PURPOSE: The purpose of this laboratory and finite element analysis study was to investigate the effects on the formation of a hybrid layer of an experimental silane coupling agent containing primer solutions composed of different percentages of hydroxyethyl methacrylate.
MATERIAL AND METHODS: A total of 125 sound human premolars were restored in vitro. Simple class I cavities were formed on each tooth, followed by the application of different compositions of experimental silane primers (0%, 5%, 25%, and 50% of hydroxyethyl methacrylate), bonding agents, and dental composite resins. Bond strength tests and scanning electron microscopy analyses were performed. The laboratory experimental results were validated with finite element analysis to determine the pattern of stress distribution. Simulations were conducted by placing the restorative composite resin in a premolar tooth by imitating simple class I cavities. The laboratory and finite element analysis data were significantly different from each other, as determined by 1-way ANOVA. A post hoc analysis was conducted on the bond strength data to further clarify the effects of silane primers.
RESULTS: The strongest bond of hybrid layer (16.96 MPa) was found in the primer with 25% hydroxyethyl methacrylate, suggesting a barely visible hybrid layer barrier. The control specimens without the application of the primer and the primer specimens with no hydroxyethyl methacrylate exhibited the lowest strength values (8.30 MPa and 11.78 MPa) with intermittent and low visibility of the hybrid layer. These results were supported by finite element analysis that suggested an evenly distributed stress on the model with 25% hydroxyethyl methacrylate.
CONCLUSIONS: Different compositions of experimental silane primers affected the formation of the hybrid layer and its resulting bond strength.
PURPOSE: The purpose of this in vitro study was to determine the wetting properties of 3 different commercially available denture base resin materials with artificial salivary substitute by using contact angle measurements and to compare these properties before and after thermocycling.
MATERIAL AND METHODS: A total 120 specimens were fabricated with 3 different denture base materials (n=40): heat-polymerized polymethylmethacrylate (DenTek), injection-molded nylon polyamide (Valplast), and microwave polymerized (VIPI WAVE). The advancing and receding contact angles were measured with a goniometer by using the WinDrop++ software program. The contact angle hysteresis was calculated from the advancing and receding contact angles values. The same specimens were subjected to thermocycling to measure the advancing and receding contact angles values. The comparative evaluation was carried out before and after thermocycling.
RESULTS: The mean ±standard deviation contact angles of the microwave-polymerized material were (62.40 ±1.21 degrees) advancing contact angle, (32.12 ±0.66 degrees) receding contact angle, and (30.28 ±1.40 degrees) contact angle of hysteresis. It was followed by the injection-molded nylon polyamide material, whose mean ±standard deviation contact angle values were (68.57 ±1.72 degrees) advancing contact angle, (43.02 ±1.39 degrees) receding contact angle, (26.27 ±2.05 degrees) contact angle hysteresis and high impact strength heat-polymerized polymethylmethacrylate material, whose mean ±standard deviation contact angle values were (69.81 ±0.16 degrees) advancing contact angle, (41.90 ±1.02 degrees) receding contact angle, and (27.91 ±0.97 degrees) contact angle hysteresis. The statistical analysis showed significant differences among contact angle values of the microwave-polymerized material as compared with the heat-polymerized polymethylmethacrylate and injection-molded nylon polyamide materials (P
PURPOSE: The purpose of this in vitro study was to evaluate the wettability of 3 different artificial saliva substitutes on heat-polymerized acrylic resin and to compare these properties with natural saliva and distilled water.
MATERIAL AND METHODS: A total of 150 heat-polymerized acrylic resin specimens were prepared with 25×15×2 mm dimensions. The specimens were divided into 5 groups (n=30): human saliva, distilled water, Aqwet, Mouth Kote, and Stoppers 4. The advancing and receding contact angle values were measured by using a goniometer, and the contact angle hysteresis and equilibrium angle were calculated. One-way ANOVA and the Bonferroni multiple comparisons test were performed to determine the difference between contact angle values among the groups (α=.05).
RESULTS: The means of the 5 groups differed significantly (P
PURPOSE: The purpose of this in vitro study was to compare the adherence of Streptococcus spp. and Candida spp. on 3D-printed denture bases prepared at different build orientations with conventional heat-polymerized resin.
MATERIAL AND METHODS: Resin specimens (n=5) with standardized 28.3 mm2 surface area were 3D printed at 0 and 60 degrees, and heat-polymerized (3DP-0, 3DP-60, and HP, respectively). The specimens were placed in a Nordini artificial mouth (NAM) model and exposed to 2 mL of clarified whole saliva to create a pellicle-coated substratum. Suspensions of Streptococcus mitis and Streptococcus sanguinis, Candida albicans and Candida glabrata, and a mixed species, each at 108 cfu/mL were pumped separately into the model for 24 hours to promote microbial adhesion. The resin specimens were then removed, placed in fresh media, and sonicated to dislodge attached microbes. Each suspension (100 μL) was aliquoted and spread on agar plates for colony counting. The resin specimens were also examined under a scanning electron microscope. The interaction between types of specimen and groups of microbes was examined with 2-way ANOVA and then further analysis with Tukey honest significant test and Kruskal-Wallis post hoc tests (α=.05).
RESULTS: A significant interaction was observed between the 3DP-0, 3DP-60, and HP specimen types and the groups of microbes adhering to the corresponding denture resin specimens (P