Materials and Methods: Ninety J-shaped canals in resin blocks were filled with 2% Methylene Blue solution and pre-instrumentation images were taken using a Leica microscope at a ×10. They were prepared until size 25 taper 0.04 using (n = 18 per group): T-Flex, HyFlex CM, Vortex Blue, S5, and iRace. After instrumentation, images were captured again, and composite images were made using Adobe Photoshop imaging software. The differences in canal width and canal curvature at each respective landmark were measured and compared. The preparation time and canal abbreviations were also recorded. Statistical analyses were performed using one-way ANOVA and post hoc Tukey HSD tests. The level of statistical significance was set to P = 0.05.
Results: HyFlex CM demonstrated the least difference in canal width after instrumentation, but no significant difference (P > 0.05) as compared to T-Flex and Vortex Blue. The mean canal straightening ranged between 0.91° and 7.65°. T-Flex created the least canal straightening after instrumentation which was significantly less (P < 0.05) than S5, but there was no significant difference (P > 0.05) when compared to HyFlex CM. Instrumentation with the S5 file was significantly faster (P < 0.05), whereas HyFlex CM was the slowest.
Conclusion: T-Flex, HyFlex CM, and Vortex Blue demonstrated better shaping ability, whilst T-Flex and HyFlex CM maintained the original canal curvatures well. S5 tended to straighten the canals and caused the greatest canal transportation, but it required the least amount of time to shape the canal.
Material and Methods: Eighty mature permanent maxillary lateral incisors from patients age range of 30-60 years with single canal were selected and randomly divided into: Group 1 - RCT + nanofilled composite (Filtek), Group 2 - RCT + microhybrid composite (Zmack), Group 3 - RCT + new nanohybrid composite (Zr-Hybrid) and Group 4 - Intact teeth (control). Standardized mesio-palatal-distal cavity was prepared, and endodontic treatment was carried out using crown-down technique until size 30, tapered 0.04. Obturation was completed using single cone technique with gutta-percha and AH plus sealer. Cavity access was restored with respective composite resins. Next, teeth were stored in incubator for 24 hours and subdivided into aged and unaged subgroups. Teeth in aged subgroups were subjected to 2500 thermal cycles for 5ºC, 37ºC and 55ºC with 30 seconds dwell time and 5 seconds transfer time. After that, root surfaces of teeth were covered with silicone-based material and placed in boxes filled with acrylic until the cemento-enamel-junction (CEJ) level. They were then tested under Universal Testing Machine until fracture occurred. Samples were then viewed under Leica microscope to determine the fracture pattern and type of fracture. Data analyzed using One-way ANOVA complimented by post hoc Tukey HSD and paired sample T test for fracture strength. Fracture pattern and type of fracture were analyzed using Chi-square test. Level of significance was set at p<0.05.
Results: Significant differences were observed (p<0.05) with Group 3 demonstrating the highest fracture strength followed by Group 4, Group 1 and lastly Group 2 in both aged and unaged subgroups respectively. A significant decreased in fracture strength was noted in Group 1 and Group 2 (p<0.05) as number of thermocycle increased but no significant differences were noted in Group 3 and Group 4 (p>0.05). Besides, Group 3 and Group 4 showed higher rate of favorable fracture pattern, followed by Group 1 and lastly Group 2. Most favorable fracture pattern was noted to exhibit horizontal fracture type (86.36%), whereas most unfavorable fracture pattern exhibited vertical fracture type (77.78%).
Conclusions: Endodontically treated teeth restored with new zirconia reinforced rice husk nanohybrid composite (Zr-Hybrid) demonstrated higher fracture strength than commercialized composite resins especially after artificial ageing. Zr-Hybrid showed similar fracture pattern to those of intact teeth with higher rate of horizontal fracture type. Key words:Fracture strength, fracture pattern, composite resin, rice husk, Zirconia.