The preparation, physical and mechanical properties of Al/B4C composites with 5 and 10 wt.% reinforcement content were investigated. In order to obtain the feedstock with a low powder loading, B4C mixtures containing fine powders were investigated to obtain the optimal particle packing. The experimental results indicated that the fine containing 5 and 10 wt.% particles are able to prepare the feedstock with a good flowability. The composites fabricated by powder metallurgy have low densities and homogeneous microstructures. Additionally there is no interface reaction observed between the reinforcement and matrix by XRD analysis. The hardness of Al/B4C composites prepared by powder metallurgy was high.
The presence of pathogenic Leptospira spp. in the environment poses threats to human health. The aim of this study was to detect and characterize Leptospira spp. from environmental samples. A total of 144 samples comprised of 72 soil and 72 water samples were collected from markets and recreational areas in a north-eastern state in Malaysia. Samples were cultured on Ellinghausen and McCullough modified by Johnson and Harris media. Leptospires were positive in 22.9% (n = 33) of the isolates. Based on partial sequences of 16S rRNA, a pathogenic leptospire, Leptospira alstonii (n = 1/33), was identified in 3% of the isolates followed by intermediate leptospire (L. wolffii, n = 1/33, and L. licerasiae, n = 7/33) and nonpathogenic leptospire, L. meyeri (n = 22/33) in 24.2% and 66.7%, respectively. This study demonstrates the presence of a clinically significant pathogenic L. alstonii in the environments which could pose health risks to the occupants and visitors.