Current study employs mixture of chlorophyll-anthocyanin dye extracted from leaves of Cordyline fruticosa as new sensitizers for dye-sensitized solar cell (DSSCs), as well as betalains dye obtained from fruit of Hylocereus polyrhizus. Among ten pigments solvents, the ethanol and methanol extracts revealed higher absorption spectra of pigments extracted from C. fruticosa and H. polyrhizus respectively. A major effect of temperature increase was studied to increase the extraction yield. The results indicated that extraction temperature between 70 and 80°C exhibited a high dye concentration of each plant than other temperatures. The optimal temperature was around 80°C and there was a sharp decrease of dye concentration at temperatures higher than this temperature. According to experimental results, the conversion efficiency of DSSC fabricated by mixture of chlorophyll and anthocyanin dyes from C. fruticosa leaves is 0.5% with short-circuit current (Isc) of 1.3mA/cm-2, open-circuit voltage (Voc) of 0.62V and fill factor (FF) of 60.16%. The higher photoelectric conversion efficiency of the DSSC prepared from the extract of H. polyrhizus was 0.16%, with Voc of 0.5V, Isc of 0.4mA/cm-2 and FF of 79.16%. The DSSC based betalain dye extracted from fruit of H. polyrhizus shows higher maximum IPCE of 44% than that of the DSSCs sensitized with mixed chlorophyll-anthocyanin dye from C. fruticosa (42%).
The natural dyes anthocyanin and chlorophyll were extracted from Musa acuminata bracts and Alternanthera dentata leaves, respectively. The dyes were then applied as sensitizers in TiO2-based dye-sensitized solar cells (DSSCs). The ethanol extracts of the dyes had maximum absorbance. High dye yields were obtained under extraction temperatures of 70 to 80°C, and the optimal extraction temperature was approximately 80°C. Moreover, dye concentration sharply decreased under extraction temperatures that exceeded 80°C. High dye concentrations were obtained using acidic extraction solutions, particularly those with a pH value of 4. The DSSC fabricated with anthocyanin from M. acuminata bracts had a conversion efficiency of 0.31%, short-circuit current (Isc) of 0.9mA/cm2, open-circuit voltage (Voc) of 0.58V, and fill factor (FF) of 62.22%. The DSSC sensitized with chlorophyll from A. dentata leaves had a conversion efficiency of 0.13%, Isc of 0.4mA/cm-2,Voc of 0.54V, and FF of 67.5%. The DSSC sensitized with anthocyanin from M. acuminata bracts had a maximum incident photon-to-current conversion efficiency of 42%, which was higher than that of the DSSC sensitized with chlorophyll from A. dentata leaves (23%). Anthocyanin from M. acuminata bracts exhibited the best photosensitization effects.