There is a great demand of Hydroxyapatite (HA) material in Orthopaedics and Dental applications due to its similarity to human bone. However, the lack of availability and due to high import cost of this material in Malaysia, research in producing synthetic HA locally is therefore timely. The use of local resources as the raw materials for the production of HA is also desirable in reducing the overall cost of HA. In this study, two HA materials were synthesised from different starting precursors, i.e. commercial pure Ca(OH)2 (HAS) and Ca(OH)2 directly from a local natural limestone deposit (HAL). Whereas a commercially available HA "Captal 60" (HAC) was used as reference. The synthesised powders obtained were fired at 1000 degrees C and at 1250 degrees C. Characterisation evaluations on bulk properties were carried out using XRD, SEM-EDX, ICP and FTIR. The results indicate that both HAS and HAL are comparable to HAC even at 1000 degrees C. Thus, the local natural limestone can be used to form HA. However, the overall appearance of these materials are quite different (HAC - blue, HAS - greenish and HAL - light green). The reasons for this and the subsequent mechanical and bioactive effects of these materials are currently being investigated.
Hydroxyapatite, (HA; Ca1O(PO4)6(OH)2) has been successfully applied in medical and dental applications for several years due to its excellent biocompatibility. The usage of HA in Malaysia, however, is limited due to the lack of availability. Therefore the aim of this work is to produce HA materials from both pure chemicals and from Malaysian natural limestone precursors, and to compare their bulk properties. However, parts of Malaysian natural limestone deposits actually consist of a combination of Ca(OH)2 and CaCO3. In order to utilise the limestone to produce HA material, the combination of these commercially pure chemicals as HA precursors should still work. In order to test this hypothesis, two HAs were produced by wet synthesis technique utilising (a) combination of Ca(OH)2 + CaCO3 from pure commercial chemicals [WCC] and (b) a local natural limestone [WL] precursors. The HAs produced; WCC and WL, were compacted into discs and sintered at 1250 degrees C. The characterisations and evaluations conducted were XRD, SEM-EDX, FTIR and shrinkage factor. The results indicate that WL gives slightly better bulk properties compared to WCC.