A wide-band and tunable Q-switched erbium-doped fiber (EDF) laser operating at 1560.5 nm with a tungsten ditelluride (WTe2) saturable absorber (SA) is demonstrated. The semi-metallic nature of WTe2 as well as its small band gap and excellent nonlinear optical properties make it an excellent SA material. The laser cavity uses an 89.5 cm long EDF, pumped by a 980 nm laser diode as the linear gain while the WTe2 based SA generates the pulsed output. The WTe2 based SA has a modulation depth, non-saturable loss and saturation intensity of about 21.4%, 78.6%, and 0.35 kW/cm2 respectively. Stable pulses with a maximum repetition rate of 55.56 kHz, narrowest pulse width of 1.77 µs and highest pulse energy of 18.09 nJ are obtained at the maximum pump power of 244.5 mW. A 56 nm tuning range is obtained in the laser cavity, and the output is observed having a signal to noise ratio (SNR) of 48.5 dB. The demonstrated laser has potential for use in a large number of photonics applications.
This work has demonstrated the potential of a reduced graphene oxide silver/polyvinyl alcohol (rGO-Ag/PVA) film as a saturable absorber (SA) in ytterbium and erbium based Q-switched optical fiber lasers. The facile hydrothermal method was used to synthesize the nanocomposite between rGO and Ag nanoparticles. This was followed by a simple solution method to form the rGO-Ag film using PVA as the host polymer. From nonlinear absorption characterization, the rGO-Ag/PVA SA was determined to have a modulation depth of 30%, a nonsaturable loss of 70%, and a saturable intensity of 0.63 kW/cm2. Stable self-starting Q-switched pulses were obtained at the threshold pump power of 72.76 mW and 18.63 mW in the ytterbium-doped (YDFL) and erbium-doped fiber laser (EDFL) cavities respectively. The center operating wavelengths were observed at 1044.4 nm and 1560 nm for the two cavities. The shortest pulse width and maximum repetition rate of the YDFL and EDFL were 1.10 µs and 62.10 kHz and 1.38 µs and 76.63 kHz respectively. This work has demonstrated that the rGO-Ag/PVA film is suitable as an SA for pulse generation in the 1.0 and 1.5 μm regions and would have many potential photonics applications.