Polyhydroxyalkanoates (PHAs) are hydrophobic biodegradable thermoplastics that have received considerable attention in biomedical applications due to their biocompatibility, mechanical properties, and biodegradability. In this study, the degradation rate was regulated by optimizing the interaction of parameters that influence the enzymatic degradation of P(3HB) film using response surface methodology (RSM). The RSM model was experimentally validated yielding a maximum 21 % weight loss, which represents onefold increment in percentage weight loss in comparison with the conventional method. By using the optimized condition, the enzymatic degradation by an extracellular PHA depolymerase from Acidovorax sp. DP5 was studied at 37 °C and pH 9.0 on different types of PHA films with various monomer compositions. Surface modification of scaffold was employed using enzymatic technique to create highly porous scaffold with a large surface to volume ratio, which makes them attractive as potential tissue scaffold in biomedical field. Scanning electron microscopy revealed that the surface of salt-leached films was more porous compared with the solvent-cast films, and hence, increased the degradation rate of salt-leached films. Apparently, enzymatic degradation behaviors of PHA films were determined by several factors such as monomer composition, crystallinity, molecular weight, porosity, and roughness of the surface. The hydrophilicity and water uptake of degraded salt-leached film of P(3HB-co-70%4HB) were enhanced by incorporating chitosan or alginate. Salt-leached technique followed by partial enzymatic degradation would enhance the cell attachment and suitable for biomedical as a scaffold.
Dendrobium sonia-28 is an important ornamental orchid in the Malaysian flower industry. However, the genus faces both low germination rates and the risk of producing heterozygous progenies. Cryopreservation is currently the favoured long-term storage method for orchids with propagation problems. Vitrification, a frequently used cryopreservation technique, involves the application of pretreatments and cryoprotectants to protect and recover explants during and after storage in liquid nitrogen. However, cryopreservation may cause osmotic injuries and toxicity to cryopreserved explants from the use of highly concentrated additives, and cellular injuries from thawing, devitrification and ice formation. Reactive oxygen species (ROS), occurring during dehydration and cryopreservation, may also cause membrane damage. Plants possess efficient antioxidant systems such as the superoxide dismutase (SOD) and catalase (CAT) enzymes to scavenge ROS during low temperature stress. In this study, protocorm-like bodies (PLBs) of Dendrobium sonia-28 were assayed for the total protein content, and both SOD and CAT activities, at each stage of a vitrification exercise to observe for deleterious stages in the protocol. The results indicated that cryopreserved PLBs of Dendrobium sonia-28 underwent excessive post-thawing oxidative stress due to decreased levels of the CAT enzyme at the post-thawing recovery stage, which contributed to the poor survival rates of the cryopreserved PLBs.
Cellulase is an enzyme that converts the polymer structure of polysaccharides into fermentable sugars. The high market demand for this enzyme together with the variety of applications in the industry has brought the research on cellulase into focus. In this study, crude cellulase was produced from oil palm empty fruit bunch (OPEFB) pretreated with 2% NaOH with autoclave, which was composed of 59.7% cellulose, 21.6% hemicellulose, and 12.3% lignin using Trichoderma asperellum UPM1 and Aspergillus fumigatus UPM2. Approximately 0.8 U/ml of FPase, 24.7 U/ml of CMCase and 5.0 U/ml of β-glucosidase were produced by T. asperellum UPM1 at a temperature of 35 °C and at an initial pH of 7.0. A 1.7 U/ml of FPase, 24.2 U/ml of CMCase, and 1.1 U/ml of β-glucosidase were produced by A. fumigatus UPM2 at a temperature of 45 °C and at initial pH of 6.0. The crude cellulase was best produced at 1% of substrate concentration for both T. asperellum UPM1 and A. fumigatus UPM2. The hydrolysis percentage of pretreated OPEFB using 5% of crude cellulase concentration from T. asperellum UPM1 and A. fumigatus UPM2 were 3.33% and 19.11%, with the reducing sugars concentration of 1.47 and 8.63 g/l, respectively.
In this study, the ability of Cupriavidus sp. USMAA2-4 to synthesize polyhydroxyalkanoates (PHA) containing 4-hydroxyvalerate monomer (4HV) was studied through one-stage cultivation using γ-valerolactone as the carbon precursor. The presence of 4HV monomer unit in the polymer was detected through gas chromatography analysis, proving the capability of this wild strain bacterium to produce poly(3-hydrxybutyrate-co-3-hydroxyvalerate-co-4-hydroxyvalerate) [P(3HB-co-3HV-co-4HV)] terpolymer. Existence of a 4HV monomer unit in the PHA produced was further confirmed through (13)C and (1)H NMR analysis. P(3HB-co-88 % 3HV-co-1 % 4HV) terpolymer with the highest PHA content of 63 wt% was obtained through combination of 0.14 wt% C of γ-valerolactone with 0.42 wt% C of oleic acid. Various compositions of P(3HB-co-3HV-co-4HV) terpolymer with 3HV and 4HV compositions ranging from 11 to 94 mol% and from 1 to 4 mol%, respectively, were acquired by manipulating γ-valerolactone and oleic acid concentrations. The molecular weight and the thermal and mechanical properties of four different compositions of terpolymers-P(3HB-co-91 % 3HV-co-1 % 4HV), P(3HB-co-55 % 3HV-co-2 % 4HV), P(3HB-co-27 % 3HV-co-2 % 4HV), and P(3HB-co-9 % 3HV-co-1 % 4HV)-were characterized. Among these terpolymers, P(3HB-co-27 % 3HV-co-2 % 4HV) terpolymer with a molecular weight of 5.7 (10(5) Da) exhibited the highest elongation to break (264 %). The monomer unit compositional distributions of these terpolymers were investigated through acetone-water fractionation analysis. The results suggested that these produced terpolymers had broad 3HV compositional distribution and narrow 4HV compositional distribution.
Oil palm empty fruit bunch (EFB) is abundantly available in Malaysia and it is a potential source of xylose for the production of high-value added products. This study aimed to optimize the hydrolysis of EFB using dilute sulfuric acid (H2SO4) and phosphoric acid (H3PO4) via response surface methodology for maximum xylose recovery. Hydrolysis was carried out in an autoclave. An optimum xylose yield of 91.2 % was obtained at 116 °C using 2.0 % (v/v) H2SO4, a solid/liquid ratio of 1:5 and a hydrolysis time of 20 min. A lower optimum xylose yield of 24.0 % was observed for dilute H3PO4 hydrolysis at 116 °C using 2.4 % (v/v) H3PO4, a solid/liquid ratio of 1:5 and a hydrolysis time of 20 min. The optimized hydrolysis conditions suggested that EFB hydrolysis by H2SO4 resulted in a higher xylose yield at a lower acid concentration as compared to H3PO4.
Regrowth of the cryopreserved protocorm-like bodies (PLBs) of Dendrobium Bobby Messina was assessed based on the plant vitrification solution 2 (PVS2) optimisation conditions. The optimized protocol obtained based on TTC spectrophotometrical analysis and growth recovery were 3-4 mm of PLBs size precultured in 0.2 M sucrose for 1 day, treated with a mixture of 2 M glycerol and 0.4 M sucrose supplemented with half-strength liquid MS media at 25 °C for 20 min and subsequently dehydrated with PVS2 at 0 °C for 20 min prior to storage in liquid nitrogen. Following rapid warming in a water bath at 40 °C for 90 s, PLBs were treated with unloading solution containing half-strength liquid MS media supplemented with 1.2 M sucrose. Subsequently, the PLBs were cultured on half-strength semi-solid MS media supplemented with 2 % (w/v) sucrose without any growth regulators and resulted in 40 % growth recovery. In addition, ascorbic acid treatment was used to evaluate the regeneration process of cryopreserved PLBs. However, growth recovery rates of non-cryopreserved and cryopreserved PLBs were 30 and 10 % when 0.6 mM ascorbic acid was added. Scanning electron microscopy analysis indicates that there are not much damages observed on both cryopreserved and non-cryopreserved PLBs in comparison to PLBs stock culture.
Lafora disease (LD) is an autosomal recessive, progressive form of myoclonus epilepsy which affects worldwide. LD occurs mainly in countries like southern Europe, northern Africa, South India, and in the Middle East. LD occurs with its onset mainly in teenagers and leads to decline and death within 2 to 10 years. The genes EPM2A and EPM2B are commonly involved in 90 % of LD cases. EPM2A codes for protein laforin which contains an amino terminal carbohydrate binding module (CBM) belonging to the CBM20 family and a carboxy terminal dual specificity phosphatase domain. Mutations in laforin are found to abolish glycogen binding and have been reported in wet lab methods. In order to investigate on structural insights on laforin mutation K81A, we performed molecular dynamics (MD) simulation studies for native and mutant protein. MD simulation results showed loss of stability due to mutation K87A which confirmed the structural reason for conformational changes observed in laforin. The conformational change of mutant laforin was confirmed by analysis using root mean square deviation, root mean square fluctuation, solvent accessibility surface area, radius of gyration, hydrogen bond, and principle component analysis. Our results identified that the flexibility of K87A mutated laforin structure, with replacement of acidic amino acid to aliphatic amino acid in functional CBM domain, have more impact in abolishing glycogen binding that favors LD.
The ability of non-living biomass of an arsenic-hypertolerant Bacillus cereus strain SZ2 isolated from a gold mining environment to adsorb As (III) from aqueous solution in batch experiments was investigated as a function of contact time, initial As (III) concentration, pH, temperature and biomass dosage. Langmuir model fitted the equilibrium data better in comparison to Freundlich isotherm. The maximum biosorption capacity of the sorbent, as obtained from the Langmuir isotherm, was 153.41 mg/g. The sorption kinetic of As (III) biosorption followed well the pseudo-second-order rate equation. The Fourier transform infrared spectroscopy analysis indicated the involvement of hydroxyl, amide and amine groups in As (III) biosorption process. Field emission scanning electron microscopy-energy dispersive X-ray analysis of the non-living B. cereus SZ2 biomass demonstrated distinct cell morphological changes with significant amounts of As adsorbed onto the cells compared to non-treated cells. Desorption of 94 % As (III) was achieved at acidic pH 1 showing the capability of non-living biomass B. cereus SZ2 as potential biosorbent in removal of As (III) from arsenic-contaminated mining effluent.
Keratinous wastes have increasingly become a problem and accumulate in the environment mainly in the form of feathers, generated mainly from a large number of poultry industries. As keratins are very difficult to degrade by general proteases, they pose a major environmental problem. Therefore, microorganisms which would effectively degrade keratins are needed for recycling such wastes. A geophilic dermatophyte, Microsporum fulvum IBRL SD3 which was isolated from a soil sample collected from a chicken feather dumping site using a baiting technique, was capable to produce keratinase significantly. The crude keratinase was able to degrade whole chicken feathers effectively. The end product of the degradation was protein that contained essential amino acids and may have potential application in animal feed production. Thus, M. fulvum could be a novel organism to produce keratinase for chicken feathers degradation.
The effect of cultivation condition of two locally isolated ascomycetes strains namely Trichoderma asperellum UPM1 and Aspergillus fumigatus UPM2 were compared in submerged and solid state fermentation. Physical evaluation on water absorption index, solubility index and chemical properties of lignin, hemicellulose and cellulose content as well as the cellulose structure on crystallinity and amorphous region of treated oil palm empty fruit bunch (OPEFB) (resulted in partial removal of lignin), sago pith residues (SPR) and oil palm decanter cake towards cellulases production were determined. Submerged fermentation shows significant cellulases production for both strains in all types of substrates. Crystallinity of cellulose and its chemical composition mainly holocellulose components was found to significantly affect the total cellulase synthesis in submerged fermentation as the higher crystallinity index, and holocellulose composition will increase cellulase production. Treated OPEFB apparently induced the total cellulases from T. asperellum UPM1 and A. fumigatus UPM2 with 0.66 U/mg FPase, 53.79 U/mg CMCase, 0.92 U/mg β-glucosidase and 0.67 U/mg FPase, 47.56 U/mg and 0.14 U/mg β-glucosidase, respectively. Physical properties of water absorption and solubility for OPEFB and SPR also had shown significant correlation on the cellulases production.
Cryopreservation is an alternative, safe, and cost-effective method for long-term plant genetic resource conservation. This study was conducted to optimize the conditions for cryopreserving the protocorm-like bodies (PLBs) of Brassidium Shooting Star orchid with the PVS3 vitrification method. Five parameters were assessed in this study: PLB size, sucrose concentration, preculture duration, PVS3 duration, and unloading duration. The viability of the cryopreserved PLBs was determined using the triphenytetrazolium chloride assay and growth recovery assessments. The optimum condition for the cryopreservation of the PLBs of Brassidium Shooting Star orchid is based on the size range between 3 and 4 mm precultured with half-strength semi-solid MS media supplemented with 0.25 M sucrose for 24 h, followed by treatment with loading solution mixture of 2 M glycerol and 0.4 M sucrose supplemented with half-strength liquid MS media at 25 °C for 20 min. The PLBs were then dehydrated with PVS3 at 0 °C for 20 min prior to immersion in liquid nitrogen; finally, the PLBs were immersed with half-strength liquid MS media supplemented with 1.2 M sucrose for 30 min. Histological analyses displayed denser cytoplasm and voluminous nucleus in the cryopreserved PLBs of Brassidium Shooting Star orchid.
Enteroendocrine cells are the largest population of hormone-producing cells in the body and play important roles in many aspects of body functions. The enteroendocrine cell population is divided into different subpopulations that secrete different hormones and peptides. Characterization of each subpopulation is particularly useful for analyzing the cellular mechanisms responsible for specific cell types. Therefore, the necessity of a pure cell line for a specific study purpose was the important motivation for the separation of cell lines for each subpopulation of enteroendocrine cells. The present research introduces a method for the isolation of L-cells, one of the important subpopulations of enteroendocrine cells. The antibiotic selection method was conducted in order to isolate the L-cells from a heterogonous population of intestinal cell line. In this method, a neomycin resistance gene (as selected marker) was expressed under the control of a specific promoter of L-cells. After transfection of manipulated plasmid, only the cells which determine the specific promoter and express neomycin resistance protein would be able to survive under Geneticin antibiotic treatment condition. In order to confirm that the isolated cells were L-cells, reverse transcriptase polymerase chain reaction (PCR) and quantitative PCR assays were performed. Based on the results, the isolated cells were pure L-cells that could be able to express specific mRNA of L-cells efficiently. This technique provides a unique method for the isolation and purification of any cell line. The purified isolated L-cells by this method can be used for future studies and for analyzing cellular mechanisms that involve L-cells' functions.
Astaxanthin, a carotenoid pigment found in several aquatic organisms, is responsible for the red colour of salmon, trout and crustaceans. In this study, astaxanthin production from freshwater microalga Chlorella sorokiniana and marine microalga Tetraselmis sp. was investigated. Cell growth and astaxanthin production were determined spectrophotometrically at 620 and 480 nm, respectively. Astaxanthin was extracted using acetone and measured subsequent to biomass removal. Aerated conditions favoured astaxanthin production in C. sorokiniana, whereas Tetraselmis sp. was best cultured under unaerated conditions. C. sorokiniana produced more astaxanthin with the highest yield reached at 7.83 mg/l in 6.0 mM in nitrate containing medium compared to Tetraselmis sp. which recorded the highest yield of only 1.96 mg/l in 1.5 mM nitrate containing medium. Production in C. sorokiniana started at the early exponential phase, indicating that astaxanthin may be a growth-associated product in this microalga. Further optimization of astaxanthin production was performed using C. sorokiniana through a 2(3) full factorial experimental design, and a yield of 8.39 mg/l was achieved. Overall, the study has shown that both microalgae are capable of producing astaxanthin. Additionally, this research has highlighted C. sorokiniana as a potential astaxanthin producer that could serve as a natural astaxanthin source in the current market.
Poly(3-hydroxybutyrate) [P(3HB)], a polymer belonging to the polyhydroxyalkanoate (PHA) family, is accumulated by numerous bacteria as carbon and energy storage material. The mobilization of accumulated P(3HB) is associated with increased stress and starvation tolerance. However, the potential function of accumulated copolymer such as poly(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] remained unknown. In this study, Delftia acidovorans DS 17 was used to evaluate the contributions of P(3HB) and P(3HB-co-3HV) granules during simulated exogenous carbon deprivation on cell survival by transferring cells with PHAs to carbon-free mineral salt medium supplemented with 1% (w/v) nitrogen source. By mobilizing the intracellular P(3HB) and P(3HB-co-3HV) at 11 and 40 mol% 3HV compositions, the cells survived starvation. Surprisingly, D. acidovorans containing P(3HB-co-94 mol% 3HV) also survived although the mobilization was not as effective. Similarly, recombinant Escherichia coli pGEM-T::phbCAB(Cn) (harboring the PHA biosynthesis genes of Cupriavidus necator) containing P(3HB) granules had a higher viable cell counts compared to those without P(3HB) granules but without any P(3HB) mobilization when exposed to oxidative stress by photoactivated titanium dioxide. This study provided strong evidence that enhancement of stress tolerance in PHA producers can be achieved without mobilization of the previously accumulated granules. Instead, PHA biosynthesis may improve bacterial survival via multiple mechanisms.
Histological observation and scanning electron microscopy analyses in Dendrobium Bobby Messina indicates the cellular process of cryopreserved protocorm-like bodies (PLBs) was different comparative to non-cryopreserved PLBs. The cellular process was not only modified by the freezing and thawing effect but also due to the dehydration process itself during the cryopreservation procedure. Histological observation in Dendrobium Bobby Messina in encapsulation-dehydration method indicated that the degree of plasmolysis causes more cellular changes to the cryopreserved PLBs comparative to non-cryopreserved and stock culture PLBs. These results revealed higher amount of homogenous cell population and denser cytoplasm in cryopreserved PLBs. Histological analysis also revealed more voluminous nucleus in cryopreserved PLBs comparative to non-cryopreserved PLBs and PLBs stock culture. In contrast, scanning electron microscope analysis showed severe damages in cryopreserved PLBs and non-cryopreserved PLBs comparative to the PLBs stock culture which in return could be the possible reason of no regrowth in encapsulation-dehydration method. Damages incurred were on top part, side part, and at the stomata of the PLBs. Histological observation and scanning electron microscopy analyses in Dendrobium Bobby Messina indicates that the degree of plasmolysis causes changes in the cellular process of PLBs from cryopreserved PLBs was different comparative to non-cryopreserved PLBs.
Free laccase and fungal biomass from white-rot fungi were compared in the thermokinetics study of the laccase-catalyzed decolorization of an azo dye, i.e., Trypan Blue. The decolorization in both systems followed a first-order kinetics. The apparent first-order rate constant, k1', value increases with temperature. Apparent activation energy of decolorization was similar for both systems at ∼ 22 kJ mol(-1), while energy for laccase inactivation was 18 kJ mol(-1). Although both systems were endothermic, fungal biomass showed higher enthalpy, entropy, and Gibbs free energy changes for the decolorization compared to free laccase. On the other hand, free laccase showed reaction spontaneity over a wider range of temperature (ΔT = 40 K) as opposed to fungal biomass (ΔT = 15 K). Comparison of entropy change (ΔS) values indicated metabolism of the dye by the biomass.
This study aimed at optimizing the production of hyaluronic acid by Lactobacillus acidophilus FTDC 1231 using response surface methodology and evaluating the effects of divalent metal ions along the production pathway using molecular docking. Among different divalent metal ions that were screened, only iron (II) sulphate and copper (II) sulphate significantly (P
The contributing molecular pathways underlying the pathogenesis of breast cancer need to be better characterized. The principle of our study was to better understand the genetic mechanism of oncogenesis for human breast cancer and to discover new possible tumor markers for use in clinical practice. We used complimentary DNA (cDNA) microarrays to compare gene expression profiles of treated Michigan Cancer Foundation-7 (MCF-7) with recombinant bromelain and untreated MCF-7. SpringGene analysis was carried out of differential expression followed by Ingenuity Pathway Analysis (IPA), to understand the underlying consequence in developing disease and disorders. We identified 1,102 known genes differentially expressed to a significant degree (p<0.001) changed between the treatment. Within this gene set, 20 genes were significantly changed between treated cells and the control cells with cutoff fold change of more than 1.5. These genes are RNA-binding motif, single-stranded interacting protein 1 (RBMS1), ribosomal protein L29 (RPL29), glutathione S-transferase mu 2 (GSTM2), C15orf32, Akt3, B cell translocation gene 1 (BTG1), C6orf62, C7orf60, kinesin-associated protein 3 (KIFAP3), FBXO11, AT-rich interactive domain 4A (ARID4A), COPS2, TBPL1|SLC2A12, TMEM59, SNORD46, glioma tumor suppressor candidate region gene 2 (GLTSCR2), and LRRFIP. Our observation on gene expression indicated that recombinant bromelain produces a unique signature affecting different pathways, specific for each congener. The microarray results give a molecular mechanistic insight and functional effects, following recombinant bromelain treatment. The extent of changes in genes is related to and involved significantly in gap junction signaling, amyloid processing, cell cycle regulation by BTG family proteins, and breast cancer regulation by stathmin1 that play major roles.
Xylitol production by bioconversion of xylose can be economically interesting if the raw material can be recovered from a cheap lignocellulosic biomass (LCB). Meranti wood sawdust (MWS) is a renewable and low-cost LCB that can be used as a promising and economic source of xylose, a starting raw material for the manufacture of several specialty chemicals, especially xylitol. This study aimed to optimize the hydrolysis process of MWS and to determine the influence of temperature, H2SO4 concentration, and residence time on xylose release and on by-product formation (glucose, arabinose, acetic acid, furfural, hydroxymethylfurfural (HMF), and lignin degradation products (LDPs)). Batch hydrolysis was conducted under various operating conditions, and response surface methodology was adopted to achieve the highest xylose yield. Xylose production was highly affected by temperature, acid concentration, and residence time. The optimum temperature, acid concentration, and time were determined to be 124 °C, 3.26 %, and 80 min, respectively. Under these optimum conditions, xylose yield and selectivity were attained at 90.6 % and 4.05 g/g, respectively.
Microbial pigments are gaining intensive attention due to increasing awareness of the toxicity of synthetic colours. In this study, a novel polymer-producing bacterium designated as Cupriavidus sp. USMAHM13 was also found to produce yellow pigment when cultivated in nutrient broth. Various parameters such as temperature, pH and ratio of culture volume to flask volume were found to influence the yellow pigment production. UV-Visible, Fourier transform infrared and (13)C-nuclear magnetic resonance analyses revealed that the crude yellow pigment might probably represent new bioactive compound in the carotenoid family. The crude yellow pigment also exhibited a wide spectrum of antimicrobial activity against Gram-negative and Gram-positive bacteria with their inhibition zones and minimal inhibitory concentrations ranged from 25 to 38 mm and from 0.63 to 2.5 mg/ml, respectively. To the best of our knowledge, this is the first report on the identification and characterization of yellow pigment produced by bacterium belonging to the genus Cupriavidus.