Cross-linked chitosan/sepiolite composite was prepared from sepiolite clay and chitosan, and was cross-linked using epichlorohydrin. Among the various weight ratio percentage of chitosan and sepiolite clay composites, CS50SP50 was selected as the best adsorbent for both methylene blue (MB) and reactive orange 16 (RO 16). At an optimum adsorbent dosage of 0.2g/100mL, the effects of initial dye concentration (25-400mg/L) and pH (3-11) on MB and RO 16 adsorption onto CS50SP50 composite were studied. Monolayer adsorption capacities of CS50SP50 composite for MB and RO 16 were 40.986mg/g and 190.965mg/g, respectively at 30°C. Freundlich, Langmuir and Temkin isotherms applied on the adsorption data for both the dyes reveal that data fitted best for Freundlich model. For both the dyes pseudo-second-order kinetics were found to describe the adsorption process better than pseudo-first-order kinetics. The adsorption capacity of CS50SP50 composite for both the dyes was found better compared to previous studies thus making it potentially low-cost adsorbent for removal of both cationic and reactive dyes.
In this work, mesoporous-activated carbon (CSAC) was prepared from chitosan flakes (CS) via single-step sodium hydroxide activation for the adsorption of methylene blue (MB). CSAC was prepared using different impregnation ratios of NaOH:CS (1:1, 2:1, 3:1, and 4:1) at 800°C for 90min. The adsorption performance of CSAC was evaluated for MB at different adsorption variables, such MB initial concentrations (25-400mg/L), solution pH (3-11), and temperature (30-50°C). The adsorption isotherm data of CSAC-MB were well fitted to Langmuir model with a maximum adsorption capacity 143.53mg/g at 50°C. Best representation of kinetic data was obtained by the pseudo-second order model. CSAC exhibited excellent adsorption uptake for MB and can potentially be used for other cationic dyes.