The lack of aesthetic properties of electrospun nanofibres in terms of colour appearance is the drive in this preliminary study. This research is conducted to study the dyeing behaviour and colorimetric properties of electrospun nanofibres blended with Remazol Yellow FG reactive dye using dope-dyeing method via electrospinning process. This paper reports the colorimetric properties of dyed poly vinyl alcohol (PVA) nanofibres within the range of 2.5 wt.% to 12.5 wt.% dye content. The electrospinning parameters were fixed at the electrospinning distance of 10 cm, constant feed rate of 0.5 mL/h and applied voltage of 15 kV. The resulting impregnated dye of 10 wt.% exhibits acceptable colour difference of dyed PVA nanofibres, with a mean fibre diameter of 177.1 ± 11.5 nm. The SEM micrographs show the effect of dye content on morphology and fibre diameter upon the increment of dye used. Further increase of dye content adversely affects the jet stability during the electrospinning, resulting in macroscopic dropping phenomenon. The presence of all prominent peaks of Remazol dye in the PVA nanofibers was supported with FTIR analysis. The addition of dye into the nanofibres has resulted in the enhancement of thermal stability of the PVA as demonstrated by TGA analysis.
Electrospinning technology, which was previously known as a scientific interdisciplinary research approach, is now ready to move towards a practice-based interdisciplinary approach in a variety of fields, progressively. Electrospun nanofiber-applied products are made directly from a nonwoven fabric-based membranes prepared from polymeric liquids involving the application of sufficiently high voltages during electrospinning. Today, electrospun nanofiber-based materials are of remarkable interest across multiple fields of applications, such as in electronics, sensors, functional garments, sound proofing, filters, wound dressing and scaffolds. This article presents such a review for summarizing the current progress on the manufacturing scalability of electrospun nanofibers and the commercialization of electrospun nanofiber products by dedicated companies globally. Despite the clear potential and limitless possibilities for electrospun nanofiber applications, the uptake of electrospinning by the industry is still limited due to the challenges in the manufacturing and turning of electrospun nanofibers into physical products. The recent developments in the field of electrospinning, such as the prominent nonwoven technology, personal views and the potential path forward for the growth of commercially applied products based on electrospun nanofibers, are also highlighted.
Titanium dioxide (TiO2) is an antimicrobial agent which is considered of potential value in inhibiting the growth of multiple bacteria. Klebsiella pneumonia and Haemophilus influenza are two of the most common respiratory infection pathogens, and are the most. Klebsiella pneumonia causes fatal meningitis, while Haemophilus influenza causes mortality even in younger patients. Both are associated with bacteremia and mortality. The purpose of this study was to test a new antibacterial material, namely nanotitania extract combined with 0.03% silver that was developed at Universiti Malaysia Sabah (UMS) and tested against K. pneumonia and H. influenza. The nanoparticles were synthesized through a modified hydrothermal process, combined with molten salt and proven to have excellent crystallinity, with the band-gap energy falling in the visible light spectrum. The nanoparticle extract was tested using a macro-dilutional method, which involved combining it with 0.03% silver solution during the process of nanoparticle synthesis and then introducing it to the bacteria. A positive control containing the bacteria minus the nanoparticles extract was also prepared. 25 mg/mL, 12.5 mg/mL, and 6.25 mg/mL concentrations of the samples were produced using the macro dilution method. After adding the bacteria to multiple concentrations of nanoparticle extract, the suspensions were incubated for 24 h at a temperature of 37 °C. The suspensions were then spread on Mueller-Hinton agar (K. pneumonia) and chocolate blood agar (H. influenza), where the growth of bacteria was observed after 24 h. Nanoparticle extract in combination with silver at 0.03% was proven to have potential as an antimicrobial agent as it was able to inhibit H. influenza at all concentrations. Furthermore, it was also shown to be capable of inhibiting K. pneumonia at concentrations of 25 mg/mL and 50 mg/mL. In conclusion, the nanoparticle extract, when tested using a macro-dilutional method, displayed antimicrobial properties which were proven effective against the growth of both K. pneumonia and H. influenza.
The development of antimicrobial packaging has been growing rapidly due to an increase in awareness and demands for sustainable active packaging that could preserve the quality and prolong the shelf life of foods and products. The addition of highly efficient antibacterial nanoparticles, antifungals, and antioxidants to biodegradable and environmentally friendly green polymers has become a significant advancement trend for the packaging evolution. Impregnation of antimicrobial agents into the packaging film is essential for impeding or destroying the pathogenic microorganisms causing food illness and deterioration. Higher safety and quality as well as an extended shelf life of sustainable active packaging desired by the industry are further enhanced by applying the different types of antimicrobial packaging systems. Antimicrobial packaging not only can offer a wide range of advantages, but also preserves the environment through usage of renewable and biodegradable polymers instead of common synthetic polymers, thus reducing plastic pollution generated by humankind. This review intended to provide a summary of current trends and applications of antimicrobial, biodegradable films in the packaging industry as well as the innovation of nanotechnology to increase efficiency of novel, bio-based packaging systems.