Immobilisation of cyclodextrin glucanotransferase (CGTase) on nanofibres was demonstrated. CGTase solution (1% v/v) and PVA (8 wt%) solution were mixed followed by electrospinning (-9 kV, 3 h). CGTase/PVA nanofibres with an average diameter of 176 ± 46 nm were successfully produced. The nanofibres that consist of immobilised CGTase were crosslinked with glutaraldehyde vapour. A CGTase/PVA film made up from the same mixture and treated the same way was used as a control experiment. The immobilised CGTase on nanofibres showed superior performance with nearly a 2.5 fold higher enzyme loading and 31% higher enzyme activity in comparison with the film.
In this study, the potential of electrohydrodynamic atomization or electrospraying to produce nanometer-order CGTase particles from aqueous suspension was demonstrated. CGTase enzyme was prepared in acetate buffer solution (1% v/v), followed by electrospraying in stable Taylor cone-jet mode. The deposits were collected on aluminium foil (collector) at variable distances from the tip of spraying needle, ranging from 10 to 25 cm. The Coulomb fission that occurs during electrospraying process successfully transformed the enzyme to the solid state without any functional group deterioration. The functional group verification was conducted by FTIR analysis. Comparison between the deposit and the as-received enzyme in dry state indicates almost identical spectra. By increasing the distance of the collector from the needle tip, the average particle size of the solidified enzyme was reduced from 200±117 nm to 75±34 nm. The average particle sizes produced from the droplet fission were in agreement with the scaling law models. Enzyme activity analysis showed that the enzyme retained its initial activity after the electrospraying process. The enzyme particles collected at the longest distance (25 cm) demonstrated the highest enzyme activity, which indicates that the activity was controlled by the enzyme particle size.