Replacing a single missing anterior tooth can be a challenge. Many factors need to be considered when choosing the appropriate treatment. Several treatment options are well established. This case report is to present the use of a cast cobalt chrome partial denture with custom made porcelain tooth to improve aesthetic. The overall shade of the artificial tooth were nicely matched with the adjacent teeth and definite enamel translucency could be achieved which would not be possible with acrylic or even with readymade porcelain tooth.
Some restorative materials are susceptible to erosion but whether it also causes microleakage is still questionable. The aim of this study was to assess the microleakage of few restorative materials after immersion in acidic solution. Standardized ‘U’ shaped cavity of 4mm diameter and 2mm depth were prepared on buccal or lingual surface of 52 human premolar and molar teeth. The teeth were divided into 4 groups which contains 13 samples and 3 controls for each and were restored either with Filtek Z250 (Group 1), Fuji IX (Group 2), Fuji II LC (Group 3), or Silverfill amalgam (Group 4).
All surfaces were painted with nail varnish leaving only 2mm of tooth structure surrounding the restoration before the study samples were immersed in acidic solution, lemon juice (pH 2.74) and control samples in deionised distilled water for 24 hours. Surface photos for erosion were taken before immersion in methylene blue for 7 days. After sectioning, the assessment of dye penetration was done using Leica Imaging System DMLM (Germany). Photos showed that Fuji IX demonstrated severe erosion but no obvious changes were seen on other materials. Kruskal-Wallis test indicated that microleakage between all four groups were statistically significant. The most significant difference was between Filtek Z250 and Fuji IX (p
Composite resins Amaris is claimed to have hydrophobic effect which minimizes the staining intake. This study is to investigate the colour stability of Amaris compared to Filtek Z250 in coffee solution. Sixty discs of composite resins Filtek Z250 (3M ESPE) and Amaris (Voco) with diameter of 5mm and depth of 2mm were fabricated by packing in a drinking straw and sectioned with hard tissue cutter (Exakt, Japan). The surfaces of the specimens were polished with Sof-Lex disc before each group of the samples is immersed in coffee solution. They were kept in the solution for 4 days at 370C and assessed at the period of 2 hours, 1 day, 2 days, 3 days, and 4 days. The staining was assessed visually and recorded using Lobene (1968) Stain Index and score was given accordingly. The colour changes of both groups were not statistically significant (p
Endodontically treated teeth are generally weaker than sound teeth. The study objective was to compare the fracture resistance of endodontically treated teeth restored with different restorative techniques. Fifty extracted human maxillary central incisors of similar size were divided into five groups of 10 teeth. Group 1 was left intact as the control group. Other groups (Groups 2, 3, 4 and 5) were all endodontically treated followed by restorations using different restorative techniques; light cured composite resin (CR), CR and crown, post and CR, and post-CR core and crown respectively. The specimens were loaded in a universal testing machine with a static force at a crosshead speed of 0.5mm/min at 135 ° to the long axis of the root until failure. The means and the standard deviations of the maximum load at failure for groups 1, 2, 3, 4 and 5 were 1259.11N (379.12N), 578.63N (196.70N), 667.13N (298.72N), 1247.65N (294.48N) and 623.60N (193.75N) respectively. The results of one-way ANOVA showed statistically significant differences existed among the groups tested (p
Tooth wear is the loss of tooth tissue and structures not due to caries. It can occur in various forms either attrition, abrasion, erosion, noncaries cervical lesion (NCCL) or a combination of two or more forms. The objective of this study was to determine the patterns and associated aetiologies of tooth wear among adults in Kelantan, Malaysia. This crosssectional study involved 81 adults with tooth wear which was visually assessed using the Smith and Knight Tooth Wear Index (TWI). A questionnaire was used to seek putative aetiologies of the wear. Data were analyzed and the results were expressed as frequencies and percentages. Six thousand three hundred and eighty four tooth surfaces were examined in 1596 teeth. 17.4% surfaces had tooth wear; 80% scored 1, 18% scored 2 and 2% scored 3. Among the 81 cases of tooth wear, 29 (35.8%) had abrasion; 25 (30.9%) had attrition; 1(1.2%) had erosion while 26 (32.1%) had the combined type. Among those with abrasion, majority had the habit of eating freshwater clams (Corbicula fluminea) as local delicacy where most of the times people use their teeth to pry open the clam shells. Erosion was related to the pooling of carbonated drinks or beverages in the mouth before swallowing. In conclusion, most adults experienced abrasion and the most common possible associated aetiology is the way of eating clams.
The in vitro cytotoxic potential of locally produced dental porcelain was evaluated in this study. The cellular response of human osteoblast and fibroblast cell lines were assessed using MTT assay by incubating with the fluid extract of dental porcelain powder and dental porcelain discs (direct test). Aging process was carried out by submerging the discs into 3% bovine serum albumin (BSA) solution. Tests on extracts showed that dental porcelain was significantly different from the control at a concentration of 250 mg/ml. Direct test showed that dental porcelain after aging was not significantly different from the control with a mean (SD) of 89.2 (13.4)%, whereas, it was significantly different from the control before conditioning of BSA with a mean (SD) of 88.5 (12.1)%. However, the dental porcelain caused mild suppression of succinate dehydrogenase activity (
Evaluation of the mechanical behaviour of restoration dental materials is essential to understand their performance under different load conditions and to estimate their durability under clinical oral function. Restorative materials and dental tissues like other materials by having specific mechanical properties, such as static strength (i.e. compressive strength, tensile strength, flexural strength) and dynamic strength (i.e. fatigue strength). The selection of proper mechanical test type depends on the goals that the study claims to define. On such basis, the mechanical test can be chosen correctly. Laboratory studies should be designed as replications of the clinical oral circumstances to measure the mechanical and physical properties of a material and any arbitrary choices in the design of the study may result in large variations of data.
Light intensity output is one of the determinants for adequate curing of visible light-cured materials. The aim of this survey was to evaluate the light intensity outputs (LIOs) of light curing units (LCUs) in dental clinics of Hospital Universiti Sains Malaysia (HUSM) and School of Dental Sciences, Universiti Sains Malaysia (USM). The respective LIOs of all functioning Quartz Tungsten Halogen (QTH) and Light Emitting Diode (LED) LCUs were tested using two light radiometers. For cordless LED LCUs, the testing procedure was done in situ and after being fully charged. Statistical analysis using Kruskal Wallis and Wilcoxon signed ranks tests were performed to compare the LIOs between groups and between the LIOs of in situ and post-charged cordless LED LCUs, respectively. The level of significance was set at 0.05 (p