Self-organized, 23 μm-thick anodic TiO2 nanotube (TNT) arrays were formed in sodium hydroxide/fluoride/ethylene glycol (EG) electrolyte at 60 V for 60 min. The presence of sodium hydroxide (NaOH) in the fluoride/EG electrolyte accelerates the formation of the TiO2 nanotube arrays. The anodic film was then decorated with silver nanoparticles (Ag NPs) by the photodeposition process and used as a photoanode in a rear-side-illuminated dye-sensitized solar cell. The Ag NPs decorated TNT arrays, with the former having diameters of 10-30 nm formed from 0.2 M of Ag-precursor solution and exhibiting the highest photoconversion efficiency (η) of 3.7% and a short-circuit current density of 12.2 mA cm(-2) compared to η = 3% and short-circuit current density of 9.1 mA cm(-2) for a sample without Ag NPs. The increase in η is thought to be due to the surface plasmon resonance and excess electrons from the nanoparticles.