatalytic activity was studied by measuring the degradation rate of methylene blue. The maximum dye degradation performances with low amount catalyst loading (30 mg) were 99 % and 63.4 % using the same duration of ultra violet and visible light irradiation, respectively (120 min).