MATERIALS AND METHODS: A total of 60 deciduous teeth subjected to extraction were employed in this in vitro research. These 60 specimens were randomly divided into two groups: Group I: Stainless steel crowns and Group II: Pedo Jacket crowns. Both crowns were subjected to cementation using self-cure resin-modified glass ionomer (RMGI) cement as well as by means of self-adhesive universal resin cement (RelyX luting cement). The specimens were subjected to storage in distilled water at 37°C for 24 h and were subjected to 500 thermal cycles between 5°C and 55°C using a dwell span of 30 s. Individual surfaces were assessed for the amount of dye infiltration at the boundaries by the side of the tooth-cement border beneath a stereomicroscope under 50× magnifying power. At the mesial and distal surfaces, the amount of microleakage was measured in micrometers (μm), and the mean value was computed for each sample.

RESULTS: Stainless steel crowns subject to cementation with RelyX luting cement exhibited the lowest microleakage (0.88 ± 0.78) versus self-cure RMGI cement (0.94 ± 0.78). There was no statistically significant difference found between the groups. Pedo Jacket crowns subject to cementation with RelyX luting cement exhibited the lowest microleakage (0.96. ± 0.32) while self-cure RMGI cement (1.83 ± 0.16) depicted the maximum microleakage. There was an extremely statistically noteworthy dissimilarity noted among the groups.