METHODS: Relevant articles written in English only, before January 15, 2017, were identified using an electronic search in the PubMed, Scopus, and Google Scholar databases. Furthermore, a manual search of the related major journals was also conducted to identify more pertinent articles. The relevancy of the articles was verified by screening the title, abstract, and full text if they met the inclusion criteria. A total of 37 articles satisfied the criteria, from which data were extracted for qualitative synthesis.
RESULTS: Among the 37 included articles, 14 were without aging, 15 were natural or artificial accelerated aging, 7 were outdoor weathering, and 1 contained both artificial aging and outdoor weathering. Only 4 studies out of the 14 without aging had significant observations; whereas 9 articles with natural or artificial aging published significant results, and 3 out of 7 outdoor weathering articles showed significant changes in the evaluated silicone elastomers.
CONCLUSIONS: Despite the varying research, it seems that the single "ideal" maxillofacial prosthetic material that can provide sufficient resistance against different aging conditions is yet to be identified. Therefore, it is imperative for standardization organizations, the scientific community, and academia to develop modified prosthetic silicones possessing improved physical properties and color stability, limiting the clinical problems regarding degradation of maxillofacial prostheses.
MATERIALS AND METHODS: Sixmaster dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Ten copings of 0.6 mm thickness were fabricated from each type of ceramic, for a total of thirty copings. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented with resin luting cement Panavia F according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.
RESULTS: The results of the present study showed the following mean loads at fracture: Turkom-Cera (2184 +/- 164 N), In-Ceram (2042 +/- 200 N), and Procera AllCeram (1954 +/- 211 N). ANOVA and Scheffe's post hoc test showed that the mean load at fracture of Turkom-Cera was significantly different from Procera AllCeram (p < 0.05). Scheffe's post hoc test showed no significant difference between the mean load at fracture of Turkom-Cera and In-Ceram or between the mean load at fracture of In-Ceram and Procera AllCeram.
CONCLUSION: Because Turkom-Cera demonstrated equal to or higher loads at fracture than currently accepted all-ceramic materials, it would seem to be acceptable for fabrication of anterior and posterior ceramic crowns.
METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.
RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.
CONCLUSION: Different luting agents have an influence on the fracture resistance of Procera AllCeram copings.