The research included corn starch (CS) films using sorbitol (S), glycerol (G), and their combination (SG) as plasticizers at 30, 45, and 60 wt %, with a traditional solution casting technique. The introduction of plasticizer to CS film-forming solutions led to solving the fragility and brittleness of CS films. The increased concentration of plasticizers contributed to an improvement in film thickness, weight, and humidity. Conversely, plasticized films reduced their density and water absorption, with increasing plasticizer concentrations. The increase in the amount of the plasticizer from 30 to 60% showed a lower impact on the moisture content and water absorption of S-plasticized films. The S30-plasticized films also showed outstanding mechanical properties with 13.62 MPa and 495.97 MPa, for tensile stress and tensile modulus, respectively. Glycerol and-sorbitol/glycerol plasticizer (G and SG) films showed higher moisture content and water absorption relative to S-plasticized films. This study has shown that the amount and type of plasticizers significantly affect the appearances, physical, morphological, and mechanical properties of the corn starch biopolymer plastic.
This paper documents the thermal and biodegradation behaviour of kenaf/cornhusk fiber reinforced corn starch-based hybrid composites film (CS/K-CH) produced by solution casting method. To develop both components as biodegradable hybrid composite, this research used corn starch as matrix, kenaf fiber and cornhusk fibre as a filler. Changes in physical structure and weight from the soil burial test were measured using Mettler Toledo digital balance ME. Films produced from physically blended corn starch reinforced kenaf biocomposites films (CS/K) biocomposite film had faster biodegradation and lost 96.18% of weight within 10 days compared with corn starch hybrid composites that only lost 83.82% of total weight. It was observed that the control film, CS/K biocomposite film was completely degraded after 10 days, meanwhile it took 12 days for hybrid composite films to be fully degrade. The thermal properties such as TGA and DTG were also measured. Addition of corn husk fiber significantly improve the film's thermal properties. Glass transition temperatures of corn starch hybrid films were significantly lowered when cornhusk compositions were increased from 0.2% wt to 0.8% wt. Importantly, the current work has demonstrated that hybrid films made of corn starch can be a suitable biodegradable material for substitute synthetic plastic.