This study employs a computational approach to analyse the impact of morphological changes on the structural properties of biodegradable porous Mg subjected to a dynamic immersion test for its application as a bone scaffold. Porous Mg was immersed in a dynamic immersion test for 24, 48, and 72 h. Twelve specimens were prepared and scanned using micro-CT and then reconstructed into a 3D model for finite element analysis. The structural properties from the numerical simulation were then compared to the experimental values. Correlations between morphological parameters, structural properties, and fracture type were then made. The relative losses were observed to be in agreement with relative mass loss done experimentally. The degradation rates determined using exact (degraded) surface area at particular immersion times were on average 20% higher than the degradation rates obtained using original surface area. The dynamic degradation has significantly impacted the morphological changes of porous Mg in volume fraction, surface area, and trabecular separation, which in turn affects its structural properties and increases the immersion time.
Pilon fractures can be caused by high-energy vertical forces which may result in long-term patient immobilization. Many experts in orthopedic surgery recommend the use of a Delta external fixator for type III Pilon fracture treatment. This device can promote immediate healing of fractured bone, minimizing the rate of complications as well as allowing early mobilization. The characteristics of different types of the Delta frame have not been demonstrated yet. By using the finite element method, this study was conducted to determine the biomechanical characteristics of six different configurations (Model 1 until Model 6). CT images from the lower limb of a healthy human were used to reconstruct three-dimensional models of foot and ankle bones. All bones were assigned with isotropic material properties and the cartilages were assigned to exhibit hyperelasticity. A linear link was used to simulate 37 ligaments at the ankle joint. Axial loads of 70 and 350 N were applied at the proximal tibia to simulate the stance and swing phase. The metatarsals and calcaneus were fixed distally in order to prevent rigid body motion. A synthetic ankle bone was used to validate the finite element model. The simulated results showed that Delta3 produced the highest relative micromovement (0.09 mm, 7 μm) during the stance and swing phase, respectively. The highest equivalent von Mises stress was found at the calcaneus pin of the Delta4 (423.2 MPa) as compared to others. In conclusion, Delta1 external fixator was the most favorable option for type III Pilon fracture treatment. Graphical abstract ᅟ.
Intact glenoid labrum is one of passive stabilizer for glenohumeral joint, which have various stiffness at different region. The aim of this study is to develop new artificial glenoid labrum from Polyvinyl Alcohol (PVA) hydrogel, which known as good biomaterial due to its biocompatibility and ability to tailor its modulus. PVA hydrogel was formed using freeze-thaw (FT) method and the stiffness of PVA was controlled by manipulating the concentration of PVA and number of FT cycles. Then, the gradual stiffness was formed using simple diffusion method by introducing the pre-freeze-and-thaw steps. The results showed 20% PVA with three FT cycles suit to highest stiffness of glenoid labrum while 10% PVA with three FT cycles suit to lowest stiffness of glenoid labrum. The functionally graded PVA hydrogel was then developed using the same method by diffusing two mixture (20% PVA and 10% PVA). Mechanical compression test showed, the highest modulus (0.41 MPa) found at the 20% PVA region and lowest modulus (0.1 MPa) found at 10% PVA region. While, at intermediate region, the compressive modulus was in between 20% and 10%, 0.2 MPa. The existence of gradual stiffness was further prove by checking crystallinity of material at each region using Differential Scanning Calorimetry (DSC) and Wide Angle X-ray Diffraction (WAXD). Microstructure of material was obtained from Scanning Electron Microscopy (SEM). This functionally graded PVA hydrogel also able to reduce about 51% of stress at glenoid implant and up to 17% for micromotion at the interfaces. Existence of artificial glenoid labrum could minimize the occurrence of glenoid component loosening.