In the present research, the structural, electronic and optical properties of transition metal dichalcogenide-doped transition metal oxides MoS2-doped-V2O5 with various doping concentrations (x = 1-3%) of MoS2 atoms are studied by using first principles calculation. The generalized gradient approximation Perdew-Burke-Ernzerhof simulation approach is used to investigate the energy bandgap (Eg) of orthorhombic structures. We examined the energy bandgap (Eg) decrement from 2.76 to 1.30 eV with various doping (x = 1-3%) of molybdenum disulfide (MoS2) atoms. The bandgap nature shows that the material is a well-known direct bandgap semiconductor. MoS2 doping (x = 1-3%) atoms in pentoxide (V2O5) creates the extra gamma active states which contribute to the formation of conduction and valance bands. MoS2-doped-V2O5 composite is a proficient photocatalyst, has a large surface area for absorption of light, decreases the electron-hole pairs recombination rate and increases the charge transport. A comprehensive study of optical conductivity reveals that strong peaks of MoS2-doped-V2O5 increase in ultraviolet spectrum region with small shifts at larger energy bands through increment doping x = 1-3% atoms of MoS2. A significant decrement was found in the reflectivity due to the decrement in the bandgap with doping. The optical properties significantly increased by the decrement of bandgap (Eg). Two-dimensional MoS2-doped-V2O5 composite has high energy absorption, optical conductivity and refractive index, and is an appropriate material for photocatalytic applications.
In the current research, the resist action of silver-doped polystyrene/polyethylene terephthalate (PET) solar thin film towards laser irradiation was observed. Moreover, silver-doped polystyrene nanoparticles were synthesized via a chemical technique while the PET film was purchased from the commercial market. Nd:YAG pulsed laser has been used to irradiate the samples at 2 minutes, 4 minutes, and 6 minutes respectively. The XRD (X-ray diffraction) pattern shows that silver-doped polystyrene peak at around angle θ = 26° tends to decrease after the bombardment of Nd:YAG pulsed laser. This indicates that the crystallinity of PET film decreased after laser irradiation. The Raman spectra have revealed the zwitter characteristics of silver-doped polystyrene are shifting of bands at 1380 cm-1 and 1560 cm-1 upon laser irradiation. For PET film, the Raman spectra showed that the exposed regions tend to change to cross-linking/chain-scissoring at 2 minutes and 4 minutes of irradiation. The surface roughness first increases and decreases upon irradiation. These results indicate that silver-doped polystyrene/polyethylene terephthalate (PET) thin film is appropriate for solar cell applications.