The demand for new glass hosts with emergent properties is constantly growing for various miniaturized applications. Thus, some new types of Sm2O3-activated strontium-telluro-alumino-magnesium-borate glasses with copper oxide nanoparticles (CuONps) insertion were made using melt-quenching approach. The obtained glasses were characterized to determine the effects of Sm2O3 concentration changes on their thermal, structural, and luminescence properties. XRD, FTIR, and HRTEM analyses of the samples verified their glassy nature, presence of different functional units and CuONps, respectively. DTA analysis showed excellent thermal stability of these glasses with a stability factor as much as 125 °C. The optical absorption properties of the glasses were highly sensitive to Sm3+ concentrations variation. The Judd-Ofelt intensity parameters of the glasses with and without CuONps followed the trend of Ω6˃Ω4˃Ω2 and Ω4˃Ω6˃Ω2, respectively. These glasses displayed 4 visible luminescence bands at 561, 598, 645, and 705 nm corresponding to 4G5/2 → 6H5/2, 4G5/2 → 6H7/2, 4G5/2 → 6H9/2, and 4G5/2 → 6H11/2 transitions in Sm3+. In addition, branching ratio above 80% and stimulated emission cross-section up to 135.82 × 10-23 cm2 were achieved. The stimulated emission cross-section and optical gain were enhanced due to the inclusion of CuONps in the glasses. These glasses may be useful for solid state laser and optical amplifier development.
This paper reports an intense up-conversion luminescence from Dy3+-doped strontium-telluro-alumino-magnesium-borate glasses for the first time. The samples were made via the melt-quenching method and characterized to determine the influence of various CuO nanoparticles contents change on their up-conversion emission traits. Absorption spectral data were used to calculate the Judd-Ofelt intensity parameters. The sample without CuO nanoparticles revealed two intense photoluminescence up-conversion emission peaks at 478 and 570 nm. In addition, CuO nanoparticles-activated sample displayed about 1.4-fold up-conversion emission intensity improvement due to strong light absorption in the visible to the infrared region at 799 nm excitation. The stimulated emission cross-section of the CuO nanoparticles-activated glasses was increased from 102.4 × 10-23 to 1301.1 × 10-23 cm2 (nearly 10-fold amplification) while the branching ratio was reduced to 66.9%. Thus, CuO nanoparticles as an additive in the current glass matrix enhanced the up-conversion emission and strengthened the associated nonlinear optical properties. CIE 1931 color matching revealed the influence of CuO in modifying the up-conversion color coordinates, thereby improving the white color purity. The achieved up-conversion emission coupled with the color tunability of the proposed glasses may be advantageous for the up-conversion UV tunable laser making.