This study was conducted to develop an edible coating containing combined hydrophilic (chitosan) and hydrophobic (palm stearin) components which demonstrated gas barrier and moisture barrier properties, respectively, to prolong the post harvest life of star fruits (Averrhoa carambola L.). The emulsions of chitosan (C) and palm stearin (S) were prepared by using different ratios of C:S which were 1:0, 1:1, 1;2, 1:3, 2:1, 3:1 and 0:1. Viscosity of emulsions was studied. The physicochemical properties of coated star fruits were also evaluated in terms of weight loss, firmness, visual appearance, oxygen concentration, carbon dioxide concentration and ethylene concentration during storage at room temperature (26-28˚C) for 18 days. The results obtained showed that coating reduced weight loss, maintained firmness and appearance, slowed down the production of respiratory gases and reduced ethylene production. The most recommended coating for star fruits was C:S of 1:1 ratio as it showed good water barrier and gas barrier properties and could extend the post harvest life of star fruits up to 20 days as compared to the control samples which had a post harvest life of 12 days.
Extraction of lemongrass oleoresin was successfully optimised using Pressurised Liquid Extraction (PLE). Character impact compounds; neral, geranial and geraniol which constituted 72% oleoresin, were monitored during this optimisation study by using GCMSD. Based on maximum extraction of these compounds, the optimised operating conditions for PLE were a temperature of 167°C, a pressure of 1203 psi and a static time of 20.43 min. The quality of PLE extract were compared with conventional extraction methods, hydrodistillation and Soxhlet extraction. The proposed method was found to be better in term of quantity of the targeted character impact compounds.
Guava is a climacteric fruit which has high nutritional content. It is a highly perishable fruit, undergoes rapid postharvest ripening in a few days under ambient condition. This paper aims to determine the effect of palm stearin and palm kernel olein blends on maintaining the quality of guava during storage. Two different coating formulations of palm stearin (PS) and palm kernel olein (PKOo) blends (1:1 and 3:2) were analysed for their slip melting point (SMP), cohesiveness, viscosity and density. Beeswax was used as a commercial coating for comparison whiles the uncoated guava was used as control. These coatings were applied onto guavas by hand-wipe technique using a sponge. Guavas were dried in corrugated fibre board boxes and stored in an air-conditioned room maintained at 20°C while a chiller maintained at 10°C was used for chilled temperature. Coating pick up, thickness and surface area were measured while guava properties were analysed for coating effect on weight loss, O2 and CO2 gases, firmness and glossiness during storage at ambient temperature (20°C) for 21 days and chilled temperature (10ºC) for 30 days. Microstructure analysis was conducted within 2 days of coating at ambient temperature (20ºC). The results obtained indicated that 1:1 PSPKOo blends had higher cohesiveness compared to beeswax. Both PSPKOo blends significantly (p