  1. Farah Atiqah Abdul Azam, Hamisah Ismail, Zalita Zainuddin, Muhammad Azmi Abdul Hamid, Angela H, Roslinda Shamsudin
    Sains Malaysiana, 2018;47:819-827.
    Tujuan kajian ini adalah untuk mengenal pasti kesan rawatan suhu yang berbeza terhadap kebioaktifan wolastonit
    yang disintesis menggunakan teknik sol gel. Abu sekam padi dan batu kapur digunakan sebagai bahan awalan untuk
    menghasilkan wolastonit. Nisbah campuran kalsium oksida dan silika dioksida CaO/SiO2 ditentukan pada 55:45 dan
    dimasukkan ke dalam autoklaf pada suhu 135°C dengan tekanan 0.26 MPa selama 8 jam. Campuran serbuk CaO dan
    SiO2 tersebut disinter pada suhu yang berbeza (1150°C dan 1250°C) dan diuji sifat kebioaktifan secara rendaman
    dalam larutan cecair badan tersimulasi (SBF) selama 1,3,5,7 dan 14 hari secara in vitro. Sifat fizikal dan kebioaktifan
    wolastonit sebelum dan selepas direndam dalam larutan SBF dan beberapa pencirian telah dijalankan menggunakan
    teknik analisis XRD, FESEM, EDX dan FTIR. Campuran serbuk CaO-SiO2 yang telah diautoklaf dan disinter pada suhu
    1250°C menghasilkan puncak tunggal pseudowolastonit. Ujian kebioaktifan menunjukkan lapisan amorfus kalsium
    fosfat (ACP) dengan julat nisbah Ca/P 1.9-1.51 terbentuk lebih pantas pada sampel wolastonit yang disinter pada suhu
    1250°C berbanding pembentukan ACP pada sampel tersinter 1150°C.
  2. Farah ‘Atiqah Abdul Azam, Roslinda Shamsudin, Zalita Zainuddin, Muhammad Azmi Abdul Hamid, Min Hwei Ng, Rashita Abdul Rashid
    Sains Malaysiana, 2018;47:2141-2149.
    Bioactive composites consist of pseudowollastonite and mullite synthesized from natural resources was developed for
    bone implant applications. To realize such applications, a mechanical test of these composites and in vitro bioactivity in
    SBF solution were studied. The present paper reports pseudowollastonite synthesized from the rice husk ash and limestone
    reinforced with 10, 20 and 30 wt. % of mullite. Influence of sintering temperature, phase composition, morphology towards
    mechanical properties of various pseudowollastonite-mullite (PSW-M) composites was examined prior to the bioactivity
    test. It was found that pseudowollastonite with the addition of 20 wt. % of mullite sintered at 1150°C gave the best result
    for diametral tensile strength (DTS) and hardness with the value of 8.8 ± 0.15 MPa and 3.79 ± 0.13 GPa, respectively.
    The obvious increment in the mechanical strength was due to the formation of liquid phase CaAl2
    O3
    during sintering at
    1150°C. In addition, the formation of fibrous apatite (HA) layer of amorphous calcium phosphate (ACP) with Ca/P ratio
    1.8 on PSW20M sample confirmed the good bioactivity of the composite.