In this study, magnetite nano-adsorbent (MNA) was extracted from mill scale waste products, synthesized and applied to eliminate Cu2+ from an aqueous solution. Mill scale waste product was ground using conventional milling and impacted using high-energy ball milling (HEBM) for varying 3, 5, and 7 milling hours. In this regard, the prepared MNA was investigated using X-ray diffraction (XRD), high-resolution transmission electron microscope (HRTEM), field emission scanning electron microscopy-energy-dispersive X-ray spectroscopy (FESEM-EDS), UV-Vis spectroscopy, Fourier-transform infrared (FTIR), Brunauer-Emmett-Teller (BET) and zeta potential. The resultant MNA-7 h milling time displayed a crystalline structure with irregular shapes of 11.23 nm, specific surface area of 5.98 m2g-1, saturation magnetization, Ms of 8.35 emug-1, and isoelectric point charge at pH 5.4. The optimum adsorption capacity, qe of 4.42 mg.g-1 for the removal of Cu2+ ions was attained at 120 min of contact time. The experimental data were best fitted to the Temkin isotherm model. A comparison between experimental kinetic studies and the theoretical aspects showed that the pseudo-second-order matched the experimental trends with a correlation coefficient of (R2 > 0.99). Besides, regeneration efficiency of 70.87% was achieved after three cycles of reusability studies. The MNA offers a practical, efficient, low-cost approach to reutilize mill scale waste products and provide ultra-fast separation to remove Cu2+ from water.
The present study synthesized nano-magnetite (Fe3O4) from milled steel chips using the high energy ball milling (HEBM) method, characterized it, and then utilized it as a sorbent to remediate boron concentration at various pH (4-9), dosages (0.1-0.5 g), contact times (20-240 min), and initial concentrations (10-100 mg/L). The nano-sorbents were characterized based on SEM structure, elemental composition (EDX), surface area analysis (BET), crystallinity (XRD), and functional group analysis (FTIR). The highest adsorption capacity of 8.44 mg/g with removal efficiency of 84% was attained at pH 8, 0.5 g dosage, contact time of 180 min, and 50 mg/L initial concentration. The experimental data fit best with the pseudo-second-order kinetic model with R2 of 0.998, while the Freundlich adsorption isotherm describes the adsorption process with an R2 value of 0.9464. A regeneration efficiency of 47% was attained even after five cycles of reusability studies. This efficiency implies that the nano-magnetite has the potential for sustainable industrial application.
High proportion of copper has become a global challenge owing to its negative impact on the environment and public health complications. The present study focuses on the fabrication of a polyvinylidene fluoride (PVDF)-polyvinyl pyrrolidone (PVP) fiber membrane incorporated with varying loading (0, 0.5, 1.0, 1.5, and 2.0 wt%) of titanium dioxide (TiO2) nanoparticles via phase inversion technique to achieve hydrophilicity along with high selectivity for copper removal. The developed fibers were characterized based on scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), permeability, porosity, zeta potential, and contact angle. The improved membrane (with 1.0 wt% TiO2) concentration recorded the maximum flux (223 L/m2·h) and copper rejection (98.18%). Similarly, 1.0 wt% concentration of TiO2 nanoparticles made the membrane matrix more hydrophilic with the least contact angle of 50.01°. The maximum copper adsorption capacity of 69.68 mg/g was attained at 1.0 wt% TiO2 concentration. The experimental data of adsorption capacity were best fitted to the Freundlich isotherm model with R2 value of 0.99573. The hybrid membrane developed in this study has considerably eliminated copper from leachate and the concentration of copper in the permeate was substantially reduced to 0.044 mg/L, which is below standard discharge threshold.