This study investigates the effects of temperature and period on the pretreatment of OPEFB using the low-cost N,N,N-dimethylbutylammonium hydrogen sulfate ionic liquid ([DMBA][HSO4] IL) with 20 wt% of water. The results demonstrate that higher pretreatment temperatures (120, 150, and 170 °C) and longer periods (0.5, 1, and 2 h) enhanced lignin recovery, resulting in increased purity of the recovered pulp and subsequently enhanced glucose released during enzymatic hydrolysis. However, at 170 °C, prolonging the period led to cellulose degradation and the formation of pseudo-lignin deposited on the pulps, resulting in a decreasing-trend in glucose released. Finally, the analysis of extracted lignin reveals that increasing pretreatment severity intensified lignin depolymerisation and condensation, leading to a decrease in number average molecular weight (Mn), weight average molecular weight (Mw) and polydispersity index (Đ) values.
Herein we report the synthesis and characterization of electro-conductive chitosan-gelatin-agar (Cs-Gel-Agar) based PEDOT: PSS hydrogels for tissue engineering. Cs-Gel-Agar porous hydrogels with 0-2.0% (v/v) PEDOT: PSS were fabricated using a thermal reverse casting method where low melting agarose served as the pore template. Sample characterizations were performed by means of scanning electron microscopy (SEM), attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR), X-ray diffraction analysis (XRD) and electrochemical impedance spectroscopy (EIS). Our results showed enhanced electrical conductivity of the cs-gel-agar hydrogels when mixed with DMSO-doped PEDOT: PSS wherein the optimum mixing ratio was observed at 1% (v/v) with a conductivity value of 3.35 × 10-4 S cm-1. However, increasing the PEDOT: PSS content up to 1.5 % (v/v) resulted in reduced conductivity to 3.28 × 10-4 S cm-1. We conducted in vitro stability tests on the porous hydrogels using phosphate-buffered saline (PBS) solution and investigated the hydrogels' performances through physical observations and ATR-FTIR characterization. The present study provides promising preliminary data on the potential use of Cs-Gel-Agar-based PEDOT: PSS hydrogel for tissue engineering, and these, hence, warrant further investigation to assess their capability as biocompatible scaffolds.