Amnion is a membrane that surrounds and structurally protects the developing fetus during pregnancy. The rupture of amniotic membranes prior to both normal and preterm deliveries involves stretch forces acting on a biochemically triggered weak zone of the membranes. Fracture toughness is an important mechanical property describing how the membranes containing a defect resist fracture, but this property has never been investigated in amniotic membranes. In this work, the fracture toughness of many samples cut from four pieces of amniotic membrane from different mothers was examined by uniaxial and pure shear (mode I) fracture tests. The measurement was checked for dependence on the sample geometry and notch length. Results from the uniaxial tensile test show J-shaped stress-strain curves and confirm that the amniotic membrane is a nonlinear material. The measured fracture toughness of four amniotic membranes ranged from 0.96 ± 0.11 to 1.83 ± 0.18 kJ m-2. Despite considering the effect of the presence of the defect on mechanical property measurement, similar fracture behaviour was observed for pre-notched and unnotched specimens, indicating that the membranes were extremely tolerant to defects. This defect-tolerant characteristic provides insight into the understanding of fetal membrane rupture.
Electrospinning is a simple and efficient process for producing sub-micron fibres. However, the process has many variables, and their effects on the non-woven mesh of fibres is complex. In particular, the effects on the mechanical properties of the fibre meshes are poorly understood. This paper conducts a parametric study, where the concentration and bloom strength of the gelatin solutions are varied, while all electrospinning process parameters are held constant. The effects on the fibrous meshes are monitored using scanning electron microscopy and mechanical testing under uniaxial tension. Mesh mechanical properties are relatively consistent, despite changes to the solutions, demonstrating the robustness of electrospinning. The gel strength of the solution is shown to have a statistically significant effect on the morphology, stiffness and strength of the meshes, while the fibre diameter has surprisingly little influence on the stiffness of the meshes. This experimental finding is supported by finite element analysis, demonstrating that the stiffness of the meshes is controlled by the volume fraction, rather than fibre diameter. Our results demonstrate the importance of understanding how electrospinning parameters influence the pore size of the meshes, as controlling fibre diameter alone is insufficient for consistent mechanical properties.