Cellulose was extracted from sugar palm fibres (Arenga pinnata) by conducting delignification and mercerization treatments. Subsequently, sugar palm nanocrystalline celluloses (SPNCCs) were isolated from the extracted cellulose with 60wt% concentrated sulphuric acid. The chemical composition of sugar palm fibres were determined at different stages of treatment. Structural analysis was carried out by Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). Morphological analysis of extracted cellulose and isolated nanocrystalline cellulose (NCCs) was investigated by using field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM), and transmission electron microscopy (TEM). The thermal stability of sugar palm fibres at different stages of treatment was investigated by thermogravimetric analysis (TGA). The results showed that lignin and hemicellulose were removed from the extracted cellulose through the delignification and mercerization process, respectively. The isolated SPNCCs were found to have length and diameters of 130±30nm and 9±1.96nm, respectively.
A novel nano-bio composite polypyrrole (PPy)/kappa-carrageenan(KC) was fabricated and characterized for application as a cathode catalyst in a microbial fuel cell (MFC). High resolution SEM and TEM verified the bud-like shape and uniform distribution of the PPy in the KC matrix. X-ray diffraction (XRD) has approved the amorphous structure of the PPy/KC as well. The PPy/KC nano-bio composites were then studied as an electrode material, due to their oxygen reduction reaction (ORR) ability as the cathode catalyst in the MFC and the results were compared with platinum (Pt) as the most common cathode catalyst. The produced power density of the PPy/KC was 72.1 mW/m(2) while it was 46.8 mW/m(2) and 28.8 mW/m(2) for KC and PPy individually. The efficiency of the PPy/KC electrode system is slightly lower than a Pt electrode (79.9 mW/m(2)) but due to the high cost of Pt electrodes, the PPy/KC electrode system has potential to be an alternative electrode system for MFCs.
In this work, an environmental friendly RC/N-TiO2 nanocomposite thin film was designed as a green portable photocatalyst by utilizing recycled newspaper as sustainable cellulose resource. Investigations on the influence of N-doped TiO2 nanorods incorporation on the structural and morphological properties of RC/N-TiO2 nanocomposite thin film are presented. The resulting nanocomposite thin film was characterized by FESEM, AFM, FTIR, UV-vis-NIR spectroscopy, and XPS analysis. The results suggested that there was a remarkable compatibility between cellulose and N-doped TiO2 nanorods anchored onto the surface of the RC/N-TiO2 nanocomposite thin film. Under UV and visible irradiation, the RC/N-TiO2 nanocomposite thin film showed remarkable photocatalytic activity for the degradation of methylene blue solution with degradation percentage of 96% and 78.8%, respectively. It is crucial to note that the resulting portable photocatalyst produced via an environmental and green technique in its fabrication process has good potential in the field of water and wastewater treatment application.
Nanofibrillated cellulose from biomass has recently gained attention owing to their biodegradable nature, low density, high mechanical properties, economic value and renewability. Although they still suffer from two major drawbacks. The first challenge is the exploration of raw materials and its application in nanocomposites production. Second one is high energy consumption regarding the mechanical fibrillation. However, pretreatments before mechanical isolation can overcome this problem. Hydrophilic nature of nano-size cellulose fibers restricts good dispersion of these materials in hydrophobic polymers and therefore, leads to lower mechanical properties. Surface modification before or after mechanical defibrillation could be a solution for this problem. Additionally, drying affects the size of nanofibers and its properties which needs to study further. This review focuses on recent developments in pretreatments, nanofibrillated cellulose production and its application in nanopaper applications, coating additives, security papers, food packaging, and surface modifications and also for first time its drying.
In this work, polylactic acid (PLA) composites filled with microcrystalline cellulose (MCC) from oil palm biomass were successfully prepared through solution casting. Fourier transform infrared (FT-IR) spectroscopy indicates that there are no significant changes in the peak positions, suggesting that incorporation of MCC in PLA did not result in any significant change in chemical structure of PLA. Thermogravimetric analysis was conducted on the samples. The T50 decomposition temperature improved with addition of MCC, showing increase in thermal stability of the composites. The synthesized composites were characterized in terms of tensile properties. The Young's modulus increased by about 30%, while the tensile strength and elongation at break for composites decreased with addition of MCC. Scanning electron microscopy (SEM) of the composites fractured surface shows that the MCC remained as aggregates of crystalline cellulose. Atomic force microscopy (AFM) topographic image of the composite surfaces show clustering of MCC with uneven distribution.
In this work, we successfully isolated microcrystalline cellulose (MCC) from oil palm empty fruit bunch (OPEFB) fiber-total chlorine free (TCF) pulp using acid hydrolysis method. TCF pulp bleaching carried out using an oxygen-ozone-hydrogen peroxide bleaching sequence. Fourier transform infrared (FT-IR) spectroscopy indicates that acid hydrolysis does not affect the chemical structure of the cellulosic fragments. The morphology of the hydrolyzed MCC was investigated using scanning electron microscopy (SEM), showing a compact structure and a rough surface. Furthermore, atomic force microscopy (AFM) image of the surface indicates the presence of spherical features. X-ray diffraction (XRD) shows that the MCC produced is a cellulose-I polymorph, with 87% crystallinity. The MCC obtained from OPEFB-pulp is shown to have a good thermal stability. The potential for a range of applications such as green nano biocomposites reinforced with this form of MCC and pharmaceutical tableting material is discussed.
The exploration of new natural fibers in the field of polymer composites can contribute to increase the invention of natural reinforcements and expand their use in possible applications. In the present work, the physico-chemical, thermal, tensile and morphological properties of Furcraea foetida (FF) fiber are presented for the first time. Chemical analysis results shows that FF has relatively higher cellulose (68.35%) with lower hemicelluloses (11.46%) and lignin (12.32%). Structural analysis of FF was conducted by Fourier transform infrared and13C (CP-MAS) nuclear magnetic resonance spectroscopy. X-ray diffraction (XRD) analysis evidenced that FF has crystallinity index of 52.6% with crystalline size of 28.36nmThe surface morphology of FF was investigated by scanning electron microscopy (SEM), energy dispersive X-ray micro analyzer (EDX) and atomic force microscopy (AFM). The thermogravimetric analysis (TGA) reveals thermal constancy of the fiber upto 320.5°C with the kinetic activation energy of 66.64kJ/mol, which can be used as reinforcements in thermoplastic green composite whose working temperatures is below 300°C. The FF results were compared with those of other natural fibers, and indicated as a suitable alternative source for composite manufacture.
As a health-beneficial fruit, litchi is widely accepted by people in subtropical and tropical regions. However, the critical chemicals responsible for the health benefits are not clear yet. As a large amount of polysaccharides are present in litchi, they might play an important role in the health benefits. In this work, the main water-soluble polysaccharide (LPPBa) was purified from litchi pulp. The chemical structure was characterized as arabinogalactan by gas chromatography and nuclear magnetic resonance spectrometry (NMR). NMR data revealed the glycosidic linkages and their locations in backbone and branches. The precise structure was putatively identified as below, and it was different to those commonly occurred arabinogalactans. The molecular weight was determined to be 2.4 × 10(6)Da by gel permeation chromatography.
Herein, this study extracted nanocrystalline cellulose (NC) and silica (SiO2) from raw oil palm leaves (OPL), and employed as nanofillers in polyethersulfone (PES) to produce NC-SiO2-PES as support to immobilize Candida rugosa lipase (CRL) (NC-SiO2-PES/CRL). XRD, TGA-DTG and FTIR-ATR data affirmed that NC and SiO2 were isolated from OPL with corresponding crystallinity indices of 68 % and 70 %. A 0.02 cm membrane size with 5% (w/v) of NC-SiO2 without PVP K30 was optimal for membrane fabrication. CRL immobilized on the Glut-AP-NC-SiO2-PES membrane gave a higher conversion of pentyl valerate (PeVa) (91.3 %, p < 0.05) compared to Glut-NC-SiO2-PES (73.9 %) (p < 0.05). Characterization of the NC-SiO2-PES/CRL biocatalyst verified the presence of CRL. Hence, raw OPL is a proven good source of NC and SiO2, as reinforcement nanofillers in PES. The overall findings envisage the promising use of NC-SiO2-PES/CRL to catalyze an expedient and high yield of PeVa, alongside the suitability of NC-SiO2-PES for activating other enzymes.
The production of pullulanase by Bacillus flavothermus KWF-1 in batch and fed batch culture were compared using 2L bioreactor. In batch culture, 0.0803 U/mL of pullulanase activity with specific activity of 0.0213 U/mg was produced by controlling the agitation speed and temperature at 200 rpm and 50 °C, respectively. Fed batch production was studied by feeding the culture with different sago starch concentrations in various feeding modes for enhanced pullulanase production. Exponential feeding mode at dilution rate of 0.01/h was the preeminent strategy for enhanced pullulanase production of 0.1710 U/mL with specific activity of 0.066 U/mg. It had shown an increment of pullulanase production and specific activity by 2.1 and 3.1-fold, respectively when compared to batch culture. Increment of pullulanase activity in exponential feeding mode improved hydrolyzation of sago starch into maltotriose and panose by 4.5 and 2.5-fold respectively compared to batch system.
Carboxymethyl chitin (CMChit) has the potential to be used as a solid polymer electrolyte (SPE) based on its ionic conductivity value of the order of 10-6 S·cm-1 in self-standing membranes. In controlled humidity of 65RH%, carboxymethyl chitin based membrane blended with 1-Butyl-3-methylimidazolium acetate (BMIM[Ac]) ionic liquid (IL) (40 wt%) showed a threshold value of ionic conductivity in the order of 10-4 S·cm-1 and electrochemical stability was up to 2.93 V. The effects of the relative humidity and ionic liquid weight fraction on the ionic conductivity and structural changes were investigated in detail. Furthermore, the X-ray diffraction (XRD) diffractogram indicated a clear reduction of crystallinity of the CMChit. The Field-emission scanning electron microscopy (FESEM) observation of the cross-sections confirmed the homogeneity of the prepared blend. This electrolyte was tested in symmetric cells based on Zn//SPE//Zn and showed good reversibility and potential for application in proton-conducting batteries.
Blends of poly (1, 8-octanediol citrate) (POC) and chitosan (CS) were prepared through solution casting technique. Films with different component fractions (POC/CS: 100/0, 90/10, 80/20, 70/30, 60/40, and 0/100) were successfully prepared and characterized for their mechanical, thermal, structural and morphological properties as well as biocompatibility. The incorporation of CS to POC significantly increased tensile strength and elastic modulus and presented limited influences on pH variation which is important to the biocompatibility of biomaterial implants. The assessment of surface topography indicated that blending could enhance and control the surface roughness of the pure films. POC/CS blends well-supported human dermal fibroblast cells attachment and proliferation, and thus can be used for a range of tissue engineering applications.
Portable dialysis is a need to implement daily and nocturnal hemodialysis. To realize portable dialysis, a dialysate regeneration system comprising superior adsorbents is required to regenerate the used dialysate. This study aims to develop a nano-adsorbent, derived from corn starch for urea removal. Oxidized starch nanoparticles (oxy-SNPs) were prepared via liquid phase oxidation, followed by chemical dissolution and non-solvent precipitation. The oxy-SNPs possessed Z-average size of 177.7 nm with carbonyl and carboxyl contents of 0.068 and 0.048 per 100 glucose units, respectively. The urea adsorption achieved the equilibrium after 4 h with 95% removal. The adsorption mechanism fitted Langmuir isotherm while the adsorption kinetics obeyed pseudo-second-order model. This new material has a maximum adsorption capacity of 185.2 mg/g with a rate constant of 0.04 g/mg.h. Moreover, the oxy-SNPs exhibited the urea uptake recovery of 91.6%. Oxy-SNPs can become a promising adsorbent for dialysate regeneration system to remove urea.
We developed tricalcium phosphate-chitosan-fucoidan biocomposite scaffold (TCP-Ch-Fu) by using the freeze-drying technique. The fabricated biocomposite scaffolds were analyzed by spectroscopy and porosity measurement. The biomechanical properties of scaffolds were assessed by compression test and the results suggested that the incorporation of Fucoidan into the biocomposite improves the compression strength of scaffolds. Biomineralization of scaffolds was evaluated by soaking them in simulated body fluid and the results revealed that the addition of Fucoidan into the scaffolds enhanced the formation of apatite layer on the surface of biocomposite after 7 days of immersion. Alamar Blue assay confirmed that the cell viability of human-derived bone marrow stromal cell was superior in the TCP-Ch-Fuscaffold. The addition of Fucoidan to TCP-Ch increased the release of osteocalcin, confirming that it can support osteogenic differentiation of human mesenchymal stromal cells in in vitro culture. Thus, TCP-Ch-Fu could be a potential candidate for bone-tissue engineering applications.
Presence of sulfated polysaccharides like heparan sulphate has often been implicated in the regulation of chondrogenesis. However, recently there has been a plethora of interest in the use of non-animal extracted analogs of heparan sulphate. Here we remodeled alginate (1.5%) by incorporating fucoidan (0.5%), a natural sulphated polysaccharide extracted from seaweeds to form a composite hydrogel (Al-Fu), capable of enhancing chondrogenesis of human mesenchymal stromal cells (hMSCs). We confirmed the efficiency of fucoidan incorporation by FTIR and EDX analysis. Further, its ability to support hMSC attachment and chondrogenic differentiation was confirmed by SEM, biochemical glycosaminoglycan quantification, real-time quantitative PCR and immunocytochemical analyses of chondrogenic markers Sox-9, Collagen II, Aggrecan and COMP. Effect of Al-Fu hydrogel on hMSC hypertrophy was also confirmed by the downregulation of hypertrophic genes Collagen X and Runx2. This composite scaffold can hence be used as a cartilage biomimetic biomaterial to drive hMSC chondrogenesis and for other cartilage repair based therapies.
Composite sago starch-based system was developed and characterized with the aim to find an alternative to gelatin in the processing of pharmaceutical capsules. Dually modified (Hydrolyzed-Hydroxypropylated) sago starches were combined with κ-carrageenan (0.25, 0.5, 0.75, and 1%). The rheological properties of the proposed composite system were measured and compared with gelatin as reference material. Results show that combination of HHSS12 (Hydrolysed-hydroxypropylated sago starch at 12h) with 0.5% κ-carrageenan was comparable to gelatin rheological behavior in pharmaceutical capsule processing. The solution viscosity at 50 °C and sol-gel transition of the proposed composite system were comparable to those of gelatin. The viscoelastic moduli (G' and G") for the proposed system were lower than those of gelatin. These results illustrate that by manipulation of the constituents of sago starch-based composite system, a suitable alternative to gelatin can be produced with comparable properties and this could find potential application in pharmaceutical capsule industry.
Cellulose continues to play an important and emerging role in photocatalysis, and its favourable properties, such as electron-rich hydroxyl groups, could enhance the performance of photocatalytic reactions. For the first time, this study exploited the kapok fibre with microtubular structure (t-KF) as a solid electron donor to enhance the photocatalytic activity of C-doped g-C3N4 (CCN) via ligand-to-metal-charge-transfer (LMCT) to improve hydrogen peroxide (H2O2) production performance. As confirmed by various characterisation techniques, the hybrid complex consisting of CCN grafted on t-KF was successfully developed in the presence of succinic acid (SA) as a cross-linker via a simple hydrothermal approach. The complexation formation between CCN and t-KF results in the CCN-SA/t-KF sample displaying a higher photocatalytic activity than pristine g-C3N4 to produce H2O2 under visible light irradiation. The enhanced physicochemical and optoelectronic properties of CCN-SA/t-KF imply that the LMCT mechanism is crucial in improving photocatalytic activity. This study promotes utilising the unique t-KF material's properties to develop a low-cost and high-performance cellulose-based LMCT photocatalyst.
Bacterial cellulose (BC) is a biopolymer with significant potential for the development of novel materials. This work aimed to prepare and characterize BC powders from nata de coco, and assess the possible enhancement of the powder properties by spray drying. Therefore, BC powders prepared by acid treatment and mechanical processing were spray-dried, and characterized according to their morphology, flowability, thermal stability, water retention capacity, and compared with commercial microcrystalline cellulose (MCC). The powders redispersibility and suspensions rheology were also evaluated. SEM showed that spray-dried BC microparticles exhibited semispherical shape and had flow rate of 4.23 g s(-1) compared with 0.52 g s(-1) for MCC. Particle size analysis demonstrated that spray-dried BC microparticles could be redispersed. TGA showed that BC samples had higher thermal stability than MCC. Water retention capacities of BC samples were greater than MCC. These findings provide new insight on the potential applications of spray-dried BC as a promising pharmaceutical excipient.
Designing environmentally friendly materials from natural resources represents a great challenge in the last decade. However, the lack of fundamental knowledge in the processing of the raw materials to fabricate the composites structure is still a major challenge for potential applications. Natural fibers extracted from plants are receiving more attention from researchers, scientists and academics due to their use in polymer composites and also their environmentally friendly nature and sustainability. The natural fiber features depend on the preparation and processing of the fibers. Natural plant fibers are extracted either by mechanical retting, dew retting and/or water retting processes. The natural fibers characteristics could be improved by suitable chemicals and surface treatments. This survey proposes a detailed review of the different types of retting processes, chemical and surface treatments and characterization techniques for natural fibers. We summarize major findings from the literature and the treatment effects on the properties of the natural fibers are being highlighted.
The aim of this study was development a composite film based on sago starch and κ-carrageenan to find a gelatin alternative in the pharmaceutical capsules processing. Hydrolyzed-Hydroxypropylated (dually modified) sago starch was mixed with κ-carrageenan (0.25, 0.5, 0.75, and 1%). The drying kinetics, thermomechanical, physicochemical, and barrier properties of composite films were estimated and compared with bovine gelatin. Results show that drying kinetics and mechanical properties of the composite films were comparable to those of gelatin. The water vapor permeability and moisture content of the composite films were lower than those of gelatin. The solubility of the composite films was higher than that of gelatin, and the composite films were more stable at higher relative humidity than were the gelatin films. These results show that dually modified sago starch in combination with κ-carrageenan has properties similar to those of gelatin, thus proposed system can be used in pharmaceutical capsules processes.